简介：Inthisstudy，theweldingthermalcyclecurveexhibitedtwotemperaturepeaksinhighheat-inputtwin-wireseparate-poolsubmerged-arcweldingandcoarse-grainedheataffectedzoneexistedintheweldedjoint.Theinclusionsofprimaryweldmetalandcoarse-grainedheataffectedzoneofCe-addedSAWshouldbeAl203,MnO,Si02,TiO,Ce2S3,CeS,Ce202SandCe203.Undertheeffectofweldingthermalcycle,oxy-sulfidesinclusionsofCe,thediameterofwhichwaslessthan2.0|Jim,slightlygrewlarger,butthecompositionandtypeoftheinclusionsdidn，tchange.ThemicrostructureofthelargeheatinputweldmetalhadacicularferritethatCeoxidesulphideparticlesinducednucleationandproeutectoidferrite.Inthecoarse-grainedheataffectedzoneofweldmetal,home-positionprecipitationofacicularferriteandsympatheticacicularferritewerebothobserved.Itwassupposedthatpreviouscrystalcellsofacicularferriteinaustenitegrainpromotedhome-positionprecipitationofacicularferrite.Meanwhile,sympatheticacicularferritetendedtonucleateattheprimaryacicularferritegrainboundaries,wherehighdislocationdensitywaslocated,andgrewinsidetheneighboringcarbon-depletedausteniticregions.Thegranularbainitenucleatedintheausteniticzonewithhighcarboncontentclosetoacicularferriteandsympatheticacicularferrite.