简介：BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope（SEM）,electron.probemicroanalysis（EPMA）andX-raydiffraction（XRD）.theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.

简介：

简介：Dynamicsinpartialtransientliquidphasebonding(PTLPbonding)ofSi3N4ceramicwithTi/Cu/Timulti-interlayerwassystematicallystudiedthroughmicro-analysisofjointinterfaces.Theresultsshowthatgrowthofreactionlayerandisothermalsolidificationprocessiondoatthesametime.GrowthofreactionlayerandmovingofisothermalsolidificationinterfaceobeytheparaboliclawgovernedbythediffusionofparticipatingelementsduringthePTLPbonding.Coordinationoftheabovetwodynamicsprocessisdonethroughtimeandtemperature.Whenreactionlayerthicknessissuitableandisothermalsolidificationprocessisfinished,thehighbondingstrengthatroomtemperatureandhightemperatureareobtained.

简介：Anewhardfacingprocess,reactivebrazecoatingprocess(RBCC)wasstudied,and(TiC+Cr3C2)/FecompositecoatingswerepreparedbyRBCCusingcarbon,Cr3C2,iron,ferrochromiumandtitaniumpowderastherawmaterialsinvacuumbrazefurnace.TheresultsshowthatTiCisin-situsynthesizedinthecoatings.ThemethodsofintroducingCr3C2havegreateffectsonthedistributionofTiC.AddingCr3C2directlytotherawmaterialsforcoatings,fineTiCparticlesaggregateintodiscoidsparalleltothecoatingsurface,whereas,in-situsynthesizingCr3C2incoatings,theaggregationsofTiCarelumpish.Duringbrazecoating,Cr3C2particlesdirectlyaddeddissolveandprecipitatetobecomeneedle-shaped.Thecoatingshaveanevenandsmoothsurfaceandarecombinedwiththeirmildsteelsubstratesbyametallurgicalbonding.