简介:
简介:在液相环境中,利用纳秒(ns)脉冲激光器轰击消融铬掺杂ZnSe(Cr^2+:ZnSe)微米颗粒,制备出Cr^2+:ZnSe纳米粒子,扫描电镜以及X射线衍射检测,结果显示,制备所得的粒子为平均尺寸为50nm的ZnSe闪锌矿结构纳米粒子。基于Cr^2+:ZnSe纳米粒子,观察到中心波长为2180nm、阈值为0.4mJ/pulse的随机激光效应。相比于Cr^2+:ZnSe晶体激光器,纳米粒子随机激光的中心波长发生了约170nm的蓝移,Cr^2+:ZnSe纳米粒子的光致发光寿命也比Cr^2+:ZnSe晶体要短。
简介:
简介:Layeredcathodematerialsofhigh-temperaturelithiumbatteries,LiNi1/3Mn1/3Co1/3O2aresynthesizedbyasol-gelmethodwithvariationinfinalsinteringtemperatureforboreholeapplications.Thestructure,morphologyandhigh-temperaturedischargeperformanceoftheseresultingproductsareinvestigatedbyX-RayDiffraction(XRD),scanningelectronmicroscopy(SEM),laserparticlesizeanalysis,galvanostaticandpulsedischarge.Theresultsofstructuralanalysisindicatethatthesamplesinteredat800℃hasthecharacteristicsofgoodcrystallinity,narrowsizedistributionandlargespecificsurfaceareaatthesametime.Thedischargeexperimentsalsoindicatethatthissamplehasthebestelectrochemicalproperties,withthemaximumdischargecapacitiesof314.57and434.14mAh·g-1at200and300℃respectivelyandtheminimumcellinternalresistancesatbothtemperatures.
简介:Anovelfluorescentprobe9-(4-(1,2-diamine)benzene-N1-phenyl)acridine(DABPA)wassynthesizedforthedetectionofnitricoxide(NO)andcharacterizedbyIR,1H-NMRandEI-MSspectroscopy.Basedonaphotoelectrontransfermechanism,thefluorescenceintensitiesofDABPAwereinvestigatedwiththedifferentconcentrationsofNO.Undertheoptimalexperimentalconditions,thefluorescenceintensityofDABPAhadagoodlinearrelationship(R2=0.9977)withNOconcentrationintherangefrom1×10-7to1.5×10-6mol/Lwithadetectionlimitof1×10-8mol/L.ThecytotoxicityinducedbyDABPAwasevaluatedbytheMTT(3-(4,5-dimethylthiazol-2-yl)-2,5diphenyltetrazoliumbromide)assayforbiologicalapplication.Furthermore,theprobeDABPAhadalsobeensuccessfullyappliedtoreal-timeimageNOproducedinPC12cellsinthepresenceofL-arginine.
简介:One-dimensional(1D)nanomaterialsandnanostructureshavereceivedmuchattentionduetotheirpotentialinterestforunderstandingfundamentalphysicalconceptsandforapplicationsinconstructingnanoscaleelectricandoptoelectronicdevices.Zincsulfide(ZnS)isanimportantsemiconductorcompoundofII-VIgroup,andthesynthesisof1DZnSnanomaterialsandnanostructureshasbeenofgrowinginterestowingtotheirpromisingapplicationinnanoscaleoptoelectronicdevices.Thispaperreviewstherecentprogresson1DZnSnanomaterialsandnanostructures,includingnanowires,nanowirearrays,nanorods,nanobeltsornanoribbons,nanocables,andhierarchicalnanostructuresetc.Thisarticlebeginswithasurveyofvariousmethodsthathavebeendevelopedforgenerating1Dnanomaterialsandnanostructures,andthenmainlyfocusesonstructures,synthesis,characterization,formationmechanismsandopticalpropertytuning,andluminescencemechanismsof1DZnSnanomaterialsandnanostructures.Finally,thisreviewconcludeswithpersonalviewstowardsfutureresearchon1DZnSnanomaterialsandnanostructures.
简介:ThetransportpropertiesintheLa2/3(Ca1-xSrx)1/3MnO3(x=0,1/3,2/3)filmspreparedusingtheRFmagnetronsputteringmethodwereinvestigated.TheeffectoftheCa,Srdouble-dopingattheApositionintheLa2/3A1/3MnO3onthestructureofthetargetsandtransportofthefilmshasbeenstudied.Withtheincreaseofx,thestructuresofthetargetstransformfromtherhombohedralphasetothecubicphase;themetal-insulatorphasetransitiontemperature(Tp)ofthefilmsincreases;andthecorrespondingpeakresistivitydecreases.Allthephenomenacanbequalitativelyexplainedbythelatticeeffect.