摘要
Intensevisibleemissionsfromdysprosium（Dy3+）ionsdopedglassesbecameprospectivefordiversetechnologicalapplications.Inthispaper,physical,opticalandstructuralpropertiesofmagnesiumborateglassesdopedwithvariedconcentrationsofDy2O3wereexamined.Suchglassesweresynthesisedbymeltquenchingmethodandcharacterizedatroomtemperatureusingseveralanalyticaltechniques.Luminescenceandabsorptionspectra（inthevisibleregion）ofas-quenchedsampleswereusedtoevaluatethephysicalandopticalproperties.XRDpatternconfimstheamorphousstateofas-quenchedsamples.TheFouriertransforminfrared（FTIR）spectraofglassesrevealvariousbondingvibrationsassignedtodifferentfunctionalgroups.UV-vis-NIRspectradiscloseeightabsorptionbandsaccompaniedbyabandforhypersensitivetransitionpositionedat1260nm(6H15/2→6F11/2).ThevaluesofdirectandindirectopticalenergybandgapofthestudiedglassesaredecreasedwiththeincreaseofDy3+ioncontents.Thephotoluminescencespectraofallglassesundertheexcitationof380nmdisplaytwoprominentemissionbandscentredat497nm(4F9/2→6H15/2,blue)and587nm(4F9/2→6H13/2,green).Theachievedintenseluminescencefromtheproposedglasscompositionmaybebeneficialforsolidstatelaserapplications.
出版日期
2018年12月22日（中国期刊网平台首次上网日期，不代表论文的发表时间）