简介：10月8日至11日,国家新材料产业发展专家咨询委员会秘书处（以下简称“专家咨询委秘书处”）副秘书长周少雄教授带领专题调研组赴安徽、福建、浙江调研稀土永磁材料研发、生产、应用情况.钢铁研究总院、安泰科技股份有限公司、有研科技集团有限公司等单位相关专家以及专家咨询委秘书处工作人员参加调研.

简介：Theaimofthisresearchistopulseco-depositnano-CeO2particlesintoNi-W-Balloycoatingsinordertoimprovethesurfaceproperties.Theinfluenceofpulsefrequencyanddutycircleondepositionrate,microhardnessandmicrostructures,andtheinfluenceofheattreatmenttemperatureonphasestructures,microhardnessandabrasivityofNi-W-B-CeO2compositecoatingswereinvestigated.Theresultsindicatedthatthepulseco-depositionofnickel,tungsten,boronandnano-CeO2particlefromthebathwhichnano-CeO2particlewassuspendedbyhighspeedmechanicalstirringledtotheNi-W-B-CeO2compositecoatings,possessingbettermicrohardnessandabrasionresistancewhenheat-treatedat400℃for1h.Themicrohardnessas-depositedwith636Hzandthedepositionratewith0.0281mm·h-1wasthehighestatpulsefrequencywith1000Hzandpulsedutycirclewith10%.Microstructuresanalysisdisplaysthatdecreasingpulsedutycycleleadstorefinementingrainstructuresandtheimprovementofmicrostructures.X-raydiffractionshowsthatthecompositecoatingas-depositedwasmainlyintheamorphousstateandpartiallycrystallized,butwhenheattreatedat400℃,thecrystallizationtrendwasstrengthenedfurther.

简介：ＥｌｅｃｔｒｏｎＭｉｃｒｏｓｃｏｐｉｃＩｎ－ｓｉｔｕＯｂｓｅｒｖａｔｉｏｎｆｏｒＰｒｅｐａｒａｔｉｏｎｏｆＵｌｔｒａｆｉｎｅＬａ２Ｏ３ＮａｎｏｐｈａｓｅＰｏｗｄｅｒＧａｏＹｕｚｕｎ（高愈尊），ＬｉＹｏｎｇｈｏｎｇ（李永洪），ＺｈａｎｇＴａｉｓｏｎｇ...

简介：OpticalabsorptionandemissionintensitiesofNd3+ioninKLu(WO4)2crystalwereinvestigated.BasedontheJudd-Offelttheory,wecalculatedthefollowingspectralparameters:phenomenologicalintensityparametersΩ2=5.567×10–20,Ω4=3.597×10–20,andΩ6=3.800×10–20cm2.Theradiativelifetimeoflevels4F3/2was182.58μs.Thefluorescencebranchingratioforthetransition4F3/2→4I11/2was46.98%.Inaddition,theradiativetransitionprobabilitiesAJ,J’,oscillatorstrengthsPJ,J’andthevaluesofinte...

简介：ＳｔｕｄｙｏｎＭｏｒｐｈｏｌｏｇｙｏｆＳｕｒｆａｃｅｏｆＬａｒｇｅＡｒｅａＹＢＣＯＴｈｉｎＦｉｌｍｓｏｎＺｒ（Ｙ）Ｏ２ＳｕｂｓｔｒａｔｅＷａｎｇＲｕｉｋｕｎ（王瑞坤），ＳｕｎＬｉｈｏｎｇ（孙丽虹），ＬｉｕＨｏｎｇｆｅｉ（刘鸿飞）ＷａｎｇＸｉａｏｐｉ?..

简介：阐述了120~150mm特厚压力容器用12Cr2Mo1R钢板在南阳汉冶特钢采用100t转炉—LF＋VD精炼—模铸浇注—3800mm轧机轧制—热处理的工艺研制开发过程,通过合理的化学成分设计、严格的冶炼、模铸浇铸、轧制及热处理工艺控制,最终确保了120~150mm厚12Cr2Mo1R保一级探伤、保力学性能的成功研制,并实现了批量化生产。

简介：近日，石嘴山国家稀有金属材料高新技术产业化基地获科技部批准认定，正式成为首批全国77家国家高新技术产业化基地成员之一。

简介：我国现有各类国营矿山企业,对我国社会主义经济建设发挥着至关重要的工业原料的保障作用。《矿产资源法》对国营矿山的法律地位作了十分明确的原则性规定:“国营矿山是开采矿产资源的主体,国家保障国营矿山企业的巩固和发展。”但多年来地方群众采矿势力不断地侵袭国营矿山资源,造成严重的干扰和破坏。此现象不仅屡禁不止而且是愈演愈烈。为何有法不能治理,如何维护国营矿山的主体地位,使其正常生产,已引起社会的关注。积极寻求有效的对策,切实加强矿产资源的保护是一个急需探讨的课题。

简介：管道磨损是影响深井矿山充填系统正常生产的主要因素之一。所谓深井开采，就是由于开采深度的增加，使矿山的岩石力学性质和地应力特征，与浅井矿山相比发生了根本性变化，即为了防止岩爆和岩石冒落事故，必须采取有针对性的、有效的局域支护措施。对于深井开采的划

