  • 简介:ApplictionofMgO0-Cr2O3brickcomposedofMgO>72%,Cr2O3>14.8%-168.69%,withporosity13%-14%,compressivestrength33.0-43.8MPa,flexurestrength11.9-16.5MPaandrefractorinessunderload≥1750℃inanassemblesnorkelof300tRHfurnaceinBaoskhanIron&SteelCompany(Baosteel)Showedgoodresultsofaverageservicelifeof106.6heats,maximum119heats.Petrologi-calanalysisandvisualexaminationwerealsodonetotheresidualbricktoinvestigatethewearmecha-nism.

  • 标签: 氧化镁 三氧化二铬 300t洛氏硬度 通气管 宝钢 炼钢炉
  • 简介:ThisworkstudiedthecharacteristicsofSiO2distributionandstructureofsilicatephasesinMgO-ZrO2compositessynthesizedbyrawmaterialsoflightfiredmagnesitendzircon,Theresultsindicatethat30wt%-40wt%SiO2contentinthesystemisexistedintheformofcrystallineofforsterite(M2S),theremainderingofSiOcontent(60wt%0-70wt%)isexistedintheglassphase,Thechemicalcompositionofglassphaseiswellagreedwiththechemicalcompositionofmonticellite(CMS).

  • 标签: 二氧化硅 氧化镁 氧化锆 复合耐火材料 硅酸盐
  • 简介:AnO'-Sialon-Al2O3compositerefractorywaspreparedbyinsitureactionofSi3N4-ZrSiO4-Al2O3mixturewithfusedaluminaaggregates.Densification,insitureactionprocedureandmicrostructureofthematerialwereinvestigatedbymeansofX-raydiffraction,opticalandscanningelectronicmicroscopesandEDAX.

  • 标签: O′-硅铝氧氮聚合材料 氧化锆 三氧化二铝 AL2O3 SIO2 ZRO2
  • 简介:β-sialon/alumina/silicamixturesweresinteredinflowingnitrogenat1500℃and1600℃respectively.ThesinteringpropertiesandmorphologyofsampleswereinvestigatedbySEM,EDSandXRD.Resultsshowthatsinteredpropertiesofthesamplesareinfluencedbysoakingtemperaturesandcompositions.Bulkdensitiesofsamplesareincreasedwiththeincreaseofthesoakingtemperature,whereastheapparentporositiesaredecreased.Masslossofthesinteredsamplesat1500℃islowerthanthatat1600℃,butallthemasslossremainsapproximatelyconstantwiththeincreaseofsialoncontent.Fromthepointofthermodynamicanalysis,ComplexchemicalreactionstakeplaceinsamplesduringsinteringprocessandthevolatileofSiO(g)isresponsibleforthemasslossofsamples.Comparedtocrosssectionmicrostructureofβ-sialon/Al2O3/SiO2mixturessinteredincokepowderbedconsistingofthedensecenterwithwell-developedcolumnofsialonphase,thetransitionalpartwithneedlelikegrainnitrogen-containingphaseandtheloosepartwithshortgranularAl2O3phase,thoseofmixturessinteredinflowingnitrogenisofwell-developedsialonindensecenterandslightlyloosepartwithsialondebris.

  • 标签: 硅铝氧氮聚合材料 氧化铝 硅石 高温条件 耐火材料
  • 简介:MicrostructureandgrainboundarycharacterofhotpressedbinaryAl2O3(mullite,ZrO2)-SiCompositesandquaternaryAl2O3-mullite-ZrO2-SiCcompositewerestudiedbyelectronmicroscopyandmicroanalysis,ResultssuggestthatthereexistgrainboundarysolidsolutionsduetoelementaldiffusionnearSiCandmatrixoxidesgrainboundaries.

