简介：Luminescentpolystyrenemicrosphereswereeasilyfabricatedfrompoly(styrene-co-methacrylicacid)andaqueousRE(III)chloridesolution(RE=Eu,Tb)inthepresenceof2,20-bipyridineassecondligand.Thenegativechargesofcarboxylgroupsonthesurfaceofmicrospherescoordinatedwithrareearthionsatfirst,suchascomplexescovalentlylinkedto2,20-bipyridine,resultinginstrongphotoluminescence.Variousmethods,includingtransmissionelectronmicroscope(TEM),scanningelectronmicroscope(SEM),energydispersivespectroscopy(EDS),Fouriertransforminfraredspectroscopy(FT-IR),andfluorescencespectrophotometer,wereusedtocharacterizetheresultantpolystyrenecompositemicrospheres.Thisworkhighlightstheideathatitisfaciletosynthesisluminescentmicrospheresbysurface-modifiedmethoddirectly.

简介：SiC/Si<潜水艇class=“a-plus-plus”>3N<潜水艇class=“a-plus-plus”>4合成是用自我繁殖的高温度的燃烧合成-Si3N<潜水艇class=“a-plus-plus”>4粉末和适当数量原文如此搽粉。两个都，sintering添加剂，系统被使用，它是YAN(Y2O3艾尔2O3AlN)并且YN(Y2O3AlN)。影响在SiC/Si的sintering行为上原文如此满意<潜水艇class=“a-plus-plus”>3N<潜水艇class=“a-plus-plus”>4合成被调查。结果证明有二个sintering添加剂系统的样品的密度，收缩，弯曲力量，坚硬，和破裂坚韧随内容的增加增加第一原文如此然后甚至当原文如此内容不断地增加时，减少。样品的重量损失的趋势是相反的。有最好的机械性质的样品原文如此满意在二个系统是不同的。为YAN系统，当原文如此内容到达10时，样品的最好的机械性质被获得?%，当至于YN系统它是5时?%。YN样品的性质比YAN样品优异。J阶段(2Y2O3吠敨爠畯整漠?灡汰楹杮氠睯瀠敲獳牵?景???慐漠?桴?獡搭獩牰灯牯楴湯瑡摥朠敲湥挠浯慰瑣搠牵湩?桴?敤潳灲楴湯爠'啼礃A慮楴湯瀠潲散獳椠?楳畴栠瑯搠晥牯慭楴湯椠??灳牡?汰獡慭猠湩整楲杮?偓?猠獹整?慣?扯慴湩挠浯汰瑥汥?敲潣扭湩摥丠??洠条敮?楷桴朠潯?湡獩瑯潲祰愠摮洠条敮楴?牰灯牥楴獥?桔?慭楸畭?慭湧瑥捩瀠潲数瑲敩??????汣獡?愢瀭畬?汰獵?慭?猯'T?????鮪徬鞪??极脿???醰鑛??鴿鎘銳????�

简介：BasedonthetechniqueforpreparingLaCl3viadirectpyrolysisofrareearthchloridesolution,ajetpyrolysisreactorwasdesignedandtheintra-reactortemperatureandchemicalreactionswerenumericallysimulatedusingcomputationalfluiddynamics(CFD)technique.Theresultsshowthattheflowratevariationatthefuelinletdoesnotlargelyaffectthetemperatureinthereactor,whiletheincreaseinexternalpressureatthematerialinletrapidlydecreasestheaveragetemperature,Venturitemperature,andoutlettemperature.TheCH4andO2insidethereactorarecombustedcompletely,andwhenthematerialinletpressureis\90Pa,theLaCl3isfullypyrogenated.ThecontentsofCO2,La2O3,andHClfluctuateneartheVenturitubeandfinallystabilize.La2O3contentattheoutletisinatop-to-bottomgradient.

