简介：Poroussiliconpillararray(PSPA)sampleswhichareidealsubstantialmaterialswithdominantelectronicandluminescencepropertieswerepreparedbysurfaceetchingmethod.ZnOnanorodswithorwithoutMndopinggrownuniformlyandalignedontoPSPAregardlessoflatticematchingshowvariousphotoluminescence(PL)properties.ThedopedMnionsinZnOnanorodsweredirectlyobservedbyX-rayphotoelectronspectroscopy(XPS),andZnOstructuresweredetectedbyX-raydiffraction(XRD).Asthedopingconcentrationincreases,XRDpeaksofZnOnanorodsshifttolowangle.TheinfluencesofdopingMnionsonluminescencepropertiesofZnOnanorodswereinvestigated.Exceptfortheultraviolet(UV)PLband,thebroadPLbandisobservedatvisibleregion.Thebandcouldbedividedintothreeseparatebands(orange,greenandred)byLorentziandeconvolution.TheintensityoforangePLbandfirstlyincreasesthendecreases,andthengetsthemaximumatthedopingMn-to-Znmolarratioof2.0:100.0whichisthemosteffectivedopingconcentration.ThegreenPLbandisattributedtozincvacancyofZnO,theorangePLbandtoMnionsrecombinationofitself,andtheredPLbandtooxygenvacancyofZnO,respectively.AstheMn-dopedZnOnanorodscouldemityellowgreenluminescenceexcitedbyUVradiation,anddopedMnionscouldimprovethecolorrenderingindexoftheluminescence,thenanorodscouldbeusedaspromisingwhite-lightemittersinthefuture.

简介：Nb-Ti-Si-based合金粉末被元素的粒子的机械alloying(麻省)准备。形态学，尺寸，阶段成分，雏晶尺寸，格子紧张，作文和内部微观结构的进化，等等，合金，粉末被X光检查衍射(XRD)分析，扫描电子显微镜学(SEM)，精力散的光谱学(版本)，激光粒子尺寸分析器和传播电子显微镜(TEM)分析。合金粒子逐渐地被精制，他们的形状随milling时间的增加变得球状。Nb稳固的答案(Nbss)的衍射山峰分阶段执行移动向从2～5在球milling期间降低2个角度?h，并且在那Nbss衍射以后，山峰变向更高，有milling的增加的2个角度从5～70预定?h，它主要由于alloying元素原子的溶液被归因于Nbss粉末的格子参数的改变进Nb格子形成Nbss。在球milling过程期间，在雏晶尺寸的减少和粉末导致他们的衍射的连续拓宽的Nbss的格子紧张的增加达到顶点。典型薄片状的微观结构为5在球milling以后在粉末粒子内被形成?h并且变得更多随milling时间的增加精制了并且一致。在40-h-ballmilling以后，典型薄片状的微观结构消失并且很同类的微观结构相反被形成。这同类的微观结构被证明由仅仅使过饱和的Nbss阶段构成。