简介:Siliconcarbide(SiC)-alumina(Al_2O_3)-mullite(Al_6Si_2O_(13))compositepowderwassuccessfullysynthesizedat1550℃for5hviacarbothermalreductionreaction,andtheeffectsofvariousmassratiosofactivecarbontoflyash(0.38,0.44and0.58)onthephasecompositionandmicrostructureofproductswereinvestigated,andtheformationprocessofthepowderwasalsoanalyzedindetail.Theproductsmainlyconsistofβ-SiC,α-Al_2O_3,Al_6Si_2O_(13)andFeSi.IncreasingcarboncontentfavorsthedecompositionofAl_6Si_2O_(13)andformationofSiC.Theaverageparticlesizeofβ-SiCandα-Al_2O_3isabout1μmandthatofAl_6Si_2O_(13)is5-10μm.TheformationprocessofSiC-Al_2O_3-Al_6Si_2O_(13)powderincludesthedecompositionofmulliteinflyashandformationofSiC.
简介:ThisworkstudiedthecharacteristicsofSiO2distributionandstructureofsilicatephasesinMgO-ZrO2compositessynthesizedbyrawmaterialsoflightfiredmagnesitendzircon,Theresultsindicatethat30wt%-40wt%SiO2contentinthesystemisexistedintheformofcrystallineofforsterite(M2S),theremainderingofSiOcontent(60wt%0-70wt%)isexistedintheglassphase,Thechemicalcompositionofglassphaseiswellagreedwiththechemicalcompositionofmonticellite(CMS).
简介:AnO'-Sialon-Al2O3compositerefractorywaspreparedbyinsitureactionofSi3N4-ZrSiO4-Al2O3mixturewithfusedaluminaaggregates.Densification,insitureactionprocedureandmicrostructureofthematerialwereinvestigatedbymeansofX-raydiffraction,opticalandscanningelectronicmicroscopesandEDAX.
简介:β-sialon/alumina/silicamixturesweresinteredinflowingnitrogenat1500℃and1600℃respectively.ThesinteringpropertiesandmorphologyofsampleswereinvestigatedbySEM,EDSandXRD.Resultsshowthatsinteredpropertiesofthesamplesareinfluencedbysoakingtemperaturesandcompositions.Bulkdensitiesofsamplesareincreasedwiththeincreaseofthesoakingtemperature,whereastheapparentporositiesaredecreased.Masslossofthesinteredsamplesat1500℃islowerthanthatat1600℃,butallthemasslossremainsapproximatelyconstantwiththeincreaseofsialoncontent.Fromthepointofthermodynamicanalysis,ComplexchemicalreactionstakeplaceinsamplesduringsinteringprocessandthevolatileofSiO(g)isresponsibleforthemasslossofsamples.Comparedtocrosssectionmicrostructureofβ-sialon/Al2O3/SiO2mixturessinteredincokepowderbedconsistingofthedensecenterwithwell-developedcolumnofsialonphase,thetransitionalpartwithneedlelikegrainnitrogen-containingphaseandtheloosepartwithshortgranularAl2O3phase,thoseofmixturessinteredinflowingnitrogenisofwell-developedsialonindensecenterandslightlyloosepartwithsialondebris.
简介:MicrostructureandgrainboundarycharacterofhotpressedbinaryAl2O3(mullite,ZrO2)-SiCompositesandquaternaryAl2O3-mullite-ZrO2-SiCcompositewerestudiedbyelectronmicroscopyandmicroanalysis,ResultssuggestthatthereexistgrainboundarysolidsolutionsduetoelementaldiffusionnearSiCandmatrixoxidesgrainboundaries.
简介:LowcementAl2O3-SiO2castableswaspreparedusingsupergradebauxite(w(Al2O3)>85%)asaggregate,brownfusedcorundum,siliconcarbide,Secar71CAcement,α-Al2O3micropowderandmicrosilicaasfinepowders.TheinfluenceofSiC(0,5wt%,10wt%,and15wt%)onresistancetoPbO-richslagwasinvestigatedbystaticcrucibleslagtest(1300℃for5h,inair).TheslagcorrosionmechanismofthecastableswasanalyzedbymeansofSEM,EDSandXRD.TheresultsshowthattheresistanceofAl2O3-SiO2castablestoPbO-richslagisimprovedobviouslybytheadditionofSiC.ThecorrosionmechanismofthePbO-richslagcanbediscribedasthatPbOintheslagreactswithSiO2andCaOinAl2O3-SiO2castables,forminglow-meltingcompounds(suchasPbO·SiO2and2PbO·SiO2).
简介:MgO-Al2O3-Cr2O3rammingmixesmadeofdifferentrawmaterialshavedifferentmineralstructureanddifferentphysicalpropertiesthoughwiththeidenticalparticlesizedistribution,thesameamountofbinderandchemicalcomposition.Theresidualcarboncontentofthefusedmagnesia-chromematerialmadeinreducingatmosphereisveryhigh,ifthismaterialsisusedintheMgO-Al2O3-Cr2O3rammingmix,itwouldcausespallingofthefurnaceliningduringdrying-out.
简介:MgO-ZrO2unfiredbrickswithZrO2contentupto8%attheintervalof2%wereprepared,usingfusedmagnesia(MgO:97%)andfusedMgO-ZrO2clinker(ZrO2:14.33%)asstartingmaterialsandphenolicresinasbinder.TheeffectsofZrO2contentonthermalshockresistance(TSR)andotherpropertiessuchascoldandhotmodulusofrupturehavebeeninvestigated.Residualcoldmodulusofruptureratioafterheatingat1000℃andquenchingbyairblowingwasadoptedtocharacterizeTSR.AdditionoftheMgO-ZrO2clinkerimprovesTSR,attributingtothemicrocracktougheningeffectbythermalexpansionmismatchbetweendifferentphases.WhenZrO2contentgoesabove4%,theimprovingeffecttendstobemoderate.TheintroductionofMgO-ZrO2clinkercanalsoimprovetheHMORat1500℃,whiletheincreasedZrO2contentreducesCMORofthebricksprefiredat1600℃,duetothethermalexpansionmismatcheffect.Compromisingtheoverallproperties,theoptimalZrO2contentforsuchmagnesiabasedunfiredbrickissuggestedtobe4%.