简介：以2,2,6,6-四甲基-4-羟基哌啶、烯丙基氯和氢氧化钠为原料催化合成4-烯丙氧基-2,2,6,6-四甲基哌啶,分别研究了反应时间、原料配比、溶剂用量和催化剂用量等条件对合成4-烯丙氧基-2,2,6,6-四甲基哌啶反应的影响,确定的最佳操作条件为：反应温度为45～54℃,反应时间5h,反应物摩尔比为：n（烯丙基氯）∶n（2,2,6,6-四甲基-4-羟基哌啶）∶n（氢氧化钠）为0.45∶0.1∶0.4,溶剂用量为10g,催化剂的用量为0.2g（2,2,6,6-四甲基-4-羟基哌啶为0.1mol）,收率可达到95.43%以上,纯度为99.5%。

简介：SlagcorrosionresistanceofMgOZrO2refractorieswasinvestigatedinthiswork.Theresultsindicatethatinanon-orientedelectricsteelslagsystemwithahighratioofcalciatosilica,theslagresistanceofMgOZrO2refractoriescanbedescribedasfollows:ZrO2reactswithCaOformingcalciumzirconatecompoundwhichstrengthensthematerialandblocksthechanneloftheslaginfiltration;however,inanorientedelectricsteelslagsystemwithahighconcentrationofsilicaandthelowratioofcalciatosilica,theslagcorrosionresistanceofMgOZrO2refractoriesisdifferent;ZrO2reactswithCaOformingthecalciumzirconateandsimultaneouslyonemoreproductC2Saswell;C2Scanimprovecorrosionresistancebyblindingporeandenhancingslagviscosity;therefore,itisexpectedtobethemajorreasonfortheenhancedcorrosionresistanceobservedforMgOZrO2refractories.

简介：2,3-戊二酮（乙酰基丙酰）是一种黄色的液体,以二酮的形式存在。然而一些GC分析表明,2,3-戊二酮还会以烯醇的形式存在,如3-羟基戊-3-烯-2-酮,所占比例很小（见图1）。

简介：Al2O3-MgOcastableshavebeenwidelyusedforworkingliningsofsteelladleduetotheirsuperiorhotstrengthandcorrosionresistance.Inthiswork,effectsofmicrosilica,ultrafinealuminaandMgOfinesadditionsontherheologicalbehaviorofthecastableswereinvestigatedbymeansofIBBrheometerV1.0tomeasuretorque(shearstress)undervaryingshearrates.Theresultsshowthatrheologicalpropertiesofcastablesatvaryingshearratesaresignificantlyimprovedwithincreaseofmicrosilicaadditions(from1mass%to5mass%)andcorrespondingdecreaseinwateraddition;thereisonlylittlechangeinrheologicalbehaviorwithvariationofultrafinealuminaandMgOfinesadditions.Optimumultrafinealuminaandmicrosilicaadditionsarerecommendedforcastableswithgoodrheologicalbehavior.

简介：日本炭黑协会近日发布，2月份日本炭黑出货量为5．49万吨，与去年同期相比减少8．2％；这已是连续5个月的同比下降。2月份的炭黑产量为5．61万吨，同比下降7．3％。

简介：该项目位于贵州省安顺市镇宁县丁旗镇，由贵州红星发展股份有限公司投资建设，建设总占地5000m2的砼结构操作平台、库房等建筑物，配置生产所需的工艺设备及给排水设备。年产2万t高纯氯化钡。

简介：Cr2O3canbesinteredwellat1500℃incarbon-embeddedconditionorH2atmosphere.Butthehighchromebearingrefractoriescannotreachdensificationwhensinteredat1700℃for10hinweakreducingatmosphereformedbythecombustionoffuel,anditsapparentporosityisabout18%.Thehighchromebearingrefractoriesaremainlyusedincoalgasifiers.Thetemperatureinthefurnaceisabout1500℃andtheproductsareH2andCO,whicharejustthesinteringconditionsofthedensechromerefractorieswithapparentporositylessthan10%.Thehighchromebearingrefractoriesusedincoalgasifiersmaybesinteredagainandthenshrink,destroyingthegasifierlining.Thethermodynamiccalculationshowsthatitissafeaboutthehighchromebearingrefractoriesusedingasifiers.Itisalsoexplainedthatthehighchromebearingrefractoriescan’tbesintereddenselyinweakreducingatmosphereformedbythecombustionoffuel.Thenewsinteringtechnologiescanbeusedtoimprovethebulkdensityofthehighchromebearingrefractories.

简介：二氧化碳压缩机是整套尿素装置中非常重要的1台动设备，在尿素生产中起着至关重要的作用。为了对尿素装置进行防腐在压缩机二段进口加入工厂空气，但在生产中不可避免的会出现工厂空气水分含量增加的现象。分析了此现象对二氧化碳压缩机系统可能造成的影响，采取了在工厂空气进入压缩机前增设干燥器和改造工艺管线的处理措施，并对效果进行了对比。

简介：本文主要对Li2SiO3粉体的固相法合成及低温烧结进行了研究。研究结果表明：原料浓度、混合介质对Li2SiO3相的合成有一定的影响。选择乙醇为球磨介质、并采用高浓度的原料有利于Li2SiO3相的生成。另外,添加B2O3-MgO复合助剂可有效地降低Li2SiO3材料的烧结温度。

简介：在2012年世界人力车速度挑战赛中，荷兰人力车团队凭借Velox2人力车夺冠。Velox2是一款由帝斯曼合作开发的空气动力型轻质维罗车（velomobile）。作为Velox2人力车的核心部件，其传动系统由帝斯曼的Stanyl”材料制成，这种高性能聚酰胺46材料使荷兰团队在挑战赛中获得了极大的竞争优势。

简介：综述了三（2-羟乙基）异氰尿酸酯合成研究进展,及其在含氯聚合物的锌基复合稳定剂和有机基复合稳定剂中的应用研究进展。