简介：TheRamanspectraof3%(molefraction)Y2O3-ZrO2(3Y)areobtainedatdifferenttemperaturefrom77Kto853K.Theresultsshowthat260cm-1Egand460cm-1Egmodesonthespectrashifttowardlowerwavenumberwiththeincreaseoftemperature;meanwhile,thecontinuityoftheHalfWidthatHalfMaximum(HWHM)andwavenumber(frequency)ofRamanbandsarebrokenandt-phaseonlypartiallytransformstom-phaseat523K.Basedontheexperimentalresults,thispaperdiscussesthet-phaselatticevibrationof3YandpresentstheimagesofvibrationdisplacementofsixRaman-activemodesfort-phaseofZrO2.TheanalysisindicatesthattherearediversitiesexistinginthedisplacementoftheatomicvibrationofRaman-activemodesbecauseoftheirdifferentsymmetriesatvarioustemperature,whichleadstothedifferentchangetendenciesofRamanbands.Furthermore,theabruptchangesofsomeRaman-activemodesindicatingtheatomicdisplacementareassumedtobethecondensationsofphononmodesinthet→mphasetransition.

简介：以四氯化钛等为原料，采用溶胶-凝胶法制备纳米TiO2，制品为锐钛矿相和金红石相的混合物，随着热处理温度的升高，其中的锐钛矿相的比例逐渐降低，金红石相比例逐渐上升；又以Na2SiO3为原料，对TiO2进行表面改性，制得TiO2／SiO2复合材料。研究发现，原位改性后的TiO2在可见光下光催化甲醛可以发生聚合反应。

简介：研究了Na^＋替代Bi^3＋、Sn^4＋替代Nb^5＋对Bi2（Zn1／3Nb2／3）2O7陶瓷烧结特性、显微结构和介电性能的影响。结果表明，替代后样品的烧结温度从1000℃降低到860℃；在-30～130℃样品出现明显的介电弛豫现象；弛豫激活能在0．3eV左右。用缺陷偶极子和晶格畸变对Na-Sn掺杂Bi2（Zn1／3Nb2／3）2O7的介电弛豫现象进行了解释。

简介：

简介：

简介：D2X终于面世了．尼康的拥趸们不用再受佳能一族的嘲笑了。在上一场单反数字相机的战争中．尼康几乎在各档价格市场上都丢失了其领先地位——只有D70在与300D苦苦地较量。当然，佳能作为回应．推出了350D。

简介：

简介：以TiCl_4的乙醇溶液作为前驱体,采用溶胶-凝胶法制备TiO_2溶胶,用浸渍-提拉法在载玻片表面制成了具有抗菌作用的TiO_2薄膜以及铁掺杂TiO_2薄膜,考察了原菌液浓度、镀膜次数以及铁掺杂量对薄膜对大肠杆菌的抗菌性能的影响。

简介：Aone-pot,solvent-thermalprocesswasusedtocreatetheultrafineZnFe2O4nanoparticlesphotocatalyst.Duringthesolvent-thermalprocess,theinsituself-formingNaClnotonlyservedasa"cage"toconfinetheiondiffusion,butalsoactedasamicroreactorfornanocrystallitegrowth.Anaverageparticlesizeof~10nmandahigh-specificsurfaceareaof~112.9m2/gwereobservedfortheultrafineZnFe2O4nanoparticlesOwingtothesynergisticeffectofultrafineparticlesize,thefullutilizationofthevisiblelightregionandhighconductionband(CB)position,ultrafineZnFe2O4photocatalystdisplayedanefficientphotocatalyticCO2reductionundervisiblelightillumination.Besides,theultrafineZnFe2O4photocatalystshowedhighproductionselectivityforCH3CHOandC2H5OHgenerationinaqueousCO2/NaHCO3solution.Thisworkmayprovideanewideaforthesynthesisofnewhigh-efficiencyphotocatalysts.

简介：

简介：以Ti（OBu）4和内蒙古杭锦2^#土为主要原料，Sr（NO3）2为掺杂剂，采用溶胶-凝胶法制备了一系列Sr元素掺杂改性的TiO2／杭锦2^#土复合光催化剂，并用X射线衍射、傅立叶红外光谱和扫描电子显微镜等对样品进行了表征。紫外光照射下，以亚甲基蓝水溶液为光降解体系，考察了Sr的掺杂量和热处理温度对光降解率的影响，结果表明，Sr的掺杂量为0．5％，焙烧温度为500℃条件下制得复合物的催化活性明显优于相同条件下的TiO2／杭锦2^#土。该复合物催化剂的优点是易于从分散体系中分离和可循环使用。

简介：综述了当前B4C增强Al基复合材料的研究现状,通过对比不同制备工艺所得复合材料的拉伸强度、硬度、耐磨性能和延伸率等力学性能,总结了粉末冶金法、高能球磨法、无压渗透法、搅拌铸造法以及其他制备技术的优缺点,提出复合材料制备过程中存在的问题及解决方法;此外还介绍了B4C的强化机制;并对B4C增强Al基复合材料未来发展方向和研究重点进行了展望。

