简介：Thedynamicandstaticrecrystallizationbehaviorsoftwinrollcastlowcarbonsteelstripwereinvestigatedwithanattempttoprovideguidingdeformationparametersfortheonlinehotrolling.Inordertoinvestigatedynamicrecrystallizationbehavior,ascaststripwasreheatedandsoakedwithaustenitegrainsizesimilartothewidthleveloftheascastcolumnarstructure.Tensiletestwasusedandthedeformationtemperatureisintherangeof900℃to1100℃andstrainratesare0.01s-1,0.1s-1,1s-1.Theactivationenergyandstressexponentweredeterminedas306kJ/moland4.69respectively.Theratioofcriticalstraintothepeakstrainis0.65,andthatofcriticalstresstothepeakstressis0.92.ThedependenceofthepeakstrainontheinitialgrainsizeandZener-HollomonparametersZisεp=9.1×10-4×D00.48Z0.13.Thekineticsofthedynamicrecrystallizationandrecrystallizedgrainsizewaspredictedusingmodelspublished.Theascastcoarseausteniteweredramaticallyrefinedaftercompletedynamicrecrystallization.Forstaticrecrystallization,thetensiletestwascarriedoutonGleeble-3500thermo-mechanicalsimulator.Thedeformationtemperatureisintherangeof800℃to1200℃withstrainrate0.01s-1to1s-1.Theprestrainisfixedat0.04to0.12andtheinter-hitdelaytimevariesfrom1sto3000s.TheactivationenergyandAvramiexponentofstaticrecrystallizationweredeterminedas241kJ/moland0.54respectively.Akineticsmodelwasproposedtodescribethestaticrecrystallizationkinetics.Thepredictedresultswereingoodagreementwiththeexperimentalresults.

简介：AttheinitialoperationstageofthecontinuousbloomcasteratBaosteel,alotofcentralporosityandcracksoccurredinblooms,especiallyinthebloomsofhigh-pressureboilersteel.Inthisstudy,amodelofheattransferandsolidificationwassetuptoanalyzetheprocessofcontinuousbloomcasting.Basedonthemodel,thedistributionsoftemperaturefieldandshellthicknesswereobtained,themushyzonewasdefined,andtherebythetechnologyofsoftreductionforbloomswasdeveloped.Afterseveraltestswereconducted,areasonabletestplanwasdeveloped,whichledtothedeterminationoftheoptimalreductionzoneandgaugereduction.Now,centralporosityandcracksinbloomsarealmostavoidedandtheinnerqualityhasbeenobviouslyimproved.

简介：Thisarticleistrytoexplainoranalyzethekeytechnologiesofcontrollingthesurfacequalityoflowcarbonsteelascaststripthroughinvestigationofinterfaceheattransferbetweensolidifiedshellandliquidsteel.Theoneofthekeytechnologiesofcontrollingsurfacequalityoflowcarbonsteelascaststripisthroughthecastingrollsurfacetextureinordertoachievethehomogeneoussolidificationonthecastingroll.Anotheristhroughformingathinfilmonthecastingrollsurfaceinordertoachieveabalancebetweenrapidsolidificationandhomogeneoussolidification.Thisfilmformedbetweenthetwinrollandthemoltensteelcanbecontrolledbyadjustingthechemicalcompositionandinclusioninliquidsteelthroughcontrollingtheamountofall[O]andfree[O].