简介：通过对2号常化酸洗线活套支撑小车弹簧式力矩卷筒进行了改进,提高了弹簧式力矩卷筒本体的强度及钢丝绳的破断拉力强度,延长了弹簧式力矩卷筒的使用寿命,降低了力矩卷筒失效频率,提高了设备的有效开动率,为设备点检和维护创造了良好的条件,满足了正常生产的管理要求,确保了生产的正常运行。

简介：高度有效的Tb3+激活SrAl2O4黄磷被一个联合combustionsolid状态反应方法综合。SrAl2O4的先锋:Tb3+黄磷经由一个燃烧过程被准备，然后同样准备的粉末被加热在一减少在1250点的激活的碳周围??慥獲？

简介：DyPt2filmswerepreparedbyalternatedepositionthinDyandPtlayersonglasssubstratesbyDCmagnetocontrolledsputteringmethod.TheXRDdataindicatedthatforas-depositedDy/Ptfilms,andtheperiodiclayeredstructuresalongthicknessdirectionwereevidencedwithlowangleX-rayscattering.Withincreasingannealingtemperature,thecompoundsofDyPt,DyPt2andDyPt3wereformedsuccessivelyattemperaturerangingfrom300to400℃.ItwasfoundthatthecompositionreactionDyPt+DyPt3→2DyPt2tookplaceat500℃.Afterannealingat500℃for1h,thecompoundsDyPtandDyPt3transformedcompletelyintotheDyPt2compound.

简介：Forthegoalofsulfurrecovery,mostmethodsareaimedatthetailgaswithhigh-concentrationH2S,butfeweffectivemethodsareusedforlow-concentrationH2S.Inthiswork,Low-concentrationH2Scouldbepurifiedwellbyliquidphasecatalyticoxidation(LCO),andthesulfurresourcecouldalsoberecovered.TheabsorptionsolutionwaspreparedbyFeCl3andsulfosalicylicacid.Undertheexperimentalconditions,theconversionofH2StoScouldbemaintainedabove94%at60℃.InordertoenhancetheeconomicalefficiencyofLCOmethod,theabsorptionsolutionwasmodifiedbydopingCe,andaseriesofexperimentsweredesignedtoinvestigateitsperformance.TheresultsshowedthattheconversionofH2Shadnoobviousimprovement,butabove98%conversioncouldbegainedat60℃,andtheH2Sconversionratewasenhanced.TheoptimumadditionqualityofCe(NO3)3was0.08gto50mlFe3+solution.

简介：据行业网站报道，台湾烨联百分百转投资子公司“福建联德企业”的4条矿热炉（RKEF）镍铁生产线陆续运转，可于2月份全部投产，未来全产能可达到20万吨，可提供不锈钢厂炼钢使用。

简介：TheeffectsofUVAphotoirradiatedCe(Ⅳ)dopedTiO2nanoparticle(CDTP)onratcoloncarcinomacellline(C26)growth,cellcycledistribution,andmorphologywerestudiedbyMTTassay,FlowCytometry,andfluorescentstaining.Theresultsindicatethatabout64.6%cellsarekilledafter24hby180μg·ml-1CDTPwhen8minexposedtoUVA,over90%deadfor30mingroup,relativeto18.7%,41.5%ofTiO2atthesameconditionrespectively.Hoe33258stainingofthefixedcellsrevealstypicalapoptoticstructures(apoptoticbodies),andcellsarearrestedinG0/G1phase.

简介：ThemorphologyandcorrosionbehaviorofNi/Al2O3compositecoatingspreparedusingdouble-pulsedelectrodepositingtechniqueafteroxidizedunder800℃NaCldepositinairenvironmentwereanalyzedbyscanningelectricalmicroscope(SEM),X-raydiffraction(XRD)andenergydispersivespectrum(EDS).TheresultsshowedthatthecorrosionofallcompositecoatingswasacceleratedunderNaCldeposits,andthecorrosionproductswereratherporouswithpooradherencetothematrix.Al2O3particlesinthecoatingscanrefinethegrainsizeandimprovethehightemperaturecorrosionresistanceofthecoatings.Withinthetestscope,themoreAl2O3particlesinthecoatings,thelowercorrosionratescouldbeobtained,andthecorrosionmechanismwasalsodiscussed.

简介：~~

简介：确定了合金成分，制定了中频感应熔炼工艺，开发了保证合金性能和质量的熔炼成分、成分均匀性以及杂质元素（O、N、H）精确控制技术；确定了MBA-2合金的铸造工艺、挤压工艺，最终产品各项性能指标均满足国标要求，形成了从合金熔炼、铸造、挤压及性能测试等关键工艺及技术。

简介：日前，中国铝业青海分公司两项发明专利获国家知识产权局授权。发明专利“一种铝及铝合金扁锭锯屑收集回炉重熔方法”，工艺流程为通过离心式轴流风机收集锯屑，由螺旋送料装置将锯屑输送到压实装置的挤压模具内，挤压成成锯屑压块，锯屑块转运、安装渣箱、残留铝液浇铸、冷却、废铝重熔。本发明工艺流程简便，操作容易，用于铝锭锯屑收集、压实、浇铸的设备简单合理，成本低，效率高。

简介：近日，国家发展改革委、财政部正式启动“节能产品惠民工程”。