简介:Thisworkinvestigatedthethermo-gravimetric(TG)changeandexplosionresistanceofultra-lowcementAl2O3-SiO2castablesaddedwith0,5%,10%,15%and20%of≤74μmrawbauxitepowderscontaining72.8%Al2O3,respectively.Thecastableswerepreparedusingwhitefusedaluminaasaggregate,powdersofwhitefusedalumina,fusedmullite,α-Al2O3ultrafines,3%CAcementand5%microsilicaasthematrixportion.TGchangeofthecastableswasinvestigatedbyathermo-gravimetricanalyzerforlargesizespecimen.Whentherawbauxiteadditionislessthan10%,themass-losingbehaviorofthecastablesissimilartothatwithoutrawbauxite,tendingtoreachaconstantmassaround400℃,beforewhichthemass-lossismildandproducinglittledestructiveinfluence.Withmorethan10%rawbauxiteaddition,however,themass-lossincreasessignificantly,andthetemperaturetoreachaconstantmassincreasesto600℃orhigher,unfavorabletostructuralstabilization.Withtherawbauxiteadditionupto20%,nonegativeinfluenceonexplosionresistanceisfound.
简介:Reactionsintereddensezirconia-mullitecompositeswerepreparedbyisostaticallypressingfromzirconflourandreactivealuminawithdifferentproportionsofTiO2andCr2O3additives.Thepressedcompactsweresinteredatdifferentelevatedtemperatureswithvariablesoakingtimes.Microstructuresandphasedevelopmentinthesinteredcompactswereanalysedtoassesstheinfluenceoftheadditivesonthepropertiesofthezirconiamullitecomposite.
简介:Inthepresentpaper,novelsidewallmaterialsforaluminumreductioncellwerepreparedinairusingmagnesiaandmagnetiteasstartingmaterials.ThesinteringbehaviorsofthespecimenswereinvestigatedbymeansofX-raydiffraction(XRD)andscanningelectronmicroscope(SEM).AndcorrosiontestsinaNa_3AlF_6-AlF_3-K_3AlF_6bathwereconductedtoevaluatetheelectrolytecorrosionresistance.TheresultsshowthattheFe_3O_4phaseistransformedintoFe_2O_3athightemperatures,whichinturnreactswiththeMgOaddedtoformMgFe_2O_4spinel.AndwithincreasingtheMgOcontentfrom0to30mass%,densificationofthespecimensdecreasesmainlyduetolargervolumeexpansionresultingfromformationofmoreMgFe_2O_4.ThecorrosiontestsshowthatcorrosionlayersareproducedinalltheMgOaddedspecimens.However,forspecimenscontainingMgFe_2O_4phaseonly,Mg(Al,Fe)_2O_4compositespinellayersarealsogenerated,whichremarkablyimprovethecorrosionresistanceofthespecimens.