简介：Anovel,Ti-6A1-4V(Ti64)/Hydroxyapatite(HAat5%byweightconcentration)metal/ceramiccompositehasbeenfabricatedusingelectronbeampowderbedfusion(EPBF)additivemanufacturing(AM):specifically,thecommercialelectronbeammelting(EBMR)process.InadditiontosolidTi64andTi64/5%HAsamples,fourdifferentunitcell(model)open-cellularmeshstructuresfortheTi64/5%HAcompositewerefabricatedhavingdensitiesrangingfrom0.68to1.12g/cm^3,andcorrespondingYoung'smodulirangingfrom2.9to8.0GPa,andcompressivestrengthsrangingfrom-3to11MPa.ThesolidTi64/5%HAcompositeexhibitedanoptimaltensilestrengthof123MPa,andelongationof5.5%incontrasttoamaximumcompressivestrengthof875MPa.Boththesolidcompositeandmeshsamplesdeformedprimarilybybrittledeformation,withthemeshsamplesexhibitingerratic,brittlecrushing.Solid,EPBF-fabricatedTi64sampleshadaVickersmicroindentationhardnessof4.1GPawhiletheTi64/5%HAsolidcompositeexhibitedaVickersmicroindentationhardnessof6.8GPa.ThelowestdensityTi64/5%HAcompositemeshstrutsectionshadaVickersmicroindentationhardnessof7.1GPa.Opticalmetallography(OM)andseanningelectronmicroscopy(SEM)analysisshowedtheHAdispersoidstobehighlysegregatedalongdomainorgrainboundaries,buthomogeneouslydistributedalongalpha(hcp)plateletboundarieswithinthesedomainsintheTi64matrixforboththesolidandmeshcomposites.Thealphaplateletwidthvariedfrom-5μmintheEPBF-fabricatedTi64to-1.1μmfortheTi64/5%HAmeshstrut.TheprecursorHApowderdiameteraveraged5μm,incontrasttothedispersedHAparticlediametersintheTi64/5%HAcompositewhichaveraged0.5μm.ThisworkhighlightstheuseofEPBFAMasanovelprocessforfabricationofatruecompositestructure,consistingofaTi64matrixandinterspersedandexposedHAdomains,whichtotheauthorsknowledgehasnotbeenreportedbefore.Theresultsalsoillustratetheprospectsnotonlyforfabrica

简介：云南省有着极其丰富的竹资源,少数民族传统竹艺及竹制品与人民生活息息相关,竹文化是民族文化的重要组成部分。然而随着时代背景的变化,一些蕴含生活智慧的传统竹艺却在消失。挖掘传统竹工艺精髓,使其'活化'为今用,是竹艺传承最好的方式。文章归纳了云南竹艺特征及竹艺制品特点,分析了现代竹制品的审美倾向,并在此基础上,提出了结合现代审美观念的设计立场、功能、形式、工艺等四方面的创新策略,旨在让云南传统竹艺制品焕发新的生命力。