简介:ItiswellknownthatthephotocatalyticactivityofTiO2thinfilmsstronglydependsonthepreparingmethodsandpost-treatmentconditions,sincetheyhaveadecisiveinfluenceonthechemicalandphysicalpropertiesofTiO2thinfilms.Therefore,itisnecessarytoelucidatetheinfluenceofthepreparationprocessandpost-treatmentconditionsonthephotocatalyticactivityandsurfacemicrostructuresofthefilms.ThisreviewdealswiththepreparationofTiO2thinfilmphotocatalystsbywet-chemicalmethods(suchassol-gel,reversemicellarandliquidphasedeposition)andthecomparisonofvariouspreparationmethodsaswellastheiradvantageanddisadvantage.Furthermore,itisdiscussedthattheadvancementofphotocatalyticactivity,super-hydrophilicityandbactericidalactivityofTiO2thinfilmphotocatalystinrecentyears.
简介:TiO2nanoparticleswithdifferentphasesarepreparedbyhydrolysisoftitaniumtetrabutoxideinthepresenceofHCl.ThecompositionandmicrostructureoftheresultingsamplesarestudiedbyXRDandTEM.TheseresultsshowthattherangeofparticlesizeofTiO2isfrom20to30nm.ThemechanismofTiO2photocatalysisreactionhasbeendiscussedextensively.PhotocatalyticactivitiesofnanometerTiO2arealsoevaluatedbydegradationofthecrystalvioletsolution.ExperimentalresultsindicatethatthesynergisticactionofH2O2andultrasonicwavegreatlyenhancesphoto-catalyticreactionofTiO2.
简介:TherelationshipofelectricalpropertiesofMn-dopedBa0.92Ca0.08TiO3PTCR(positivetemperaturecoefficientresistance)ceramicswithtwosinteringscheduleswasdiscussed.UsingTEM(transmissionelectronmicroscope)combinedwithEDS(energydispersiveX-rayspectrometer),theMnionsdistributedatgrainboundarieswereanalyzed.TheresultsshowthatthePTCReffectofMn-dopedPTCRceramicsismoredependentonthesinteringschedulethanthoseofMnfree.ThephenomenonmaybecausedbythevalencestatesvarianceofMnionssegregatedatthegrainboundaries.
简介:ElectrocrystallizationMechanismofTungsteninMoltenKF-B_2O_3-K_2WO_4WenZhenhuanandLiGuoxun文振环,李国勋(GeneralResearchInstiiuteforNo...
简介:本文采用磁粉、X射线、CT和超声等无损检测和金相分析等方法对40CrNi2Si2,MoVA钢制零件的磁痕显示进行了系统分析。研究认为,40CrNi2Si2MoVA钢制零件的磁痕显示为显微成分沿变形方向偏析导致的马氏体转变点Ms差异所致。显微成分偏析是钢锭结晶过程中不可避免的,但可通过优化熔炼工艺参数降低显微偏析的程度。本文还分析了四种磁痕显示的类型及其判别方法。
简介:Thesegregationanddiffusionofboronduringheattreatmentswerestudied.Theinfluenceofboroncontents,agingtimeandappliedstressonFeMo2B2formationwasalsostudied.Finally,theeffectsofboroncontentsandFeMo2B2formationonthehightemperaturestrengthwerestudied.Boronatomsweresegregatedtoprioraustenitegrainboundaryduringnormalizingtreatment.Andtheseboronatomswereslowlydiffusedintothegraininteriorduringtemperingandagingat700℃.TheFeMo2B2phasewasonlyformedafter1,000hagingat700℃inalloycontaining196ppmboron.TheformationofFeMo2B2phaseisacceleratedbytheappliedstress.ItwasexpectedthattheformationofFeMo2B2iscloselyrelatedtotheredistributionofboronatoms.Thetensilestrengthsat700℃areincreasedwiththeincreaseofboroncontents.However,theformationofFeMo2B2phaseresultsinlowertensilestrength.
简介:Byuseofmicro-DTAtechniqueaswellasambientandhightemperatureX-rayanalysisthephasediagramofNaCl-CaCl2hasbeenchecked.Itis.asimpleeutecticsystemwithasolidsolubilityinthesodiumchlorideside.Theeutecticpointisat773K,49mol%NaCl.Theexperimentalresults,especiallythoseoftheX-raydiffractionstudieshaveshowedthattheincongruentcompound4NaCl-CaCl2doesnotexistintheNaCl-CaCl2system.