简介：研究烧结温度对含Mn-Nb-Tb的Zn-V-O基陶瓷显微组织和压敏性能的影响。结果表明,随着烧结温度由875°C升高到950°C,烧结陶瓷样品的密度由5.55g/cm3降低到5.45g/cm3,其平均晶粒尺寸由4.1μm增大至8.8μm,击穿场强由7443V/cm显著降低至1064V/cm。经900°C烧结的压敏陶瓷样品具有明显的非线性特性,其非线性系数为49.4,漏电流密度为0.21mA/cm2。当烧结温度由875°C升高到950°C时,Zn-V-O基陶瓷样品的介电常数由440.1增大到2197.2,其损耗因数的变化范围为0.237-0.5。因此,本研究中Zn-V-O基陶瓷组分和烧结条件有利于以银为内电极的先进多层芯片压敏电阻的开发。

简介：2015年6月15日,覆铜板行业协会(CCLA)在苏州举办了"CEM-3UL标准讨论会"。全国生产CEM-3的12家CCL企业的19名代表参加了会议。CCLA(中电材协覆铜板分会,ULSTP796小组成员)为了让UL新标准草案更能反映我们中国厂家的诉求,让中国大陆的厂家尽早获取相应信息,特邀请美国ULSTP796小组专家、IPC基材材料组主席、ESSEXTechologiesGroup,Inc.总裁DouglasJ.Sober先

简介：HotcompressionbehaviorofTiC–Al2O3/AlcompositeswasstudiedusingtheGleeble-1500systematatemperaturerangeof300–550°Candatstrainraterangeof0.01–10.00s-1.TheassociatedstructuralchangeswerestudiedbyTEMobservations.Theresultsshowthatstressleveldecreaseswithdeformationtemperatureincreasingandstrainratedecreasing,whichcanberepresentedbyaZener–Hollomonparameterinanexponent-typeequationwithhotdeformationactivationenergyQof172.56kJ·mol-1.Dynamicrecoveryoccurseasilywhenstrainratesarelessthan10.00s-1.Dynamicrecrystallizationcanoccuratstrainrateof10.00s-1.

简介：采用丝印法在铝基板上制备具有低室温电阻率、适中热敏常数的负温度系数BaCo0.02ⅡCo0.04ⅢBi0.94O3/Ba0.5Bi0.5Fe0.9Sn0.1O3复合热敏厚膜。采用数字多用表、吉时利2400和阻抗分析仪对热敏厚膜的电学性能进行表征。结果表明：随着Ba0.5Bi0.5Fe0.9Sn0.1O3含量从0.05增加至0.25,厚膜的室温电阻率、热敏常数和峰值电压均有所增加且分别处于1.47-26.5Ω·cm、678-1345K和18.9-47.0V范围内,厚膜峰值电压对应的电流也有所降低且处于40-240mA范围。阻抗谱测试表明,这些热敏厚膜表现出非正常的异质电学微结构行为,由高阻态的晶粒和较低电阻态的晶界区域构成。由此可知,在BaCo0.02ⅡCo0.04ⅢBi0.94O3中添加Ba0.5Bi0.5Fe0.9Sn0.1O3改善了热敏行为但也恶化了电流特征.

简介：ExtractingB2O3fromcalcinedboronmud(CBM)wasstudied.TheeffectoffactorssuchasreactiontemperatureandNaOH-to-CBMmassratioonB2O3extractionefficiencywasinvestigated.TheresultsshowthatincreasingreactiontemperatureandNaOH-to-CBMmassratioincreasesB2O3extractionefficiency.TherearetwostagesfortheB2O3extractingprocess:0–20ministhefirststage,whichisrapid;20–50ministhesecondstage,whichisslowerthanthefirststage.Theoverallextractingprocessfollowstheshrinkingcoremodel,andthefirstandsecondstagesaredeterminedtoobeythesurfacechemicalreactionmodelandthediffusionthroughtheproductslayermodel,respectively.Theactivationenergiesofthefirstandsecondstagesarecalculatedtobe41.74and15.43kJ·mol-1,respectively.TheB2O3extractingkineticsequationsofthefirstandsecondstagesarealsoobtained.

