简介：研究结果表明，1Cr18Ni9Ti不锈钢在pH=1的酸性NaCl溶液介质中浸泡最初期，噪声电流曲线无噪声峰，噪声电阻大，电化学阻抗谱为一容抗弧，阻抗模值大，电极表面处于稳定状态。浸泡24h噪声电流曲线出现尖峰波动，但波动峰值只有几个微安，噪声电阻直线下降，阻抗谱高频部分为一容抗弧，低频下出现感抗特征，阻抗模值大幅度下降表面处于点蚀诱导期的亚稳状态。浸泡48h后，噪声电流波动峰值突然增大至100μA，噪声峰也增多，噪声电阻基本稳定，阻抗谱低频下的感抗成分消失，点蚀进入稳定发展阶段。动电位极化曲线与电化学噪声测试结果表明，1Cr18Ni9Ti不锈钢在pH=1的酸性NaCl溶液介质中的耐点蚀性能随浸泡时问延长而降低。

简介：ThestructureandelectrochemicalpropertiesofanewlowcobalthydrogenstorageelectrodealloysLa1-xLixNi3.2Co0.3Al0.3(0≤x≤0.2)wereinvestigatedwithadifferentadditionsofLiinreplacementofLa.WiththeincreaseofLicontentsthemaximumdischargecapacityincreasesfrom240mAh·g-1(x=0)to328.4mAh·g-1(x=0.1)andthecyclestabilityisimprovedcorrespondingly.ThecapacitydecaycanremaiN28.6%(x=0.2)after230charge/dischargecycles.Thehighratedischarge(HRD)abilityofthealloys(x≤0.1)isimprovedandthebestHRDis34.1%(x=0.1)underthedischargecurrentdensity1200mA·g-1.ItisfoundthatthepreparedalloysarebasicallycomposedofLaNi5asmatrixphaseandLaNi3assecondphase(x≤0.1).ButtheabundanceofLaNi3phasedramaticallydecreaseswithincreasingx.Whenx=0.2,anewphaseAl(NiCo)3isformed.

简介：用机械合金化和热压法制备可降解的Mg-6Al-4Zn金属植入体。通过X射线衍射分析、透射电镜、压缩试验、浸泡试验、电化学测试和MTT比色法研究添加1%Si(质量分数)对Mg-6Al-1Zn合金显微组织、力学性能、生物腐蚀行为和细胞毒性的影响。结果显示,添加1%Si后,Mg-6Al-1Zn中形成了细小的多边形Mg2Si相,材料的抗压强度、伸长率和耐腐蚀性能提高,且骨肉瘤(Saos-2)细胞的细胞活性提高。根据MTT测试结果,释放出的镁离子没有细胞毒性。因此,添加1%Si提高了Mg-6Al-4Zn作为可降解植入体的综合性能。

简介：室温下用溶胶凝胶自蔓延燃烧法合成平均尺寸约50nm的仿立方体结构KxNa1-xNbO3纳米粉体并制备成陶瓷,对陶瓷进行相结构、显微组织以及电性能的表征。XRD结果表明,KxNa1-xNbO3陶瓷为纯的钙钛矿结构,且K0.5Na0.5NbO3陶瓷具有正交相和单斜相的混合相结构。SEM结果表明,所有陶瓷样品均为孪晶分布,且孪晶分布中小晶粒数随K+含量的增加而减少。在室温下,晶粒尺寸均匀且具有最大密度的K0.5Na0.5NbO3陶瓷具有较优异的电性能:εr=467.40,tanδ=0.020,d33=128pC/N,kp=0.32。K0.5Na0.5NbO3陶瓷的优良电性能说明溶胶凝胶自蔓延燃烧法合成的K0.50Na0.50NbO3粉体性能较好,且制备的陶瓷满足无铅压电材料应用。