简介:ThelongafterglowSrAl2O4:Dy,Euphosphorisliabletohydrolyzeinwaterwithdeteriorationoftheluminescentproperty.SrAl2O4:Dy,Euphosphorswerethereforeheatedat60-90℃inTEOSsoltoformasurfacegelandthenheat-treatedat400℃toobtainSiO2coatedphosphors.ObservationbyTransmissionElectronMicroscope(TEM)andX-rayphotoelectronspectroscopy(XPS)showsthatathinsilicafilmformsonthesurfaceofthephosphors.Thecoatingprocedurecanbeillustratedbyafour-stepprocessandthetransparentsilicafilmcansuppressthehydrolysisprocess,sothattheluminescentpropertiesofthephosphorsareunimpairedorevenbetter.
简介:Basedonclustervariationmethod(CVM)andnaturaliterationmethod(NIM),order-disorderphasetransitionintheintercalationcompoundsM1/2TiS2issimulatedbycomputer.Thefavorableconditions,underwhich3a0×a0superstructureisformed,aregiven,andtheresultsareingoodagreementwiththeexperimentsandtheoreticalcalculations.TherelationshipbetweencriticaltemperatureandM-ion-vacancyinteractionparameterislinear.
简介:InordertocontrolthesizeanddistributionofthehighconductiveFe2PinLiFePO4/Fe2Pcomposite,twodifferentcoolingrates(Fast:15℃·min-1,Slow:2℃·min-1)wereemployedaftermechanicalalloying.Thedischargecapacityofthefastcooledwas83mAh·g-1andtheslowcooled121mAh·g-1.TheparticlesizeofthesynthesizedpowderwasexaminedbytransmissionelectronmicroscopyanddistributionofFe2Pwascharacterizedusingscanningelectronmicroscopy(SEM).Inaddition,two-stepheattreatmentwascarriedoutforbetterdistributionofFe2P.X-raydiffraction(XRD)andRietveldrefinementrevealthatLiFePO4/Fe2Pcompositeconsistsof95.77%LiFePO4and4.33%ofFe2P.
简介:Nano-ZrO2wasusedtopreparecompositeelectroplatingbathbyaddingdifferentkindsofdispersantssuchasPEGandMZS.Thecompositeelectroplatingbathwasstudiedbymeansofsedimentationexperimentsandparticle-sizeanalysis.Theresultsshowedthatdispersantswithsimplestructureandsmallmolecularweightcouldnotplaystericrole,however,thehighlydispersedandstabilizednanoparticleNi-ZrO2compositeelectroplatingbathwasobtainedatpHvalueequalingto3byaddingMZSwhichisakindofmacromoleculedispersantwithplentifulbranchedchains.
简介:ZrO2-SnO2compositenanoparticleswerepreparedbyheatingthehydrateprecursorssynthesizedbythechemicalco-precipitationreactionofZrOCl2andSnCl4.Theprecursorswereexaminedbydifferentialthermalanalysis(DTA)andthermogravimetricanalysis(TGA).ThecompositepowderwascharacterizedusingX-raydiffraction(XRD),transmissionelectronmicroscopy(TEM)anddesorptionisotherm(Barrett-Joyner-Halendamethod).Theaveragecrystalsizeofthenanoparticlerangesfrom15to30nmforthesamplecontaining5%-25%ZrO2(massfraction).MostoftheporesintheZrO2-SnO2nanoparficlesareabout10-20nmindiameter.Thecompositepowderispromisingforchemicalsensors.
简介:SpatialDistributionofEL2DefectinSemi-insulatingGaAsRuQiongna;LiGuangpingandHeXiukun(汝琼娜)(李光平)(何秀坤)(TianjngElectronicMaterials...
简介:Thecorrosionbehaviorandanti-corrosionmechanismoftheZn-Ni-Al2O3compositecoatingwereinvestigatedbySEM,EDSandXPS.TheresultsindicatethatthecorrosiontypeoftheZn-Ni-Al2O3coatingsinneutral5wt.%NaClsolutionisuniformcorrosion.ThepresenceofcompactanduniformlydispersednanoaluminaparticlessubstantiallyinhibitsthecorrosionofZn-Ni-Al2O3compositecoatings.Intheinitialcorrosionstage,thecorrosiveproductsofZn-NimatrixformacompactZnCl2·4Zn(OH)2layer.Withthedevelopmentofcorrosion,somenanoaluminaparticlesareembeddedandformaNienrichmentlayer.InNienrichmentlayer,NipresentsasNiandNiO.
