简介:ThisworkstudiedthecharacteristicsofSiO2distributionandstructureofsilicatephasesinMgO-ZrO2compositessynthesizedbyrawmaterialsoflightfiredmagnesitendzircon,Theresultsindicatethat30wt%-40wt%SiO2contentinthesystemisexistedintheformofcrystallineofforsterite(M2S),theremainderingofSiOcontent(60wt%0-70wt%)isexistedintheglassphase,Thechemicalcompositionofglassphaseiswellagreedwiththechemicalcompositionofmonticellite(CMS).
简介:AnO'-Sialon-Al2O3compositerefractorywaspreparedbyinsitureactionofSi3N4-ZrSiO4-Al2O3mixturewithfusedaluminaaggregates.Densification,insitureactionprocedureandmicrostructureofthematerialwereinvestigatedbymeansofX-raydiffraction,opticalandscanningelectronicmicroscopesandEDAX.
简介:β-sialon/alumina/silicamixturesweresinteredinflowingnitrogenat1500℃and1600℃respectively.ThesinteringpropertiesandmorphologyofsampleswereinvestigatedbySEM,EDSandXRD.Resultsshowthatsinteredpropertiesofthesamplesareinfluencedbysoakingtemperaturesandcompositions.Bulkdensitiesofsamplesareincreasedwiththeincreaseofthesoakingtemperature,whereastheapparentporositiesaredecreased.Masslossofthesinteredsamplesat1500℃islowerthanthatat1600℃,butallthemasslossremainsapproximatelyconstantwiththeincreaseofsialoncontent.Fromthepointofthermodynamicanalysis,ComplexchemicalreactionstakeplaceinsamplesduringsinteringprocessandthevolatileofSiO(g)isresponsibleforthemasslossofsamples.Comparedtocrosssectionmicrostructureofβ-sialon/Al2O3/SiO2mixturessinteredincokepowderbedconsistingofthedensecenterwithwell-developedcolumnofsialonphase,thetransitionalpartwithneedlelikegrainnitrogen-containingphaseandtheloosepartwithshortgranularAl2O3phase,thoseofmixturessinteredinflowingnitrogenisofwell-developedsialonindensecenterandslightlyloosepartwithsialondebris.
简介:MicrostructureandgrainboundarycharacterofhotpressedbinaryAl2O3(mullite,ZrO2)-SiCompositesandquaternaryAl2O3-mullite-ZrO2-SiCcompositewerestudiedbyelectronmicroscopyandmicroanalysis,ResultssuggestthatthereexistgrainboundarysolidsolutionsduetoelementaldiffusionnearSiCandmatrixoxidesgrainboundaries.
简介:MgO-Al2O3-Cr2O3rammingmixesmadeofdifferentrawmaterialshavedifferentmineralstructureanddifferentphysicalpropertiesthoughwiththeidenticalparticlesizedistribution,thesameamountofbinderandchemicalcomposition.Theresidualcarboncontentofthefusedmagnesia-chromematerialmadeinreducingatmosphereisveryhigh,ifthismaterialsisusedintheMgO-Al2O3-Cr2O3rammingmix,itwouldcausespallingofthefurnaceliningduringdrying-out.
简介:ThepaperdescribestheeffectofadditivesAl,Si,SiCandB4ContheexpansionofMgO-ZrO2-Cmaterialafterbeingcoked.TheresultsindicatethatAlandSicannotincreaseitshotandcoldstrength.AlandSiwereoxidizedtoformAl2O3andSiO2respectively,andthenreactedwithCaZrO3orstabilizerinc-ZrO2toformcalciumaluminate,spinel(MA),dicalciumsilicate(C2S)andforsterite(M2S).Meanwhile,α-C2Swastransformedtoγ-C2Sandc-ZrO2tom-ZrO2whentemperaturechanged.AlltheabovereactionsresultedinthedecreaseoftheamountofAl4C3andSiCandtheincreaseinbulkvolume,whichcausedthestructureofMgO-ZrO2-Cmaterialdestroyed.Hence,contrarytotheMgO-Cmaterial,whenaddingAl.andSi,theMgO-ZrO2-Cmaterialwouldbestructurallydeterioratedafterheat-treatmentanditsstrengthandcorrosionresistancedecreased.
