简介：SiC/Si<潜水艇class=“a-plus-plus”>3N<潜水艇class=“a-plus-plus”>4合成是用自我繁殖的高温度的燃烧合成-Si3N<潜水艇class=“a-plus-plus”>4粉末和适当数量原文如此搽粉。两个都，sintering添加剂，系统被使用，它是YAN(Y2O3艾尔2O3AlN)并且YN(Y2O3AlN)。影响在SiC/Si的sintering行为上原文如此满意<潜水艇class=“a-plus-plus”>3N<潜水艇class=“a-plus-plus”>4合成被调查。结果证明有二个sintering添加剂系统的样品的密度，收缩，弯曲力量，坚硬，和破裂坚韧随内容的增加增加第一原文如此然后甚至当原文如此内容不断地增加时，减少。样品的重量损失的趋势是相反的。有最好的机械性质的样品原文如此满意在二个系统是不同的。为YAN系统，当原文如此内容到达10时，样品的最好的机械性质被获得?%，当至于YN系统它是5时?%。YN样品的性质比YAN样品优异。J阶段(2Y2O3吠敨爠畯整漠?灡汰楹杮氠睯瀠敲獳牵?景???慐漠?桴?獡搭獩牰灯牯楴湯瑡摥朠敲湥挠浯慰瑣搠牵湩?桴?敤潳灲楴湯爠'啼礃A慮楴湯瀠潲散獳椠?楳畴栠瑯搠晥牯慭楴湯椠??灳牡?汰獡慭猠湩整楲杮?偓?猠獹整?慣?扯慴湩挠浯汰瑥汥?敲潣扭湩摥丠??洠条敮?楷桴朠潯?湡獩瑯潲祰愠摮洠条敮楴?牰灯牥楴獥?桔?慭楸畭?慭湧瑥捩瀠潲数瑲敩??????汣獡?愢瀭畬?汰獵?慭?猯'T?????鮪徬鞪??极脿???醰鑛??鴿鎘銳????�

简介：ThesubmicronpowdermixturesofTiC-TiN-WC-Mo-C-Nisinteredat1400℃orbelowinvacuumwerestudiedbyX-raydiffraction(XRD),scanningelectronmicroscopy(SEM)andtransmissionelectronmicroscopy(TEM)analyses.TheresultsshowedthatMo2Cformedat800℃orbelow.BothWCandMo2Cdisappearedat1200℃,andTiNdisappearedat1250℃.Inaddition,thevariationsoflatticeconstantsofthetitaniumcarbonitrideandnickelbinderphasewithsinteringtemperaturewereexperimentallyobtained,andthereasonwasanalyzed.

简介：Usingdensityfunctionalmethods,somepropertieswerestudiedsuchastheenergiesandcompositionsoffrontiermolecularorbitalsandtheatomiccharges,whicharerelatedtothereactivebehaviorofthioureascontainingdifferentN-substituentgroupings.ThecalculationresultsindicatethattheN-substituentgroupingshavesignificanteffectontheflotationperformanceofthioureacollectors.Theorderofelectron-donatingabilityisN-propyl-N'-benzyl-thiourea(PBZYTU)>N-propyl-N'-ethyl-thiourea(PETU)>N-propyl-N'-allyl-thiourea(PALTU)>>N-propyl-N'-acetyl-thiourea(PACTU)>N-propyl-N'-ethoxycarbonyl-thiourea(PECTU)>N-propyl-N'-benzoyl-thiourea(PBZOYTU),andtheorderoffeedback-electron-acceptingabilityisPBZOYTU>PACTU>PECTU>>PALTU>PETU>PBZYTU.ThisimpliesthatPBZOYTU,PACTUorPECTUcanreactwithcopperatomshaving(t2g)6(eg)3Cu(II)ort6e4Cu(I)configurationonthesurfacesofcoppersulfidemineralsthroughnormalcovalentbondandbackdonationcovalentbond,andexhibitexcellentlycollectingperformanceforcoppersulfideminerals.Theseareconsistentwiththeexperimentaldatareportedintheliteratures.

