简介:ScanningElectronMicroscopyStudiesofYBa_2Cu_3O_(7-δ)SuperconductorsShaWei(沙维)(DepartmentofCivilEngineering,TheQueen′sUniversit...
简介:Therulessuchasprocessparametersaffectingjointpropertiesandtheevolutionprincipleofweld'smicrostructurehavebeenresearchedbyadoptingdiffusionweldingprocesstoconnectSiCw/6061Alcomposite.ExperimentalresultsshowthatthereexistsacriticaltemperatureregionbetweensolidandliquidphaselineofSiCw/6061Alcomposite,andtheregionwillshrinkwiththeincreasingofweldingpressure.Whendiffusionweldingoccurredunderthecriticaltemperatureregion,weldingjointexhibitsbadpropertyofbonding,andthematrixandthereinforcementcan'tbondeffectively.Whendiffusionweldingoccurredinthecriticaltemperatureregion,thestrengthofweldingjointchangeswidelywiththevariationofweldingtemperature.Whenweldingtemperaturevariesin10℃,thestrengthofweldingjointwillchangeobviously.Onlywhenweldingtemperatureishigherthanthecriticaltemperatureregion,stablejointpropertiescanbeobtained.Simultaneouslythematrixandthereinforcementhasbetterinterfacialbondedindiffusionweldinginterface,andnoobviousinterfacereactionoccurred,andthusdiffusionweldingofSiCw/6061Alcompositecanbesuccessfullyrealized.
简介:ThemixturemodelofAl85Y4Nd4Ni7alloyinwhichapartiallycrystallizedamorphousalloyisregardedasananocompositeofanAlnanoparticleandaremainingamorphousmatrixispresented.Itsevolutionintheprocessofcrystallizationhasbeeninvestigatedbydifferentialscanningcalorimetry(DSC),X-raydiffraction(XRD),andtransmissionelectronmicroscopy(TEM).Mainlyamorphousstructurewithα-Alnanocrystalsembeddedintheamorphousmatrixhasbeenrevealedbymeltspiningthealloy.Crystallizationisshowedtooccurinthreestages:(1)crystallizationofamorphousalloyandformationofAlNiY,AlNdNiandunknowncrystallinephases,(2)formationofAl3YandAl3Nd,and(3)formationofAl3Ni.
简介:Theeffectofnonmetallicinclusionsinthedropletofthestainlesssteelcoveredelectrodeontheporositywasresearched.Theresultshowsthatthenonmetallicinclusionsinthedropletarespherical,theircompositionisdifferentfromtheoneofslagandtheinclusionshavethecharacterof"innerformation".Whentheratioofrutiletoilmeniteinthecoatedmaterialisincreased,thedropletbecomescoarse,thecontentofnonmetallicinclusioninthedropletdecreases,andtheporositysensitivityintheweldmetalalsodecreases.Whentheratiooffledspartoilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusioninthedropletincreases,andtheporositysensitivityintheweldmetalincreases.WhentheratioofFe2O3toilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusiondecreases,whiletheporositysensitivitydoesnotreduce.
简介:ThesusceptibilityofweldedjointfortheX65pipelinesteeltoH2Sstresscorrosioncracking(SCC)isinvestigated.SCCtestsonthesteelarecarriedoutintheenvironmentbasedonNACETM-01-77solutionwithsaturatedgaseousH2S.Thethresholdstressintensityfactorandcrackpropagationvelocityarecalculatedaccordingtowedge-openingloading(WOL)specimens.Thethree-dimensionalelastic-plasticfiniteelementanalysisofWOLspecimensisperformedbyusingtheFEMprogrammingpackageANSYS.Stressfieldandconcentrationofhydrogendistributionpropertyaheadofthecracktipareobtained.ThispapersurveyedthemicrostructureofweldedjointandstudiedonthemechanicalpropertiesofX65pipelinesteel.Itprovidesexperimentalbasisforstudyingstresscorrosion.Theresultsofnumericalanalysisareconsistentwithconclusionsofstresscorrosiontest.