简介：研究不同碳源下Al2O3-SiC-C铁钩料的性能。分别以球沥青、焦炭和炭黑为碳源,比较了常温下三者的显气孔率、抗折和抗压强度。结果表明,不同种类碳源将对试样的气孔率和抗折强度产生不同程度的影响。

简介：ThegrainrefiningmechanismofC-Mnsteelsheetoncompactstripproduction(CSP)linewasinvestigatedinthisstudy.Thegrainwasabout100μmafterF1passanddecreasedallthewayoftherollingprocess(F2-F6)to15μm.Repeatedphasetransformationexperimentwasconductedtothesteelforgrainrefinement.Thephasetransformationat860℃and920℃canrefinethegrainsizeto7.5μm.

简介：采用碱熔处理样品，酸化后，移取部分溶液稀释后引入ICP测定ZrO2、TiO2、Fe2O3含量，剩余溶液用强碱分离钛、铁、锰等干扰元素后，EDTA—CuSO4法返滴定Al2O3，终点明显，检测重现性好；

简介：High-strengthsteelshavebeenwidelyappliedtoautomotivechassisparts.Inordertoformcomplexshapes,highholeexpansionratesandhighformabilityarerequired.Dualphase(DP)steelhasagoodformability,butapoorholeexpansionrate.Inthiscircumstance,anotherkindofsteelwhichhasamicrostructureofferrite-bainite,ratherthanferrite-martensite,hasbeenfoundtobeanalternativesolution.ItiscalledFBsteel.ThissteelwithSi,CandMnadditionsareappliedinthisstudy.Atwo-stepcooling...

简介：对Q345C钢板表面产生的裂纹进行了宏观和光学显微镜分析。结果显示：裂纹产生于加热炉之后的轧制过程中，另外，1号裂纹上出现的大型杂质有可能是压入的氧化铁皮。

简介：本文就通过采取多种手段、组织灵活多样的课堂教学和上实验课等措施，以调动学习学习《C＋＋语言程序设计》课程的兴趣和主观积极性的实践，能收到良好的教学效果。

简介：为改善南钢2×24m^2生产线烧结矿质量和降低烧结能耗，烧结厂实施应用了热风烧结技术，并进行相应的技术措施，使烧结能耗大大降低，烧结矿质量明显改善，取得了良好的经济效益。

简介：鄂钢利用铌微合金化技术及控制轧制、控制冷却和热处理工艺,自主研发了高炉炉壳用钢WSM50C。WSM50C钢板的焊接性能优良,具有高强度和良好的韧性,质量稳定可靠,能满足用户要求。

简介：A0.06%Clowcarbonsteelwasdeformedintorsionoverthetemperaturerange877-917℃ina2%H2-Argasatmosphere.Strainsof0.25-5.0wereappliedatstrainratesofε=0.04s-1andε=0.4s-1tostudytheformationofferritebydynamictransformation（DT）attemperaturesabovetheAe3.ThecriticalstrainforferriteformationbyDTwasaboutε=0.2anditsvolumefractionincreasedwithstrainanddecreasedwithtemperatureabovetheAe3.Averageferritegrainsizesof1.5μmto5μmwereproduced,whichdecreasedwithstrainrate.Atthelowerstrainrate(ε=0.04s-1)reversetransformation（RT）tookplaceduringdeformationonceanincubationtimeofabout40s,wasexceeded.Anincreaseinstrainratefromε=0.04s-1toε=0.4s-1arrestedRTduringtestingatalltemperaturesasthetotaltesttimesdidnotexceed13s.ThepresentworkshowsthatDTisfavoredathigherstrainratesbyincreasingthedrivingforce（i.e.storedenergy）andbysuppressingRT.