简介：本文针对N4／1Cr18Ni9Ti与N4／0Cr25Ni20复合板的特殊焊接要求，根据NB／T47014—2011《承压设备焊接工艺评定》的要求，制备2块N4／1Cr18Ni9Ti试板，2块N4I／0Cr25Ni20试板，尺寸均为500mmX150mmX（4＋14）mm。不锈钢基层采用GTAW打底，焊丝选用HOCr21Ni10，SMAW填充与盖面，焊条选用A302与A402。镍复层的焊接采用手工钨极氩弧焊，焊丝选用含Ti、AI等脱氧元素的ERNi-1焊丝，保护气体选择98％Ar＋2％H2。试板焊接完成，外观检验合格后进行100％RT，检测结果符合JB厂r4730，2—2005I级合格，镍复层进行100％PT，检测结果符合JB／T4730．5—2005I级。两种焊接试板分别取样并做拉伸、弯曲力学性能分析，镍复层焊缝做化学成分分析。通过两块焊接试板试验对比，不锈钢基层焊接材料选择HOCr21Ni10焊丝与A302焊条。镍复层焊接采用ERNi-1焊丝，焊接保护气体为98％Ar＋2％H2。通过焊接工艺评定试验研究，解决了N4／1Cr18Ni9Ti与N4I／0Cr25Ni20复合板焊接问题，提高了用户坩埚的返修质量与再次使用寿命，为使用单位节约了成本。

简介：本文根据管道施工过程中，环氧粉末防腐层经常被划伤这一现象，对其耐划伤性能进行研究，以达到控制质量、提高使用寿命的目的。通过研究，提出了影响环氧粉末防腐层耐划伤性能的主要影响因素，并根据研究结果，计算得出了目前常用环氧粉末防腐层耐划伤性能的可靠厚度和使用可靠度，提出了环氧粉末涂层的理论厚度值和研发方向。研究结论的应用将显著提高管道环氧粉末外防腐层的抗机械损伤性能，保证了防腐层的一体性和管道运行寿命。同时，对降低工程造价、改善涂层结构具有指导意义。

简介：分别采用低强匹配焊丝ER50-6、等强匹配焊丝ER-60G和超强匹配焊丝ER-70G，对高强度钢610L进行焊接，对比三种焊接试样的机械性能、抗裂性以及金相组织，验证焊材的匹配性。

简介：Dynamicsinpartialtransientliquidphasebonding(PTLPbonding)ofSi3N4ceramicwithTi/Cu/Timulti-interlayerwassystematicallystudiedthroughmicro-analysisofjointinterfaces.Theresultsshowthatgrowthofreactionlayerandisothermalsolidificationprocessiondoatthesametime.GrowthofreactionlayerandmovingofisothermalsolidificationinterfaceobeytheparaboliclawgovernedbythediffusionofparticipatingelementsduringthePTLPbonding.Coordinationoftheabovetwodynamicsprocessisdonethroughtimeandtemperature.Whenreactionlayerthicknessissuitableandisothermalsolidificationprocessisfinished,thehighbondingstrengthatroomtemperatureandhightemperatureareobtained.

简介：WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability，evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.

简介：FlameheatingcombinedwithwatercoolingwasusedtostraightenA6N01aluminumalloyweldedjointandeffectofflameheatingpassonitsmicrostructureandmechanicalpropertieswasstudied.ResultsshowedthattheflameinducedtheprecipitationandgrowthoftheMg2SiphaseontheAlsubstrateforthethermalagingA6N01aluminumalloyweldedjoints,thusitledthedecreaseofmicro-hardnessandtensilestrengthoftheA6N01aluminumalloyweldedjointwiththeincreaseoftheheatingpass.However,thefatiguepropertyoftheflameheatedjointwasimprovedbecausetheMg2Siprecipitationhinderedtheinitiationandpropagationofthefatiguecrack.

