简介：Nb-24Ti-18Si-2Al-2Hf-4CrandNb-24Ti-18Si-2Al-2Hf-8Cralloyswerepreparedbyarcmeltinginawater-cooledcrucibleunderargonatmosphere.Microstructuralcharacteristicsandoxidationresistanceofthealloysat1250℃wereinvestigated.Theresultsshowthat,whentheCrcontentis4at%,themicrostructuresconsistof(Nb,Ti)_(ss)andNb_5Si_3;asCrcontentincreasesto8at%,C14LavesphaseCr_2Nbisformed.Theisothermaloxidationtestsshowthattheoxidationkineticsofthetwoalloysfollowsimilarfeatures.Theweightgainsofthetwoalloysafteroxidationat1250℃for100hare235.61and198.50mg·cm~(-2),respectively.Duringoxidation,SiO_2,TiO_2,Nb_2O_5andCrNbO_4areformedatfirst.Then,Ti_2Nb_(10)O_(29)isformedafteroxidationfor20minandbeginstochangeintoTiNb_2O_7astheoxidationproceeds.SiO_2isformedassolidstateatfirstbutlaterevolvesintoglassystatetoimprovethecohesionofthescale.Afteroxidationfor100h,oxidationproductsconsistofSiO_2,TiNb_2O_7,Nb_2O_5andCrNbO_4.

简介：Nb-Ti-Si-based合金粉末被元素的粒子的机械alloying(麻省)准备。形态学，尺寸，阶段成分，雏晶尺寸，格子紧张，作文和内部微观结构的进化，等等，合金，粉末被X光检查衍射(XRD)分析，扫描电子显微镜学(SEM)，精力散的光谱学(版本)，激光粒子尺寸分析器和传播电子显微镜(TEM)分析。合金粒子逐渐地被精制，他们的形状随milling时间的增加变得球状。Nb稳固的答案(Nbss)的衍射山峰分阶段执行移动向从2～5在球milling期间降低2个角度?h，并且在那Nbss衍射以后，山峰变向更高，有milling的增加的2个角度从5～70预定?h，它主要由于alloying元素原子的溶液被归因于Nbss粉末的格子参数的改变进Nb格子形成Nbss。在球milling过程期间，在雏晶尺寸的减少和粉末导致他们的衍射的连续拓宽的Nbss的格子紧张的增加达到顶点。典型薄片状的微观结构为5在球milling以后在粉末粒子内被形成?h并且变得更多随milling时间的增加精制了并且一致。在40-h-ballmilling以后，典型薄片状的微观结构消失并且很同类的微观结构相反被形成。这同类的微观结构被证明由仅仅使过饱和的Nbss阶段构成。

简介：研究流变压铸工艺参数浇注温度、振动频率和蛇形通道弯道数量对Al-30%Si合金的显微组织和力学性能的影响。流变压铸过程中的半固态Al-30%Si合金浆料采用振动蛇形通道浇注工艺制备。实验结果表明：浇注温度、振动频率和通道数量对Al-30%Si合金显微组织和力学性能的影响较大。在浇注温度为850°C、通道弯道数量为12和振动频率为80Hz的条件下，流变压铸工艺制备的样品组织的初生硅晶粒被细化成平均粒径约为24.6μm的块状颗粒；此外，流变压铸样品的抗拉强度、伸长率和硬度分别为296MPa、0.87%和HB155。因此，振动蛇形通道浇注工艺能有效地细化组织中的初生Si晶粒。初生Si晶粒的细化是流变压铸样品力学性能改善的主要原因。