简介:采用单辊法制备了宽20mm、厚25μm的Fe78Si9B13合金带材,用绕带机将其绕制成环型磁芯,然后将磁芯进行退火处理,结果表明,随着退火温度的升高,Fe78Si9B13非晶磁芯的初始磁导率m、饱磁感应强度Bs和矫顽力Hc呈先增大后减小的趋势,当退火温度达到450℃时,磁化曲线呈现出一定的线性关系,即恒导磁特性。将经4500(=/100min退火的Fe78Si9B13非晶磁芯用环氧树脂进行封装后,环氧封装后μi和Bs减小,而Hc和损耗Ps增大,磁化曲线和损耗曲线的形状与封装前相同。
简介:Aneffectivedispersion-strengtheningphaseinAl-8Fe-2Mo-2Zr-2Nd-0.7Ti-1.6SialloywasidentifiedtobeanagedprecipitatephasewithpossiblechemicalstoichiometryofAl20(Ti,Mo)2Ndandfcccrystalstructurewithao=1.455nm.ThestructurewasdeterminedtobeFm3mspacegroup.
简介:Eu(TTA)4CsHsNC16H33(TTA:1-(2-Thenoy)-3,3,3-Trifluoracetate)isencapsulatedinSi-MCM41modifiedwithN-(3-Trimethoxysilethyl)ethylenediamine.Theemissionspectrumoftheassemblyshowsonlya5D0→7F2transition.Ascomparedwiththerareearthcomplexitself,thelifetimeoftheassemblybecomeslongeranditsstabilityundertheUVradiationismuchbetter.