简介：对弹簧扁钢的全厚度范围进行C扫描成像检测时,需以一定间隔调整焦点位置以确保检测精度。本研究测量了聚焦声束焦柱高度并分析其对C扫描图像的影响,提出了应用于弹簧扁钢全厚度C扫描成像检测的焦距调整法则。此外,通过分析C扫描图像的特征区域确定缺陷边界,并通过金相试验对其进行了验证。研究结果显示：根据焦柱高度确定焦距调整间隔可在提高检测效率的同时保证较高的检测精度,所提出的缺陷图像特征边界可用于精确测量缺陷尺寸;水浸聚焦超声C扫描成像方法可用于评价弹簧扁钢内部缺陷的尺寸及其分布。

简介：ExtractingB2O3fromcalcinedboronmud(CBM)wasstudied.TheeffectoffactorssuchasreactiontemperatureandNaOH-to-CBMmassratioonB2O3extractionefficiencywasinvestigated.TheresultsshowthatincreasingreactiontemperatureandNaOH-to-CBMmassratioincreasesB2O3extractionefficiency.TherearetwostagesfortheB2O3extractingprocess:0–20ministhefirststage,whichisrapid;20–50ministhesecondstage,whichisslowerthanthefirststage.Theoverallextractingprocessfollowstheshrinkingcoremodel,andthefirstandsecondstagesaredeterminedtoobeythesurfacechemicalreactionmodelandthediffusionthroughtheproductslayermodel,respectively.Theactivationenergiesofthefirstandsecondstagesarecalculatedtobe41.74and15.43kJ·mol-1,respectively.TheB2O3extractingkineticsequationsofthefirstandsecondstagesarealsoobtained.

简介：XFP81R·可完全替代进口钢材CENA1或CPM40，帮您降低成本60％以上。·特殊的成份配方经固溶时效处理后晶粒细致硬度均匀。·拥有良好的耐腐蚀性及导热性。·抛光蚀纹性能优异。·放电加工白层浅薄利于后期研磨加工。·适合氮化处理。XF2343R·可完全替代进口钢材1．2343，帮您降低成本至少40％以上。·采用ESR电渣重熔工艺冶炼，材质更加纯净。·材质韧性良好。·具有优良的热处理尺寸稳定性。

简介：通过单向拉伸试验研究镁合金AZ31B的电塑性效应。为了显示脉冲电流的非热效应,在相同温度下开展两类试验：环境箱中的单向拉伸试验和脉冲电流辅助的单向拉伸试验。此外,对脉冲电流在材料变形过程中引起的温度场进行数值模拟。结果表明,沿材料截面方向温度分布均匀。通过对比两类单向拉伸试验的真应力-真应变曲线,证实了脉冲电流非热效应的存在。通过光学显微镜研究脉冲电流对材料微观组织演化的影响,结果表明：脉冲电流引起的动态再结晶对流动应力的下降起重要作用。最后,提出一个考虑电塑性响应的AZ31B流动应力模型,并通过实验进行验证。结果表明：模型预测结果和实验结果吻合较好。

简介：汽车轻质化的发展趋势是一场立足现实，着眼长远的新技术革命。在近期内，汽车重量是燃料经济性方程的几个关键变量之一。公司平均燃料经济性（CAFE）标准规定到2025年时客车的燃料经济性为（平均）50英里每加仑以上。同时，要促使更多客户选择燃料经济性更好的汽车。这些措施迫使OEM在考虑现在和今后车型的燃料经济性时，必须充分考虑各种可能因素，于是汽车轻质化在该过程中发挥了重要作用。