简介:Theprinciplesandfeaturesofmicrowavesintering,theapplicationinrefractoriesandsynthesismethodsofZrB2arereviewed.ThesynthesisresultsofZrB2bythermitdeoxidatemethodshowthatproductionpriceofZrB2canbeeffectivelyloweredthroughmicrowavesynthesis.ItwillexpandtheapplicationofZrB2inrefractories.
简介:TherearemanyprocessestoproduceCr2O3fromchrome-ores,DifferentparticlesizerangesofCr2O3powder,finepinmentgradegreenCr2O3andcoarsemetallurgygradeblackCr2O3,aremadebydifferentprocessesinChina,GreenCr2O3assuperfineandadditionandmetallurgygradeblackCr2O3usedtosynthesizeCr2O3graincanbeappliedtorefractories.ItisverydifficultforhighpurityCr2O3tosintertodensificationandTiO2additioniscontributedtodensificationofCr2O3sinteredathightemperature,Cr2O3grainswithrelativedensityof91%-95%aregainedbysinteringCr2O3withTiO2additionandelectrofusingCr2O3rawmaterials.
简介:Inthis,phasecompsitionandthermalexpansionbehaviourofCaOStabilisedrefractorieswerestudied,Specialattentionwaspaidtotheexpasionbehaviourofthreematerialswithdifferentphasecomposition,TheresearchresultsindicatedthattheexpansionbehaviourcouldbeimprovedbymodifyingthestabilizationofZrO2,whichthusleadstotheincreaseinthethermalshockresistanceandpossiblyeroionresistaceofas-obtainedCaOstabilisedZrOmaterial.
简介:Themicrostructureandslagerosionfractaldimensionofreactioninterfaceofβ-Sialon-Al2O3brickusedin300MtironladleofBaosteelhavebeenstudiedbySEMandXRD.Theresultsindicatedthatβ-Sialon-Al2O3brickexhibitedexcellentslagresistance.Themainwearmechanismofβ-Sialon-Al2O3brickismainlyfromthespallingcausedbythermalmechanicalstressandattackedbyslagsecondly.
简介:TheinfluencesoffourkindsofadditivesaddedintothematrixofMgO-Al2O3unbunedproductswereinvestigated,TheresultsshowthatsampleswithproperMgO/Al2O3rationandproperadditionofCr2O3(2%-4%)havegoodthermalshockresistanceandslagcorrosionresistanceaswell,XRDandSEMdeterminationresultsindicatethatakindofcompoundspinel(Mg,Al,Cr)O4wasformedandthemicrostuctureofthesamplesaredenser.
简介:O'-sialon-ZrO2compositebasedonthecheapcommercialavailablezirconandsiliconasrawmaterialscanbeachievedbyusingreac-tionnitridationmethod,Moreattentionwasgiventothenitridingprocessandtheeffectofadditivesonit.Theexperimentalresultsshowthattherearetwonitridationpaths:oneisthedirectnitridationofsiliconpowderandtheotheristhroughthereactionbetweenthemedi-umcompoundZrSi2andthenitrogen.Theeffectsofadditionofcalciaandtheincorpora-tionofBNonthenitridingreactionwerealsoinvestigated,theprimitiveexperimentalresultsdemonstratedthatbothofcalciaandBNcoulddeterioratethenitridingdegree.
简介:TheinfluenceofthreedifferentAl2O3powderonself-flowingaluminacastablewasstudied.MaximumcompactionofsamplewascomputedbyAndresenEquation.TheresultshowedthattheAl2O3powder,whichhasmuchsmallerparticlesize,couldimprovethemicrostructureandthemechanicalpropertiesofcastableunderroomtemperatureandhightemperature.Withthesamepowdersize,theroomtemperaturestrengthofthecastableaddedwithAl2O3powderproPertiesofwhichwerealteredbyaddingmineralizingagent,washigherthanthatofthecastableaddedwithcommonAl2O3powder,buttheflowabilityofthesethreedifferentcastablewasalmostthesame.
简介:Thestabilizationofγ-aluminiumoxyni-tridespinel(γ-AlON)hasbeeninvestigatedbyadditionofMgO,MgAl2O4,etc.,inreactionprocess.Theresultsindicatedthattherearewidersolidsolutionareasnear,Al2O3-richsideinAlN-Al2O3-MgOternarysystems,ThecontentofstabilizedAlONphaseinsamplesisrelatedtoheatingtemperatures,additives,etc.ThelatticeparametersoftheirAlONphasescouldbewelldescribedbytheequation:a0=0.7900+0.0375[MgO]+0.015[AlN](nm)