  • 标签: 微观结构 氧化铝 AL2O3 ZRO2 碳化硅 氧化锆
  • 简介:LowcementAl2O3-SiO2castableswaspreparedusingsupergradebauxite(w(Al2O3)>85%)asaggregate,brownfusedcorundum,siliconcarbide,Secar71CAcement,α-Al2O3micropowderandmicrosilicaasfinepowders.TheinfluenceofSiC(0,5wt%,10wt%,and15wt%)onresistancetoPbO-richslagwasinvestigatedbystaticcrucibleslagtest(1300℃for5h,inair).TheslagcorrosionmechanismofthecastableswasanalyzedbymeansofSEM,EDSandXRD.TheresultsshowthattheresistanceofAl2O3-SiO2castablestoPbO-richslagisimprovedobviouslybytheadditionofSiC.ThecorrosionmechanismofthePbO-richslagcanbediscribedasthatPbOintheslagreactswithSiO2andCaOinAl2O3-SiO2castables,forminglow-meltingcompounds(suchasPbO·SiO2and2PbO·SiO2).

  • 标签: 二氧化硅 氧化铝 硅含量 氧化铅 碳化 料渣
  • 简介:MgO-Al2O3-Cr2O3rammingmixesmadeofdifferentrawmaterialshavedifferentmineralstructureanddifferentphysicalpropertiesthoughwiththeidenticalparticlesizedistribution,thesameamountofbinderandchemicalcomposition.Theresidualcarboncontentofthefusedmagnesia-chromematerialmadeinreducingatmosphereisveryhigh,ifthismaterialsisusedintheMgO-Al2O3-Cr2O3rammingmix,itwouldcausespallingofthefurnaceliningduringdrying-out.

  • 标签: 原材料 氧化镁 三氧化二铬 搪炉料 搪包料 三氧化二铝
  • 简介:MgO-ZrO2unfiredbrickswithZrO2contentupto8%attheintervalof2%wereprepared,usingfusedmagnesia(MgO:97%)andfusedMgO-ZrO2clinker(ZrO2:14.33%)asstartingmaterialsandphenolicresinasbinder.TheeffectsofZrO2contentonthermalshockresistance(TSR)andotherpropertiessuchascoldandhotmodulusofrupturehavebeeninvestigated.Residualcoldmodulusofruptureratioafterheatingat1000℃andquenchingbyairblowingwasadoptedtocharacterizeTSR.AdditionoftheMgO-ZrO2clinkerimprovesTSR,attributingtothemicrocracktougheningeffectbythermalexpansionmismatchbetweendifferentphases.WhenZrO2contentgoesabove4%,theimprovingeffecttendstobemoderate.TheintroductionofMgO-ZrO2clinkercanalsoimprovetheHMORat1500℃,whiletheincreasedZrO2contentreducesCMORofthebricksprefiredat1600℃,duetothethermalexpansionmismatcheffect.Compromisingtheoverallproperties,theoptimalZrO2contentforsuchmagnesiabasedunfiredbrickissuggestedtobe4%.

  • 标签: 氧化镁 氧化锆 防火砖 抗热震性
  • 简介:Thisworkinvestigatedthethermo-gravimetric(TG)changeandexplosionresistanceofultra-lowcementAl2O3-SiO2castablesaddedwith0,5%,10%,15%and20%of≤74μmrawbauxitepowderscontaining72.8%Al2O3,respectively.Thecastableswerepreparedusingwhitefusedaluminaasaggregate,powdersofwhitefusedalumina,fusedmullite,α-Al2O3ultrafines,3%CAcementand5%microsilicaasthematrixportion.TGchangeofthecastableswasinvestigatedbyathermo-gravimetricanalyzerforlargesizespecimen.Whentherawbauxiteadditionislessthan10%,themass-losingbehaviorofthecastablesissimilartothatwithoutrawbauxite,tendingtoreachaconstantmassaround400℃,beforewhichthemass-lossismildandproducinglittledestructiveinfluence.Withmorethan10%rawbauxiteaddition,however,themass-lossincreasessignificantly,andthetemperaturetoreachaconstantmassincreasesto600℃orhigher,unfavorabletostructuralstabilization.Withtherawbauxiteadditionupto20%,nonegativeinfluenceonexplosionresistanceisfound.

  • 标签: 氧化铝微粉 铝土矿石 超低水泥 二氧化硅 浇注料 热行为