Anexplicitfull-fieldexpressionoftheGreen’sfunctionsforanisotropicpiezoeleetricbimateri-alswithaslippinginterfaceisderived.Whentheelectro-elasticsingularityreducestoapraydislocationindisplacementandelectricpotential,interactionenergy,betweenthedislocationandthebimaterialsisobtainedexplicitlywhilethegeneralizedforceonthedisloeationisgiveninarealformwhiehisalsovalidfordegener-atematerials.Theinvestigationdemonstratesthatthehoundaryconditionsatlheslippinginterfacebetweentwopiezoelectricmaterialswillexertaprominentinfluenceonthemobilityofthedislocation.