简介:Li4Ti5O12(LTO)/carbonnanotubes(CNTs)compositematerialissynthesizedbasedonasolid-statemethodbysand-milling,spray-dryingandcalciningat8508CunderN2flow.TheLTO/CNTssampleswith1wt%and3wt%weightratioofCNTsadditionandthepristineLTOsampleareprepared.TherateperformanceandthethermalstabilityofthesesamplesareinvestigatedbasedonLiMn2O4(LMO)/LTOfull-cell.TheresultsshowthattheweightratioofCNTsadditionhasdistincteffectonLTOperformances.ThecompositematerialsofLTOcompositedCNTshavebetterperformanceathigh-rateduetotheintercalationenhancementbyconductivenetworkofCNTs.Atsecond,theoverchargingtemperatureresponseofthecell’ssurfacewith1wt%CNTsadditionisthelowest.Theparticlesizedistributionismeasuredandthemostuniformparticlesareobtainedwith1wt%CNTsaddition.ThistrendcouldexplainthatthemediumquantityofCNTsisoptimaltoimprovetheheatandmasstransferandpreventtheproblemsofcrystallitegrowinginterferenceandaggregationduringthecalcinationprocess.
简介:标题化合物C26H26O5以2,3-萘二甲醛和5-甲基-1,3-环己二酮为原料,在醋酸溶剂中,室温下经搅拌多组分一锅法合成得到.其结构通过单晶X-射线衍射法确定,晶体属单斜晶系,空间群P21,相对分子质量Mr=418.47,晶胞参数a=0.99004(8)nm,b=1.09098(9)nm,c=1.04246(11)nm,V=1.08753(17)nm3,Z=2,晶胞密度Dc=1.278g/cm3,吸收系数μ=0.088mm-1,单胞中电子的数目F(000)=444.晶体结构用直接法解出,经全矩阵最小二乘法对原子参数进行修正,最终的偏离因子为R1=0.0533,wR2=0.1293.在晶体结构中新形成的吡喃环为半椅式构象,而茚中五元环则为信封式构象.