简介：ParkNelco公司的生产及工艺工程经理DougLeys先生撰文指出，当设计3～6GHz印制电路板时要注意考虑电路的趋肤效应、表面粗糙度、临近效应、电磁兼容性及介质基板材料等问题；并结合该公司的产品及有关技术数据，阐明了在选用高频电路基材时必须掌握的技术细节。同时本文中还搜集了一些低介电常数、低损耗因数基板材料的商品名称、型号及其主要技术数据。

简介：Mg–9Li–3Al–1.6Yalloyswerepreparedthroughmixturemethod.Themicrostructure,mechanicalproperties,andcorrosionresistanceoftheas-castandasextrudedalloyswerestudiedbyopticalmicroscopy（OM）,scanningelectronicmicroscopy（SEM）,X-raydiffraction（XRD）,mechanicalpropertiestesting,andelectrochemicalmeasurement.Theas-castMg–9Li–3Al–1.6Yalloywiththeaveragegrainsizeof325lmiscomposedofb-Limatrix,blocka-Mg,andgranuleAl2Yphases.Afterextrusion,thegrainsizeoftheas-castalloyisobviouslyrefinedandreachesto75lm;thestrengthandelongationoftheextrudedalloyareenhancedby17.20%and49.45%,respectively,owingtotheirfinemicrostructureandreductionofcastingdefects.Theas-extrudedalloyshowsbettercorrosionresistancecomparedtotheas-castone,whichmayberelatedtothelowstoredenergyanddislocationdensityintheextrudedalloy,alsothehomogenizationtreatmentbeforeextrusion.

简介：通过一个简单的水热方法成功地合成出由SnO2纳米片作次级结构的新型花状ZnSnO3-SnO2分级纳米结构。ZnSnO3多面体在生长分级SnO2纳米片的过程中主要起模版作用,制备出的SnO2纳米片的厚度约为25nm。还讨论了ZnSnO3-SnO2样品的形貌随反应时间变化的规律,并且进一步讨论了形成这种分级结构的形成机制。此外,由这种新型ZnSnO3-SnO2纳米结构作敏感材料的气体传感器对乙醇气体具有高灵敏和快响应的特点。ZnSnO3-SnO2纳米片在最佳工作温度270°C时,对50×10-6乙醇气体的灵敏度约为27.8,其响应和恢复时间分别在1s和1.8s内。

简介：

简介：研究了扭转挤压做为一种大塑性变形加工技术的可行性，并将其与普通的正挤压进行比较。在室温下对AA1050铝合金成功进行了扭转挤压和正挤压。采用商用有限元软件ABAQUS/Explicit模拟挤压过程。结果表明，在扭转挤压中，所需的载荷要比正挤压所需的小。有限元分析结果表明，在扭转挤压中，试样承受了较高的等效塑性应变，在挤压的最后阶段扭转挤压试样中的应变分布较之正挤压更为平滑，均匀。

简介：ThemicrostructuresandcrystallizationbehaviorofTi–47at%Ni–3at%Feshapememoryalloywireundertheconditionofseverecolddrawingatroomtemperatureanddifferentpost-deformationannealingprocesseswereintensivelyinvestigatedusingtransmissionelectronmicroscope(TEM)anddifferentialscanningcalorimetry(DSC).ItisindicatedthattheamorphousphaseisdominantintheTi50Ni47Fe3wireafterthecolddrawingof78%arealreduction.Thecriticaltemperatureforrecrystalizationisdeterminedatabout300°C.Theaveragegrainsizegrowsfrom7upto125nmwhenannealingtemperaturerisesfrom300to500°C.Post-deformationannealingprocessexertssignificantinfluenceonthecrystallizationtemperaturewhichclimbsupwiththeincreaseofannealingtemperature.

