简介：Fournewlow-band-gapalternatingcopolymers(P-1,P-2,P-3andP-4)basedonelectron-richbenzodithiopheneandnewlydevelopedelectron-deficientunits,thienopyrazineordithiadiazatrindenederivatives,weresynthesizedbyStillepolycondensation.Allpolymersexhibitgoodsolubilityincommonorganicsolventsandabroadabsorptionbandinthevisibletonear-infraredregions.Thefilmopticalbandgapsofthepolymersareintherangeof1.28-2.07eVandthehighestoccupiedmolecularorbital(HOMO)energylevelsareintherangeof-4.99eVto-5.28eV.Bulkheterojunctionpolymersolarcells(PSCs)ofthepolymerswerefabricatedwithphenyl-C61-butyricacidmethylester(PC61BM)asacceptormaterial,andapowerconversionefficiencyof0.80%wasrealizedwithP-1asdonormaterial.

简介：一系列新奇低乐队差距施主领受人(D-A)类型在主要的链(M1)并且在由电子缺乏的领受人块组成的器官的共聚物(BT-F-TPA，BT-CZ-TPA和BT-SI-TPA)悬挂(M2)是与不同电子富人一起的polymerized施主(M3M5)块，即，9,9-dihexyl-9H-fluorene，N-alkyl-2,7-carbazole，和2,6-dithinosilole，分别地经由铃木方法。这些聚合物展出了相对低的乐队差距(1.651.88eV)和宽广吸收范围(680740nm)。作为电子施主合并这些聚合物的体积异质接面(BHJ)太阳能电池，相配与[6,6]-phenyl-C61-butyric酸甲基酉旨(PC61BM)或[6,6]-phenyl-C71-butyric酸甲基酉旨(PC71BM)作为在不同重量的电子领受人，比率下面被制作并且测试与白光的照明的AM1.5的100mW/cm2。包含施主BT-SI-TPA和领受人PC71在1:2重量比率的BM显示出1.88%的最好的力量变换效率(PCE)值，与开的电路电压(Voc)=0.75V，短路电流密度(Jsc)=7.60妈/厘米2,并且充满因素(FF)=33.0%。