简介：镍钛形状记忆合金样品分别在573、723和873K时效2h。在573和723K时效的镍钛样品中,可以观察到2个R相变体,而且这2个R相变体与B2基体之间的取向关系可以确定。在573和723K时效的镍钛样品中,细小均匀的Ni4Ti3沉淀相与B2奥氏体基体之间保持共格关系。在873K时效的镍钛样品中,可以观察到Ni4Ti3沉淀相在晶粒内部和晶界处析出,不均匀的Ni4Ti3沉淀相与B2基体之间保持共格、半共格和非共格关系。对于873K时效的镍钛样品,加热时发生B19’马氏体向B2奥氏体转变的一阶相变,但在冷却时发生B2-R-B19’的二阶相变。723K时效的镍钛样品在冷却时也表现出B2-R-B19’的二阶相变,但在加热时发出B19’-R-B2的二阶相变。对于573K时效的镍钛样品,由于Ni4Ti3沉淀相周围的局部应力不均匀和局部成分不均匀,则其发生三阶相变。

简介：通过水热法成功合成Co3O4/CuO复合物,并探索十六烷基三甲基溴化铵（CTAB）和聚乙烯吡咯烷酮（PVP）对其形貌和性能的影响。用X射线衍射仪（XRD）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）和氮气吸附-脱附测试表征其微观结构和表面形貌。采用循环伏安、恒流充放电和交流阻抗测试等方法研究样品的电化学性能。结果表明,多孔Co3O4/CuO-CTAB纳米片具有最好的电化学性能,在电流密度1A/g下的比容量达398F/g,而在10A/g时其比容量仍能保持90%。此外,该复合物具有很好的循环稳定性,在2000次循环后容量几乎没有衰减。

简介：通过水热法成功合成Co3O4/CuO复合物,并探索十六烷基三甲基溴化铵(CTAB)和聚乙烯吡咯烷酮(PVP)对其形貌和性能的影响。用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和氮气吸附-脱附测试表征其微观结构和表面形貌。采用循环伏安、恒流充放电和交流阻抗测试等方法研究样品的电化学性能。结果表明,多孔Co3O4/CuO-CTAB纳米片具有最好的电化学性能,在电流密度1A/g下的比容量达398F/g,而在10A/g时其比容量仍能保持90%。此外,该复合物具有很好的循环稳定性,在2000次循环后容量几乎没有衰减。

简介：Twinninganddetwinningaretheimportantdeformationmodesinmagnesiumalloysduringcyclicloadingatroomtemperature.Toanalyzethesetwodeformationmechanism,cycliccompression–tensionexperimentswereperformedonMg–3Al–1Znrolledsheetalongtherollingdirection.Inthesetests,themicrostructureevolutionsofaseriesofgrainsduringdeformationweretracedbyusingquasiinsituelectronbackscatterdiffraction(EBSD).ImportantquantitiesliketheSchmidfactorsoftwinningsystem,thefractionoftwinningduringcompression,andthefractionoftwinningafterreverseloadingwerecalculatedonthebasisofmeasuredquantities.TheinfluenceofSchmidfactoroftwinningvariantsondetwinninguponreverseloadingwasanalyzed.DetwinningwouldprefertoproceedduringreverseloadingiftheSchmidfactoroftwinninginthetwinningareabeforereverseloadingissufficientlylarge.

简介：基于炉渣结构分子和离子共存理论,建立1273-1733K下的PbO-CaO-SiO2-FeO-Fe2O3渣系氧化铅活度热力学模型,计算PbO活度并绘制等活度曲线,考察炉渣碱度Q、氧化铁比率R和温度T对活度NPbO和活度系数γPbO的影响。结果表明,活度系数γPbO的模型计算值与文献测定值吻合程度高,说明该模型能较好地反映该渣系结构本质;NPbO呈拉乌尔正偏差,且随渣中PbO含量的升高而增大,但受温度的影响不明显;γPbO随Q的升高而增大;对于Q〉0.3的碱性渣,γPbO随R的升高而出现极大值。该研究结果可用于现代炼铅工艺的热力学研究和操作优化。

简介：在H2SO4-Fe2（SO4）3体系中研究载金黄铁矿的浸出动力学,探讨反应温度、Fe3＋浓度、硫酸浓度、搅拌速度等对黄铁矿浸出的影响规律。结果表明：在H2SO4-Fe2（SO4）3体系中,在30~75°C下黄铁矿浸出过程主要受化学反应控制Fe3＋浓度与黄铁矿的浸出呈正相关,通过Arrhenius经验公式求得浸出表观活化能为51.39kJ/mol。EDS与XPS分析结果表明：黄铁矿氧化过程中硫的氧化经一系列中间形态,最终被氧化成硫酸根,并伴有部分元素硫生成,符合硫代硫酸根氧化路径机理。