简介：Au/-Al2O3催化剂被免职降水方法为低集中白酒溪流(甲醇，乙醇，iso-propanol和n-propanol)的催化燃烧作好准备。催化剂被X光检查光电子描绘光谱学(XPS)，X光检查diffractometry(XRD)和精力散X光检查微分析(版本)技术。XPS结果证明仅仅催化剂的表面上有Au0。XRD模式证明Au高度大概在-Al2O3上被驱散。为有2.0g/m3的集中的甲醇，乙醇，iso-propanol和n-propanol的完全的变换的温度是60，155，170和137?，分别地但是他们完全在60，220，260和217点被使矿物化进CO2和H2O吗？分别地在优化催化剂上。催化剂的活动在130h是稳定的。为催化甲醇消除的动力学跟随了伪--首先订表示为r=0.6528c0+0.084的反应2。明显的激活精力的价值是在反应温度的范围的54.7kJ/mol。

简介：ThedistributionsoftheaxialstressandshearstressinAl2O3-TiC/Q235diffusionbondedjointswerestudiedusingfiniteelementmethod(FEM).Theeffectofinterlayerthicknessontheaxialstressandshearstresswasalsoinvestigated.Theresultsindicatethatthegradientsoftheaxialstressandshearstressaregreatnearthejointedge.ThemaximalshearstressproducesattheinterfaceoftheAl2O3-TiCandTiinterlayer.WiththeincreaseofCuinterlayerthickness,themagnitudesoftheaxialstressandshearstressfirstdecreaseandthenincrease.Thedistributionoftheaxialstresschangesgreatlywithalittlechangeintheshearstress.TheshearfractureinitiatesattheinterfaceoftheAl2O3-TiC/TiinterlayerwithhighshearstressandthenpropagatestotheAl2O3-TiCside,whichisconsistentwiththestressFEMcalculatingresults.

简介：TheeffectofyttriaonthesolidreactionmechanismofaCaHPO4·2H2O+CaCO3systematdifferenttemperatureswasexperimentallystud-ied.Thesampleswithandwithoutyttriaweresubjectedtothermogravimetric/differentialscanningcalorimetrymeasurement.ThesampleswereheattreatedatthetemperaturescorrespondingtothepeaksontheDSCspectra,andtheresultedphasecompositionswereidentifiedbyX-raydiffraction.Thetransformationmechanismwasdeducedbycomparingthephasesobtainedatdifferenttemperatures.Theresultsshowthatthetransformationsatbelow1073Karenotaffectedbyyttria,butallthoseatabove1073Karecompletelyaltered.Theformationtem-peratureofhydroxyapatitedecreasesby134K,andthedecompositiontemperatureincreasesby38K.ThepolymorphoustransformationofCa3(PO4)2fromβphasetoαphaseincreasesby47K.Thethermodynamicpropertiesofthetransformationsatabove1073Karealsomodi-fiedbytheadditionofyttria;thatis,theendothermalpeaksaresubstitutedbyexothermalpeaks.

简介：在含有10％硫酸、5％硼酸和2％磷酸的混合电解液中，对2024-T3铝合金进行阳极氧化处理，以提高其耐腐蚀性能。使用电化学阻抗频谱分析研究阳极氧化处理后合金的腐蚀行为。利用塔菲尔图和盐水喷雾技术进行对比发现，与只用磷酸或硫酸和硼酸的电解液相比，使用含有10％硫酸、5％硼酸和2％磷酸的混合电解液阳极氧化处理后的2024-T3铝合金，具有更好的耐腐蚀性和持久性。该电解液可以替代普遍用于阳极氧化铝合金的铬酸盐浴。

简介：GrainboundarydiffusiontechniquewithTbH_3nanoparticleswasappliedtofabricateTb-lesssinteredNdFe-Bpermanentmagnetswithhighcoercivity.Themagneticpropertiesandmicrostructureofmagnetsweresystematicallystudied.Thecoercivityandremanenceofgrainboundarydiffusionmagnetareimprovedby112%andreducedby26%comparedwiththoseoftheoriginalmagnet,respectively.Meanwhile,boththeremanencetemperaturecoefficient(α)andthecoercivitytemperaturecoefficient(β)ofthemagnetsareimprovedafterdiffusiontreatment.MicrostructureshowsthatTbelementenrichesinthesurfaceregionofNd_2Fe_(14)Bgrainsandisexpectedtoexistas(Nd,Tb)_2Fe_(14)Bphase.Thus,themagneto-crystallineanisotropyfieldofthemagnetimprovesremarkably.Asaresult,thesinteredNd-FeBmagnetsbygrainboundarydiffusionwithTbH_3nanoparticlesexhibitenhancedcoercivity.