简介：氮(N)和磷(P)共同做锐钛矿TiO2nanosheets被与外国先锋做的高温度的P跟随的低温度的自我做的N-TiO2认识到。做过程的P能维持好TiO2nanosheets形态学与，这被发现暴露{001}方面。掺杂物的化学状态显示N和P原子在TiO2格子在O地点上代替O。与纯TiO2和做N的TiO2,N-P相比，共同做的TiO2nanosheets在可见轻政体展出更强壮的光吸收和染料分子的更高的降级率。提高的photocatalytic性质被归因于二个因素。一方面，N-P共同做能有效地从3.20～2.48减少TiO2的乐队差距?eV，在可见的光导致吸收的改进政体。在另一方面，存在暴露{001}TiO2nanosheets的方面能在反应导致photogenerated电子和洞的有效分离。

简介：Solventextractionofpalladium(Ⅱ)fromhydrochloricacidsolutionwith2-n-octyl-4-isothiazolin-3-one(OIT)/cyclohexanewasstudied.Effectsofdifferentparametersonextractionefficiencywereevaluated.99.96%and98.26%palladium(Ⅱ)couldbeeffectivelyextractedwith0.018mol·L-1OIT/cyclohexaneof0.1and4.0mol·L-1HClmedium,respectively.Nonpolarsolventandlowaciditycouldimprovetheextractingefficiency,andsuccessfullystrippalladium(Ⅱ)fromtheloadedorganicphasewasachievedwith0.5mol·L-1(NH2)2CSsolution.ItwasproposedthattheextractionofPdcomplexesfromHClmediumproceededthroughtheionassociationmechanismbyslopemethod,NMRandFT-IRspectra.

简介：本文从H2s在石油、天然气采输中对金属基材的腐蚀机理研究、防腐涂层的耐硫化氢腐蚀理论探讨以及与国外同类产品性能比较进行研究分析，证明TC2000SS涂层可以在硫化氢的腐蚀环境获得应用，表现出令人满意的效果。

简介：

简介：Inthispaper,Ni-basedalloycompositecoatingreinforcedbyTi(C,N)particleswasfabricatedonthemildsteelthroughlasercladdingtechnology.Themicrostructureoflasercladdinglayerwasanalyzedbymeansofopticalmicroscopy(OM),X-raydiffraction(XRD)andscanningelectronmicroscopy(SEM).ThewearresistancetestofthecoatingwasevaluatedusinganM-2000tester.TheresultsshowedthattheNi-basedcompositecoatinghadanabilityofrapidsolidificationtoformdendriticcrystalsmicrostructureconsistingofTi(C,N)particulatesuniformlydistributedinthematrix.ItwasfoundthatsomeTi(C,N)particlesaresimilartoberoundinshape,andtheothersareirregular.LasercladdinglayerreinforcedbyTi(C,N)particulateswasfoundtopossessgoodwearresistanceproperty.

简介：对ＨＬＤ－ＦＱＺ－２Ｃ型程控式汽车发电机进行了工况分析和失效分析，同时对其关键易失效部件转子轴进行了受力分析，运用有限元模拟的方法对汽车发电机转子轴进行了应力分析，根据其材料特性Ｓ－Ｎ曲线，得到该型号汽车发电机的疲劳寿命极限，以及一般汽车发电机基于Ｓ－Ｎ疲劳曲线的寿命估计模型，并对再制造汽车发电机产品进行了可靠性预测。

简介：

简介：本文介绍Si3N4(代替部分金刚石浓度）配合铁基（以Fe代Co)结合剂氮化金刚石薄膜涂层节块，可大大降低成本，该节块性能良好，有较高使用效果及经济效益。

简介：针对激光直接沉积修复的1Cr15Ni4Mo3N钢零件在磁粉检测时出现的磁痕现象,采用接触通电、湿磁粉连续法,对设计的试样进行磁粉检测,确定磁痕显示位置;利用光学显微镜对磁痕显示处形貌及修复接头和组织进行观察和研究,分析磁痕的性质和形成原因。研究发现:激光直接沉积修复1Cr15Ni4Mo3N钢在磁粉检测过程中与修复区外轮廓完全重合的磁痕显示是伪磁痕显示,主要是由修复区与基体中奥氏体含量的差异造成的。

简介：

简介：作为材料的重要性质之一，硬度一直受到人们广泛的重视和研究。Cohen和Liu利用第一性原理计算从理论上预言了一种超硬性能的新材料β—C3N4，其体积弹性模量超过金刚石。CVO3组采用微波等离子体化学气相沉积法(MPCVD)，用高纯N2(99．999％)和CH4(99．9％)作反应气体，在单晶Si(100)和多晶Pt衬底上沉积碳氮薄膜，开展了对β-C3N4薄膜的制备与表征的探索性研究，取得了一定的进展。