简介:Byanalogueexperimentofexhaustgas,thesensitivecharacteristicsoftitaniatoair/fuelratiowasinvestigated.Theeffectsofsomeimpuri-tiesontheelectricconductivityofTiO2,thedeviationof(A/F)cfrom(A/F)sinnonequilibriumgassystemandtheself-catalyticoxidationofTiO2wereexplainedrespectively.Theeffectsofca-talyst,porosityandthicknessofsensorelementontheresponsetimewasalsoanalyzed.
简介:在电的运输性质上评估Ni替换的影响,p类型skutteruditesRyFe3NiSb12(R=Ba,Nd和Yb)系统地从2.5K被调查到800K。由小心地修改三fillers,Ba,Nd和Yb的充满的部分,搬运人集中精确被调整,它按比例改变到数统治的原子价计算的名字的价值。活动性和Seebeck系数的搬运人集中依赖表示在原子价乐队的二乐队贡献,和为热电的性能的优化搬运人集中在之间(5–9)×1020厘米−3。样品的热电导率用稀土元素的元素(Nd和Yb)填满的格子作为与相比显著地更低充满Ba,由于更低的反响的频率并且部分充满。与公司替换相比,Ni替换趋于关上乐队差距,它为RyFe3NiSb12。然而由于状态的密度的改进,当搬运人集中是类似的时,RyFe3NiSb12比RyFe2公司2在更低的温度范围的Sb12。0.73的ZT价值为Yb0.77Fe3在600K的NiSb12。
简介:Samplesofacobalt-basedalloythatunderwentasurfacetreatmentwereevaluated.Thesamples,whichwereobtainedbycastingalloyASTMF75,weregroundandpolishedononesideuntilamirrorfinishwasobtained.Thesampleswereencapsulatedinwollastonite(W)usinguniaxialpressure,treatedat1220℃for1handsubsequentlytemperedinwater.Thecharacterisationofthesampleindicatedthatpartoftheceramicencapsulatingmaterialwasmechanicallyincorporatedonthemetallicsurfacebygrowthoftheoxidelayerofthealloy.Afterthermaltreatment,aseriesofspecimensweresubmergedinasolutionwith5-foldsimulatedbodyfluid(5SBF)for3,5and21days.Characterisationbyscanningelectronmicroscopy(SEM),energydispersivespectroscopy(EDS)andX-raydiffraction(XRD)indicatednucleationandgrowthofahomogenouslayerofapatite,beginningonthethirddaywhenthesamplewassubmerged.
简介:三新奇Ba_5RNiNb_9O_(30)(R=La,Nd和Sm)陶艺在BaO-R_2O_3-NiO-Nb_2O_5系统被准备并且描绘。所有三混合物areparaelectjicphasesadopting。在房间温度的充满的四角形的钨铜(TB)结构。在1MHz,Ba_5RNiNb_9O_(30)陶艺有高电介质在范围193-245.3,在范围0.0059-0.0087的低绝缘的损失,和在范围的绝缘的常数(tau_e)的温度系数的常数-1140-1310X10~(-6)中心点degC。他们绝缘的常数的温度系数显著地Ba_5RNiNb_9O_(30)与那些相比被减少(R=La,Nd,Sm)陶艺。
简介:Thestatusandthevariationofelectricalresistanceofimpactedcarbonfiber/epoxy-matrixcompositeswerestudiedbyultrasonicF-scanandelectricalresistancemeasurementTheexperimentalresultsshowsthatimpactdamageenergythresholdvalueofcarbonfabric/epoxy-matrixcompositescandeterminebyusingultrasonicF-scan.Whentheimpactenergyexceedsthethresholdvalue,damageisgeneratedincomposites.Electricalresistanceofimpactedcompositesischangedowingtothecontactofeachcarbonfiberunitincomposites,whichcauseachangeoftheseries-parallelinconductors.Theveracityofdetectingimpactdamageincompositescanbeimprovedinthiscase.
简介:以KF、SbCl3和SnCl2为原料配制乙醇溶胶,通过在Ti基底上涂胶、干燥、预热处理和煅烧等工艺制备出了F—Sb-SnO2/Ti复合电极。以F—Sb—SnO2/Wi复合电极为阳极,镍片为阴极,施加恒电压观测甲基橙电解液的脱色变化,在正交设计试验基础上,考察溶胶涂层数、煅烧温度、掺杂F离子的浓度等因素对甲基橙降解率的影响,结果表明,固定电解参数电压3V,甲基橙浓度50mg/L,添加荆h(Ⅲ)浓度110mg/L,溶液pH=l,优化的溶胶涂层数9,煅烧温度为773K,溶胶中维持Sn/Sb摩尔比9/1时,优化的KF掺杂摩尔比为0.5时,电解75min,甲基橙的降解率达93%。