简介:LiCoO2thinfilms,whichcanbeusedasacathodematerialinmicrobatteries,weredepositedusingradiofrequency(r.f.)magnetronsputteringsystemfromaLiCoO2targetandinanO2+Aratmosphere.ThefilmswerecharacterizedbyvariousmethodssuchasXRD,SEMandAFM.TheLiCoO2filmswereannealedinairat300,500,700and800℃respectively.Theeffectoftheannealingtemperatureonthestructure,thesurfacemorphologyandtheelectrochemicalpropertiesofthefilmswereinvestigated.TheLiCoO2thinfilmdepositedatroomtemperatureisamorphousandhassmallergrainsize.Withincreasingofannealingtemperature,thecrystallinityofthefilmsispromoted.Whentheannealingtemperatureincreasesto700℃,thefilmshaveaperfectcrystallineLiCoO2phase.TheLiCoO2thinfilmwithoutannealinghasnodischargeplateauandsmalldischargecapacity(about27μAh·cm-2μm).Thedischargecapacityincreaseswiththeincreasingofannealingtemperatureandreaches47μAh·cm-2μmforthefilmannealedwith700℃,whichalsoshowsthetypicaldischargeplateauof3.9V.ThecycleperformanceofLiCoO2thinfilmsofasgrownandannealedatdifferenttemperatureswerestudied.Inthecaseofthefilmwithoutthermaltreatment,thecapacityfadingismuchfasterthanthatofthefilmannealedatdifferenttemperature,showingabout40%capacitylossonlyafter25cycles.However,inthecaseofthefilmannealedat700℃,thecapacityreachestosteadystategraduallyandmaintainedconstantlywithcycling.After25timescycling,thedischargecapacityofthefilmannealedat700℃decreasestoabout36.9μAh·cm-2·μm,only0.8%capacitylosspercycle.
简介:ScanningElectronMicroscopyStudiesofYBa_2Cu_3O_(7-δ)SuperconductorsShaWei(沙维)(DepartmentofCivilEngineering,TheQueen′sUniversit...
简介:TheCurietemperatureof(Nd1-xPrx)2Fe14CoyBcompounds(x=0,0.2,…,1.0andy=O,2,4,6,14)hasbeendeterminedwithACinitialsusceptibilitymeasurement.ItwasfoundthatthevariationsofCurietempera-turewithxisnotlinearfory=0and14,whereasitislinearforothervaluesofy.Thelatticeconstantsof(Nd1-xPrx)2Fet14BweredeterminedbyusingX-raydiffraction.Thelatticeexpansionwasmostlyalongthecaxis,whereasthatalongthea-axisremainedpracticallyzeroforthewholeseries.ItissuggestedthatPratomsmayshowsitepreferenceinR2M14Bcompounds(M=FeorCo).DuetothesubstitutionofCoforFe.thetendencyofsitepreferenceofPrbecomeslesspronounced,whichmaybeattributedtothedecreaseofdiffer-enceofcrystalelectricfield(CEF)actingonthetworareearthsiteswiththeintroductionofCoorFe.Incon-trasttothatofthePratoms,thesitepreferenceofCoiu(Nd(1-x)Prx)2Fe(14-y)CoyBcompoundsdoesnotdependonthecompositionoftherareearthsublattice(R=NdorPr).
简介:AZr-1.15wt%Cr-0.10wt%Fealloywasbeta-quenchedfrom1050℃toproduceasupersaturatedα′-phase,andthenheatedforvaryingtimesattemperaturesfrom650℃to760℃toprecipitateZr(CrFe)2.Athermoelectricpower(TEP)techniqueandtransmissionelectronmicroscopy(TEM)wereusedtomonitorthisprecipitationprocess.UsingtheJohnson-Mehl-Avramiequation,theTEPresultsandalineregressionmethod,theactivationenergyfordiffusionandthediffusioncoefficientofchromium(andFe)inα-Zrhavebeencalculatedover650℃~760℃.Thetemperaturedependenceofthediffusioncoefficient,DCr/α(cm2/s)isdescribedat650℃~760℃bytherelationshipformula.ThecoarseningoftheZr(CrFe)2particlesshowsat1/2dependenceofmeanparticlesizeonagingtime,t.Suchatimedependenceistypicalofcoarseningwhereatomtransferacrosstheinterfaceisrate-controlling.