简介:Fe3AlandCr18-Ni8steelwerebondedinvacuumandaninterfacewasformedbetweenFe3AlandCr18-Ni8steel.Stressdistributionatthediffusion-bondedinterfacewasresearchedbynumericalsimulationandfiniteelementmethod(FEM).TheresultsindicatedthatthepeakstressappearedattheinterfacenearCr18-Ni8steelside.Thisisthekeyfactortoinducecrackatthisposition.Withtheenhancementofheatingtemperature,thepeakstressatthebondedinterfaceincreases.Whenthetemperatureis1100℃,thepeakstressisupto65.9MPa,whichisbiggerthanthatat1000℃by9.4%.Inaddition,thepeakstressbecomesbiggerwiththeincreaseofthethicknessofbasemetalfrom1mmto8mm.Whilethethicknessismorethan8mm,thepeakstressvariesslightlywiththechangeofthethickness.
简介:BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope(SEM),electron.probemicroanalysis(EPMA)andX-raydiffraction(XRD).theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.
简介:ThispaperintroducesabrazingprocessbetweenAl_2O_3ceramicandInvaralloy.Al_2O_3canbebrazedwithInvareffectively.TheinterfacialstructureofAl_2O_3/Invarjointcanbeexpressedas:Invar/Ag(s,s)+Cu(s,s)+Fe_2Ti(zoneⅠ)/Ag(s,s)+Cu(s,s)+Fe_2Ti+NiTi+Cu_3Ti(zoneⅡ)/Ag(s,s)+Cu(s,s)+Cu_2Ti+Al(s,s)+TiC+TiO(zoneⅢ)/Al_2O_3.Themaximumshearstrengthof139MPawasmeasuredforas-brazedAl_2O_3/Invarjointbrazedat850℃for25minor900℃for15min.
简介:Anewhardfacingprocess,reactivebrazecoatingprocess(RBCC)wasstudied,and(TiC+Cr3C2)/FecompositecoatingswerepreparedbyRBCCusingcarbon,Cr3C2,iron,ferrochromiumandtitaniumpowderastherawmaterialsinvacuumbrazefurnace.TheresultsshowthatTiCisin-situsynthesizedinthecoatings.ThemethodsofintroducingCr3C2havegreateffectsonthedistributionofTiC.AddingCr3C2directlytotherawmaterialsforcoatings,fineTiCparticlesaggregateintodiscoidsparalleltothecoatingsurface,whereas,in-situsynthesizingCr3C2incoatings,theaggregationsofTiCarelumpish.Duringbrazecoating,Cr3C2particlesdirectlyaddeddissolveandprecipitatetobecomeneedle-shaped.Thecoatingshaveanevenandsmoothsurfaceandarecombinedwiththeirmildsteelsubstratesbyametallurgicalbonding.
简介:ThedistributionsoftheaxialstressandshearstressinAl2O3-TiC/Q235diffusionbondedjointswerestudiedusingfiniteelementmethod(FEM).Theeffectofinterlayerthicknessontheaxialstressandshearstresswasalsoinvestigated.Theresultsindicatethatthegradientsoftheaxialstressandshearstressaregreatnearthejointedge.ThemaximalshearstressproducesattheinterfaceoftheAl2O3-TiCandTiinterlayer.WiththeincreaseofCuinterlayerthickness,themagnitudesoftheaxialstressandshearstressfirstdecreaseandthenincrease.Thedistributionoftheaxialstresschangesgreatlywithalittlechangeintheshearstress.TheshearfractureinitiatesattheinterfaceoftheAl2O3-TiC/TiinterlayerwithhighshearstressandthenpropagatestotheAl2O3-TiCside,whichisconsistentwiththestressFEMcalculatingresults.
简介:本《指南》编写依据:根据《船级社焊工考试委员会要求》和《船级社材料与焊接规范》编写而成。编写的目的是让焊工了解船舶焊接基础知识,掌握船舶焊接应知应会的施工常识和要求,了解焊工考试内容,提高焊工持证率。