简介：ＴｈｅｒｍａｌｂｅｈａｖｉｏｒｏｆＢ４Ｃｐａｒｔｉｃｌｅｓｕｎｄｅｒｐｌａｓｍａａｒｃｐｏｗｄｅｒｓｕｒｆａｃｉｎｇｃｏｎｄｉｔｉｏｎ￥ＷＡＮＧＸｉｂａｏ；ＺＨＡＮＧＷｅｎｙｕｅ；ＬＵＴｏｎｇｌｉａｎｄＰＥＮＧＪｉｅ(ＨｅｂｅｉＵｎｉｖｅｒｓｉｔｙ...

简介：Anewhardfacingprocess,reactivebrazecoatingprocess(RBCC)wasstudied,and(TiC+Cr3C2)/FecompositecoatingswerepreparedbyRBCCusingcarbon,Cr3C2,iron,ferrochromiumandtitaniumpowderastherawmaterialsinvacuumbrazefurnace.TheresultsshowthatTiCisin-situsynthesizedinthecoatings.ThemethodsofintroducingCr3C2havegreateffectsonthedistributionofTiC.AddingCr3C2directlytotherawmaterialsforcoatings,fineTiCparticlesaggregateintodiscoidsparalleltothecoatingsurface,whereas,in-situsynthesizingCr3C2incoatings,theaggregationsofTiCarelumpish.Duringbrazecoating,Cr3C2particlesdirectlyaddeddissolveandprecipitatetobecomeneedle-shaped.Thecoatingshaveanevenandsmoothsurfaceandarecombinedwiththeirmildsteelsubstratesbyametallurgicalbonding.

简介：Basedonalargeamountofdissectionatweldedinterfaceandquantitativemicroscopicexaminationofweldedrate,thesuitablelimitgreyscalevaluewasdetermined,andtheweldedrateofsuperplasticsolid-stateweldinginterfaceofheterogeneoussteelwassystematicallystudiedbymeansofself-madeultrasonicC-scanningimaginginspectionsystem.Theexperimentalresultsshow:theweldedstateofsuperplasticsolid-stateweldinginterfaceofheterogeneoussteelcanbeconductedtobemoreaccurately,reliablyandquicklyinspectedbymeansofthissystem,andtheultrasonictestingresultsaregoodconsistentwithactualexaminationresultsoftheinterfacedefectivedistribution.Withintheextentofthesuitbleweldedrate,theweldedratein40Cr/T10Asuperplasticweldingprocesstestedbythissystemislinearwithitstensilestrengthofjoint.

简介：EffectsofalloyelementsonthemicrostructureandcrackresistanceofFe-C-Crweldsurfacinglayerwereinvestigated.Theresultsshowthatmicrostructuresofthelayermainlyconsistofcarbidesandaustenitematrix.IncreasingCandCrcontentsimpairthecrackresistanceofthelayerduetoincreasedamountofbrittlecarbides.TheadditionofNi,NborMoimprovesthecrackresistanceofFe-C-CrweldsurfacinglayerbyincreasingtheamountofausteniteandformingfineNbCorM7C3carbidesinthelayer.But,theexcessiveNb(>2.50wt%)orMo(>1.88wt%)impairsthecrackresistanceofthelayer,whichhasrelationwithincreasedcarbidesorcarbidecoarseningandaustenitematrixsolidsolutionstrengthening.ThepropercombinationofC,Cr,Ni,NbandMocanfurtherimprovenotonlythecrackresistanceofFe-C-CrweldsurfacinglayerbutalsotheerosionresistanceasaresultoffineNbCandM7C3carbidesdistributinguniformlyinaustenitematrix.Theoptimallayercompositionsare3.05wt%C,20.58wt%Cr,1.75wt%Ni,2.00wt%Nband1.88wt%Mo.

简介：北京市东升电焊机厂生产的ZX7-400ST手/氩两用焊机是具有国内先进水平、高效节能的焊接设备,具有直流手工电弧焊和直流氩弧焊两种工作方式。该焊机使用IGBT模块为开关元件,采用脉宽调制技术实现电流控制,具有良好的动特性和电网波动自动补偿功