Inordertostudythestresscorrosioncracking(SCC)ofX70pipelinesteelanditsweldjointinacidsoilenvironmentofsoutheastofChina,twosimulatingmethodswereusedhere.Theonewastoobtainthebadmicrostructuresinheataffectedzonebyannealingat1300°Cfor10minandaircoolingtoroomtemperature,theotherwastogetaseriesofsimulatingsolutionsoftheacidsoilenvironment.SCCsusceptibilitiesofX70pipelinesteelsbeforeandafterbeingnormalizedinthesimulatedsolutionswerestudiedbyslowstrainratetest(SSRT)andmicrostructuralobservationoffractureareas.Potentiodynamicpolarizationcurveswereusedtostudytheelectrochemicalbehaviourofdifferentmicrostructures.SCCdoesoccurtoboththeas-receivedmaterialandnormalizedmicrostructureafterheattreatmentasthepolarizationpotentialdecreased.Hydrogenembrittlement(HE)isindicatedoccurringtoalltestedmaterialsat-850mV(vsSCE)and-1200mV(vsSCE).TheSCCmechanismsaredifferentwithinvaryingpotentialrange.Anodicdissolutionisthekeycauseaspolarizationpotentialhigherthannullcurrentpotential,andHEwillplayamoreimportantroleaspolarizationpotentiallowerthanthenullcurrentpotential.
出版日期
2009年02月12日（中国期刊网平台首次上网日期，不代表论文的发表时间）