简介：

简介：Inthisstudy,Almatrixcompositesreinforcedby7.5and15vol.%B4CparticlesandalsomonolithicAl（AlwithouttheB4Cparticles）wereproducedbywetattritionmillingandsubsequenthotforwardextrusionprocesses.Themicrostructureofthecomposites,evaluatedbyscanningelectronmicroscopy（SEM）,showedthattheB4CparticleswereproperlydistributedintheAlmatrix.MechanicalpropertiesoftheAI/B4CcompositesandmonolithicAlwereinvestigatedbytensile,wearandhardnesstests.TheresultsrevealedthatwithincreasingcontentofB4Cparticles,thetensilestrengthandmicrohardnessofcompositesincreasedbuttheelongationdecreased.Inaddition,thetensilestrengthandmicrohardnessofcompositesampleswerehigherthanthoseofmonolithicAl.ThedensitymeasurementsrevealedthatthedensityofcompositesdecreasedwithincreasingcontentoftheB4Cparticles.

简介：以超重力场辅助燃烧合成技术制备了呈梯度分布的Y2O3-Al2O3-SiO2玻璃／Y3Al5O12陶瓷梯度复合材料。结果表明，梯度布置两种组分的原料既可防止下层熔体的喷溅，又能提高上层玻璃的透过率。该梯度材料沿超重力方向依次为YAS透明玻璃层、YAS-YAG玻璃陶瓷层和YAG陶瓷层。

简介：固体太酸那么<潜水艇class=“a-plus-plus”>42/ZrO2-SiO2被剧降受精方法，和它的催化活动准备与p-nitrobenzoic酸和甲醇的酯化作用被测试。最佳条件也被发现，也就是说，在硅石和氧化锆之间的臼齿的比率是10:1，锻烧温度是550猠湩整楲杮愠摤瑩癩獥愠敲愠潤瑰摥?桴?琠?瀠慨敳琠慲獮瑩潩?景匠???汣獡?愢瀭畬?汰獵??猯'T举猼扵挠慬獳∽?汰獵瀭畬?????愠摮琠敨洠'炭鷳T?牰灯牥楴獥漠?桴?潣灭獯瑩獥愠?潢桴爠潯?整灭牥瑡牵?湡?楨桧琠浥数慲畴敲愠敲愠汬椠据敲獡摥眠瑩?浳污?硥整瑮

简介：CeO2稳定了ZrO2极端好nanoparticles成功地经由简单、有效的大音阶的第五音胶化被综合由把zirconylchlorideoctahydrate，铈硝酸盐hexahydrate，和柠檬性的酸用作开始材料的合成途径。一系列技术包括X光检查衍射(XRD)，thermogravimetry(TG)，微分扫描热量测定(DSC)，Fourier变换红外线的光谱学(FTIR)，传播电子显微镜学(TEM)，和N2-sorption分析，被用来描绘同样准备的样品的结构和形态学。XRD研究显示同样综合的样品具有CeO2的很好使结晶的四角形的阶段有高纯净的稳定的ZrO2。TEM图象证明同样综合的样品与一种平均尺寸由很多好散nanoparticles组成大约10nm。同样综合的四角形的CeO2稳定了ZrO2样品在不同温度被加热以便评估它的热稳定性。exprimental结果表明同样综合的四角形的CeO2稳定了ZrO2样品展览没有阶段转变的出现的优秀稳定性。

简介：初步探讨了以Yb2O3／TiO2鼓泡空化降解有机染料，研究了鼓泡时间、染料初始浓度、催化剂含量、气体流速对刚果红降解率的影响，对比了不同染料的降解率及可能的降解过程。

简介：采用均匀沉淀法在磁性NiFe2O4表面包覆TiO2，制备了一种新型纳米TiO2／NiFe2O4光催化复合材料。通过改变Ti和Ni物质量之比确定了复合材料最佳钛镍比，用X射线衍射、透射电镜、UV—vis漫反射、BET、TG—DSC、磁力学测试等手段对复合材料进行了表征，以甲基橙的水溶液为模拟污染物，评价样品的光催化性能：该复合材料在光照2h后，甲基橙的脱色率可达98．5％，是一种在可见光范围内有响应、便于回收、可重复使用的高效光催化剂。

简介：采用先驱体浸渍裂解工艺制备了2.5D-SiO2f/（SiO2＋硅树脂）透波材料,并对其力学性能、耐环境性能和耐大功率微波辐照性能进行了研究.结果表明,环境试验前后,2.5D-SiO2f/（SiO2＋硅树脂）透波材料的力学性能和介电性能变化均较小.采用功率密度为60W/cm2的微波考核1h后,透波材料表面无变化,表面温升仅为82℃.