简介:利用角分辨紫外光电子谱对乙烯和乙炔气体在Ru(1010)表面的吸附及与K的共吸附的研究结果表明:当衬底温度超过200K,乙烯即发生脱氢反应,σCH和σCC能级均向高结合能方向移动。在室温下,σCH和σCC能级位置与乙炔在Ru(1010)表面的吸附时的分子能级完全一致。乙烯发生脱氢反应后的主要产物为乙炔。衬底温度从120K到室温,Ru(1010)表面上乙炔的σCH和σCC能级均未发现变化。室温下乙炔仍然可以在Ru(1010)表面以分子状态稳定吸附。在有K的Ru(1010)表面上,室温时σCC谱峰几乎。碱金属K的存在促进了乙炔的分解。
简介:ThisworkinvestigatedC2F6/O2/ArplasmachemistryanditseffectontheetchingcharacteristicsofSiCOHlow-kdielectricsin60MHz/2MHzdual-frequencycapacitivelycoupleddischarge.FortheC2F6/Arplasma,theincreaseinthelow-frequency(LF)powerledtoanincreasedionimpact,promptingthedissociationofC2F6withhigherreactionenergy.Asaresult,fluorocarbonradicalswithahighF/Cratiodecreased.Theincreaseinthedischargepressureledtoadecreaseintheelectrontemperature,resultinginthedecreaseofC2F6dissociation.FortheC2F6/O2/Arplasma,theincreaseintheLFpowerpromptedthereactionbetweenO2andC2F6,resultingintheeliminationofCF3andCF2radicals,andtheproductionofanF-richplasmaenvironment.TheF-richplasmaimprovedtheetchingcharacteristicsofSiCOHlow-kfilms,leadingtoahighetchingrateandasmoothetchedsurface.
简介:采用EXAFS方法研究了经中温等温和低温LN2处理的2mol%Y2O3-ZrO2陶瓷中Zr^4+和Y^3+离子的近邻结构。结果表明,与中温等温试样相比,LN2处理的试样中Zr-O层和Zr-Zr(Y)层的配位数显著减少,平均键长明显缩短;Y-O层配位数减少,Y-Zr(Y)层平均键长伸长;各配位层畸变程度均增大。两个试样的Y-O层配位数均高于Zr-O层配位数,表明点阵中的氧空位倾向于与Zr离子为邻。分析认为,该试样Zr-O配位层中较多的氧空位主要来源于从高温快速冷却时所保留下来的Schottky缺陷,对四方相稳定性和中温相变具有重要的影响。
简介:本文通过高分辨X射线衍射及掠入射(GID)的实验方法对生长在SrTiO3衬底上的LLa2/3Ca1/3MnO3和YBaCu3O7单层膜及YBa2Cu3O7-x/La2/3Ca1/3MnO3异质结构双层薄膜的微结构进行了研究。结果发现,所有薄膜都呈c向生长。由于热膨胀系数的不同而引起的热应力使得LCMO膜的晶格参数与靶材的相差较大。La2/3Ca1/3MnO3在单层腹及双层膜中都由靶材的立方结构变成了薄膜状态的四方结构。YBa2Cu3O7在单层膜及双层膜中都由靶材的正交结构变成了薄膜状态的四方结构。La2/3Ca1/3MnO3膜与YBa2Cu3O7膜在不同的样品中处于不同的应力状态。
简介:
简介:利用XRD、TPR和EXAFS等手段考察了焙烧温度对Cu/MnO2/ZrO2催化剂性能影响,结果表明,随着焙烧温度增加,铜的配位环境发生变化,铜和锰之间相互作用增强,有效地防止铜组分在还原及反应过程中聚集长大,从而使催化剂活性显著增加,当催化剂经过高温焙烧,催化剂活性由于ZrO2结晶和铜的聚集而降低。