简介：利用金相显微镜、能谱仪以及电子探针对探伤不合格的Q345C钢板进行分析，试验结果表明钢板靠近中心存在断续的数毫米裂纹是引起Q345c钢板探伤不合格的原因。钢板心部严重的C、Si、Mn、S、P元素正偏析、硫化物夹杂聚集、严重的马氏体＋贝氏体偏析带是导致中心产生裂纹的主要原因。根据分析结果提出改进措施以减少和消除此种缺陷。

简介：本文通过分析2号高炉2段水温差随铁中钛的变化情况，提出铁中钛的理想控制范围为0．08－0．10％在正常护炉时，2段28^#冷却壁水温差与铁中钛无关。

简介：ToimprovethemechanicalpropertiesofWC-Al2O3composites,theeffectsoftraceamountofCeO2additivesonthemicrostructureandmechanicalpropertiesoftheWC-Al2O3compositespreparedbyhotpressingwereinvestigated.TheresultsrevealedthattheWC-Al2O3compositesdopedwith0.1%CeO2possessedrefinedmicrostructureandenhancedmechanicalpropertiescomparedwiththatoftheundopedWC-Al2O3composites.TraceCeO2suppressedthedecarburizationofWC,promotedthemicrostructuralrefinement,andimprovedtheinterfacecoherenceoftheWCmatrixandAl2O3.When0.1%CeO2wasaddedtotheWC-Al2O3composites,theeffectofCeO2resultedintheachievementofarelativedensityof98.82%withanexcellentVickershardnessof16.89GPa,combiningafracturetoughnessof9.85MPa·m1/2withanacceptableflexuralstrengthof1024.05MPa.

简介：C厂2号门内机关大楼的斜对面,有一幅约6×10m~2的广告油漆画。画面背景是热火朝天的生产景象,广告词的内容是该厂的几种优质名牌产品。"KL"牌船板钢为其中之一,获国家金质奖,是国际上八国免检产品。C厂得此荣誉确实受之无愧。前后历时

简介：本文介绍了2^#高炉自2000年9月份大修时为提高其装备水平所采用的先进技术以及投产后增铁降耗所取得的成绩，促进了2^#高炉技术经济指标的不断改善。

简介：2005年12月10日,因设备故障引起高炉无计划休风10个多小时,复风后频繁崩料最后导致炉凉,事故处理耗时5天,损失很大。

简介：网状渗碳体的组织结构是影响C86DA帘线钢盘条拉拔断丝的主要原因。为了能够有效的解决成品盘条网状渗碳体的形成概率降低下游客户拉拔断丝频次，本文主要从网状渗碳体的形成原因入手抓住轧钢工序中可控点，在原有工艺的基础上把加热二段温度提高10℃，均热段提高20℃，加热时间保证在120min以上，2#和3#风机增加10％的开度。结果表明，通过关键参数的调整有效地减轻了C86DA网状渗碳体的形成，达到了下游客户的使用要求。

简介：通过热模拟试验，对Q390C钢的再结晶行为进行了研究。结合中板厂的现场实际条件，制定出使用260mm厚连铸坯轧制75mmQ390C—z15厚板的控制轧制与控制冷却工艺。实践表明，利用该工艺可以在中板厂现有装备条件下生产出满足GB1591—2008的75mm厚Q390C—z15厚板。

简介：Thehot-deformationbehaviorofFe-Mn-Ctwinninginducedplasticity(TWIP)steelwasinvestigatedbyconductinghotcompressiontestswithinarecommendedhotrollingtemperaturerangeatvariousstrainrates.Flowresistancecurvesduringhot-deformationwereobtained,andstrainratesensitivitiesandactivationenergiesforplasticdeformationwerecalculatedusingthepowerlaw.ItisfoundthattheadditionofAlandSiclearlyincreasesthepeakstressesforthepresentalloys,especiallyat950℃.ButMnhasaminoreffectonthestress-straincurvesandactivationenergywhenitscontentvariesfrom15mass%to22mass%forthepresentalloys.

简介：高炉原料中的有害元素锌和碱金属氧化物对炉内砖衬有不同程度的侵蚀作用,研究有害元素对高炉炉衬的危害,并掌握不同的有害元素对高炉生产的影响显得尤为重要。

简介：1996年12月31日我厂2号高炉停炉大修。炉容仍为300m~3,由原来10个风口改为12个风口。炉底、炉缸采用自焙炭砖——陶瓷砌体,水冷炉底、水冷炉喉钢砖。设计顶压60kPa,料车由2.5m~3改为2.8m~3。1997年2月25日点火开炉,开炉后两个月内未能