简介:Vibrationfatigueisthemainfailuremodeofcompressorblade.Evaluatingthevibrationstressofbladethatleadstocrackingisveryusefulforanalysisofvibrationfatigue.Inthispaper,fatiguestressestimationmethodsbyquantitativefractographywerestudiedthroughexperimentalbladeandin-servicefirst-stagecompressorbladeinordertoevaluatetheinitiationvibrationstressofin-serviceblade.Theanalysisprocessofinitiationvibrationstresswasestablished.Theevaluatingresultofvibrationstressofin-servicebladesubjectedtocentrifugalforceandbendingvibrationstressagreeswithaeroenginetestresult.Itisshownthattheevaluationmethodcannotonlyevaluatetheequivalentfatiguestressesofdifferentcrackdepthsbutalsoyieldtheinitiationequivalentfatiguestress.
简介:ScanningElectronMicroscopyStudiesofYBa_2Cu_3O_(7-δ)SuperconductorsShaWei(沙维)(DepartmentofCivilEngineering,TheQueen′sUniversit...
简介:Thequenchsensitivityandtheirinfluentialfactorsof7,021,7,085,and7,050alloyswereinvestigatedbytheendquenchingtestmethodandthemeasurementofelectricalconductivity,hardness,andmicrostructureafteraging.Theresultsindicatethat7,050alloyhasthelargestchangeswithhardnessdecreasingfromHV199toHV167,andelectricalconductivityincreasesfrom16.6to18.2MSm-1whenthedistancefromquenchedendincreasesfrom2to100mm.Alloys7,085and7,021haverelativelysmallerchanges.Accordingtotherelationshipbetweenthehardnessandelectricalconductivityofasupersaturatedsolidsolution,7,050alloyhashigherquenchsensitivitythan7,085and7,021alloys.Themicrostructureof7,050alloywithhighermajoralloyelement(Zn+Mg+Cu)additionandCuelementadditionismostlyaffectedbythechangesofdistancefromquenchedend.In7,050alloy,thesizeofintragranularprecipitatesisfromabout10–200nm,andthe(sub)grainboundaryprecipitatesareabout20–300nm.Alloy7,085withlowerCucontentismoderatelyaffected,while7,021isleastaffected.Itisfoundthatwiththeincreaseofdistancefromquenchedend,quenched-inducedprecipitatepreferentiallynucleatesandgrowsinthe(sub)grainboundaryandthenonthepre-existingAl3Zrparticles.