简介：1．价格走势分析1．1国际铂价受日本地震影响大幅下跌2010年，由于需求改善，铂价震荡上行，年末上涨至1750美元／盎司。2011年初，铂价承接去年的上涨趋势，1月中旬在投资者推动下上涨至1800美元／盎司，随后铂价出现小幅回调。2月初，受南非供应吃紧影响铂再次发力，快速突破1850美元阻力，2月9日最高达到1864．5美元／盎司。

简介：广州国际3D打印展、广州国际模具展9月15日至17日隆重举行期间，记者采访时得到这样的信息-“首届formnext法兰克福国际精密成型及3D打印制造展览会即将精彩亮相!”

简介：

简介：本文介绍Si3N4(代替部分金刚石浓度）配合铁基（以Fe代Co)结合剂氮化金刚石薄膜涂层节块，可大大降低成本，该节块性能良好，有较高使用效果及经济效益。

简介：许多想快速掌握三维CAD建模的初学者，都苦于一些案例教程太复杂，小编将每个月推出针对初学者的需求，提供能在短时间内了解三维CAD建模基本操作的安全教程。

简介：镍钛形状记忆合金样品分别在573、723和873K时效2h。在573和723K时效的镍钛样品中,可以观察到2个R相变体,而且这2个R相变体与B2基体之间的取向关系可以确定。在573和723K时效的镍钛样品中,细小均匀的Ni4Ti3沉淀相与B2奥氏体基体之间保持共格关系。在873K时效的镍钛样品中,可以观察到Ni4Ti3沉淀相在晶粒内部和晶界处析出,不均匀的Ni4Ti3沉淀相与B2基体之间保持共格、半共格和非共格关系。对于873K时效的镍钛样品,加热时发生B19’马氏体向B2奥氏体转变的一阶相变,但在冷却时发生B2-R-B19’的二阶相变。723K时效的镍钛样品在冷却时也表现出B2-R-B19’的二阶相变,但在加热时发出B19’-R-B2的二阶相变。对于573K时效的镍钛样品,由于Ni4Ti3沉淀相周围的局部应力不均匀和局部成分不均匀,则其发生三阶相变。

简介：利用高频辅助激光熔覆技术在镍基合金上制备Al2O3-13%TiO2（质量分数）陶瓷涂层。采用SEM、XRD和EDS等方法分析陶瓷涂层的微观结构和陶瓷层与粘结层之间的结合界面。结果表明：陶瓷层出现了完全熔化区和液相烧结区双层结构,其中,完全熔化区颗粒充分烧结长大,而液相烧结区则出现了三维网状结构,该三维网状结构由熔化的TiO2相包裹Al2O3颗粒形成。通过激光熔覆作用下的粉末熔化和扁平化行为解释双层结构形成机理。同时,在陶瓷层与粘结层的结合界面上发现具有尖晶石结构的NiAl2O4和针状结构的Cr2O3,证明在激光熔覆过程中发生的化学反应可以有效增加陶瓷层与粘结层的结合强度。

简介：2010年8月9日，美国国际贸易委员会发布公告，对原产于中国、巴西和加拿大的铸铁件进行反倾销快速日落复审调查，以确定在取消反倾销措施后，在合理的、可预见的期间内，涉案产品对美国国内产业造成的实质性损害是否继续或再度发生。

简介：针对激光直接沉积修复的1Cr15Ni4Mo3N钢零件在磁粉检测时出现的磁痕现象,采用接触通电、湿磁粉连续法,对设计的试样进行磁粉检测,确定磁痕显示位置;利用光学显微镜对磁痕显示处形貌及修复接头和组织进行观察和研究,分析磁痕的性质和形成原因。研究发现:激光直接沉积修复1Cr15Ni4Mo3N钢在磁粉检测过程中与修复区外轮廓完全重合的磁痕显示是伪磁痕显示,主要是由修复区与基体中奥氏体含量的差异造成的。