简介：对10B21冷镦钢盘条出现的冷镦开裂现象,用光学显微镜、扫描电镜、直读光谱仪对缺陷部位进行了显微组织、化学成分等分析。结果表明,冷镦开裂是由钢坯裂纹缺陷所导致,且通过Ti元素的加入,杜绝了钢坯裂纹的产生。

简介：Withpricesformetalresourcessuchasnickelandmolybdenumsoaring,thereisaheightenedsenseofcrisisconcerningresourcescarcity.WhileType304,themostcommonstainlesssteel,offersexcellentcorrosionresistance,itspriceisaffectedsignificantlybythecostofnickelbecauseofits8%nickelcontent.ThestainlesssteelthathasthesamecorrosionresistanceasthatofType304anddoesnotcontainnickelandmolybdenumhasbeenrequired.JFESteelCorporationhasdevelopedanew21%Cr-0.4%Custainlesssteel,theworld’sfirstferriticstainlesssteel,whichoffersequivalentcorrosionresistancetoType304whilecontainingabsolutelynonickelormolybdenum,tworaremetals.Thenewlydevelopedsteelcontains21%chromiumwiththeadditionof0.4%copper.Thedevelopmentofthesteelisbasedonanewdiscoverythatthepassivefilmsofstainlesssteelscouldbestrengthenedbythesynergyeffectofhighchromiumcontentandcopperaddition.Copperadditionenrichesthechromiumcontentinpassivefilmsafterfieldexposure.Newlydeveloped21%Cr-0.4%CustainlesssteelisadoptedformanyapplicationsasasubstitutionforType304,includingcommercialkitchenware,buildingmaterialsandindustrialmachinery.ThesteelisexpectedtobeanewstandardofaferriticstainlesssteelasasubstitutionforType304.

简介：Improvingtheunitheatefficiency,reducingcoalconsumptionandtheemissionofCO2andmeetingtherequirementsofenvironmentalprotectionandenergyconservationisthegoaloftheboilerandthepowerindustry.Developmentsoflargecapacityandhighparameterultra-supercritical（USC）unitsarethetendencyofthepowerindustry.ThereisnodoubtthatthedevelopmentofUSCunitsisbasedonthedevelopmentofmaterials,especiallythematerialsusedforsuper-heaterandreheaterinhigh-temperatureUSCboiler.Duetothelongtimeexposuretotheharshenvironment,suchasbearingthe600℃steamoxidation,andwithstandingthecorrosivefluegasandflyasherosion,thematerialsrequirenotonlygoodhigh-temperaturestrength,butalsoagoodcorrosionresistance.Inconsiderationoftherequirementscitedabove,foreigncountrieshaddevelopedTP310HCbN（07Cr25Ni21CbN）austeniticheat-resistantsteel.However,thedomesticdemandsforthismaterialstilldependonimportandthecostishigh,sotheboilerandthepowerindustryexpectseagerlythatthesesteelscanbeproducedbydomesticmetallurgicalindustry,especiallyBaosteel,toreplacetheimportedproducts.Inordertosatisfytherequirementsofdomesticmanufacturingsuper-heaterandreheaterusedinultra-supercriticalpowerboiler,afterdevelopedT23、T91、T92、S30432highpressureboilertube,BaosteelbegantodevelopTP310HCbN（07Cr25Ni21CbN）austeniticstainlesssteeltubeinJanuaryof2007.Thisstudydescribesthecompositiondesign,themanufacturingprocessofproduct,andtheassessmentofperformanceofBaosteel’sTP310HCbN（07Cr25Ni21CbN）.ThedataindicatesthatpropertiesofBaosteel’sTP310HCbN（07Cr25Ni21CbN）conformtotheASMESA-213standardandGB5310standard,soitcansubstitutetheimportedproductsandissuitableformanufacturingpowerstationboilerofgreatcapacityandhighsteamparameters.

简介：据浙江省经贸委发布的信息表明，2005年浙江省组织实施节电改造项目660项，年节电21．264亿kW·h，相当于节约了杭州的主要电源之一——萧山电厂这样一个中型电厂一年多的发电量。

简介：

简介：烧结料在混合过程中需加水润湿并制粒，以改善混合料透气性，增加通过料层的风量，达到提高烧结矿产、质量的目的。混合料水分的准确检测和自动控制是烧结工艺中不可缺少的环节，烧结料水分的相对稳定对烧结过程的顺利进行以及实现烧结生产优质、低耗至关重要，烧结工作者为此做了大量的工作，其中引进北京宇宏泰测控技术公司开发研制的MM710-2lCS水分测量控制系统就是一次有益的尝试。

简介：