简介：WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability，evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.

简介：FlameheatingcombinedwithwatercoolingwasusedtostraightenA6N01aluminumalloyweldedjointandeffectofflameheatingpassonitsmicrostructureandmechanicalpropertieswasstudied.ResultsshowedthattheflameinducedtheprecipitationandgrowthoftheMg2SiphaseontheAlsubstrateforthethermalagingA6N01aluminumalloyweldedjoints,thusitledthedecreaseofmicro-hardnessandtensilestrengthoftheA6N01aluminumalloyweldedjointwiththeincreaseoftheheatingpass.However,thefatiguepropertyoftheflameheatedjointwasimprovedbecausetheMg2Siprecipitationhinderedtheinitiationandpropagationofthefatiguecrack.

简介：

简介：Inthispaper,thebrazingmechanismofLY12aluminumalloyatmiddlerangetemperaturewaspresented.TheCsF-AlF3non-corrosivefluxwasutilizedtoremovethecomplexoxidefilmonthesurfaceofLY12aluminumalloy.TheresultsrevealedthattheoxidefilmwasremovedbytheimprovedCsF-AlF3fluxaccompaniedwiththeoccurrenceofreactionaswellasdissolutionandthecompoundsCsFplayedanimportantroletoremovetheoxidefilm.Actually,thehighactivityofflux,say,theabilitytoremovetheoxidefilm,wasduetothepresenceofthecompounds,suchasNH4F,NH4AlF4andcompositemoltensalt.TheproductionofHFwasthekeyissuetoacceleratethereactionandenhancetoeliminatetheoxidefilmbydissolution.ItwasfoundthattherareearthelementLaatsmallpercentagewasnotenrichedattheinterface.Moreover,therareearthfluorideenhancedthedissolutionbehavior.

简介：根据《“十二五”智能制造装备产业发展规划》，到2015年，智能制造装备产业销售收入超过1万亿元，年均增长率超过25％，工业增加值率达到35％。本土化智能制造装备满足国民经济重点领域需求，国内市场占有率超过30％。到2020年，将我国智能制造装备产业培育成为具有同际竞争力的先导产业。建立完善的智能制造装备产业体系，

简介：ThevacuuminductionbrazingofSiCparticulatereinforcedLY12alloymatrixcompositeusingAl-28Cu-5Si-2Mgfillermetalhasbeencarriedout.Themicrographofthejointinterfacewasobservedbyscanningelectronmicroscopy.Thejointstrengthwasdeterminedbysheartests.Theresultsshowthatbrazingtemperature,holdingtime,SiCparticlevolumepercentageandpostheattreatmentinfluencejointstrength.SiCparticleshappeninthebrazingseamandthedistributionofSiCparticlesinthejointisnotuniform.Particle-poorzonesinthejointexistnearthebasemetal,andparticleconcentratezonesexistinthecenterofthebrazingseam.Inaddition,thefailureofthecompositeispredominantlyinitiatedbytherootingofSiCparticleinthebrazingseamandthemicro-crackexpandedalongthebrazingseamwithlowenergy.

简介：2015年4月14日,第19届＂林德金杯＂青年焊工国际大赛在捷克弗莱代克·米斯特克正式举行。本次赴捷克的中国代表团的团员主要来自广西机电职业技术学院,广西石化高级技工学校以及江南造船（集团）有限公司。

简介：Inthispaperanewmethodforpreventingweldinghotcracking—theinversestrainmethod(ISM)isdevelopedontheprincipleofweldingmechan-ics.EffectivenessandfeasiblityofmethodinpreventingweldinghotcrackingofhighstrengthaluminumalloyLY12CZbysynchronousrollingduringwelding(SRDW)alongbothsidesoftheweldatasuitabledistancebehindtheweldingarcareexamined.ExperimentalresulteindicatethatweldinghotcrackingofLY12CYcanbeeffectivelypreventedandthemechanicalpropertiesofweldedjointcanalsobeimprovedbythemethod.Itisanimportantnewsolutionforpreventinghotcrackinginweldingofsheetmetal.

简介：Themechanicalproperties,creepdamage,creeprupturestrengthandfeaturesofinterfacialfailuresofweldedjointsbetweenmartensite(SA213T91)andpearlitesteel(12Cr1MoV)havebeeninvestigatedbymeansofargontungstenpulsedarcwelding,hightemperatureacceleratedsimulation,creeprupture,mechanicalpropertytestsandscanningelectronicmicroscope(SEM).Theresearchresultsindicatethatthemechanicalpropertiesofovermatchedandmediummatchedjointdeteriorateobviously,andtheyaresusceptibletocreepdamageandfailureafteracceleratedsimulationoperation500h,intheconditionofpreheat250℃,andpostweldingheattreatment750℃×1h.However,themechanicalpropertiesofundermatchedjointarethebest,theinterfacialfailuretendencyofundermatchedweldedjointislessthanthoseofmediumandovermatchedweldedjoint.Therefore,itisreasonablethatlowalloymaterialTR31isusedasthefillermetalofweldbetweenSA213T91and12Cr1MoVsteel.

简介：<正>6月19～22日,第12届北京·埃森焊接与切割展览会在上海新国际博览中心召开。为了加强与企业的交流和沟通,增强对厂家的了解,以便今后进一步做好行业服务工作,成都奥力公司携旗下中国焊接博览会组委会、《现代焊接》杂志社、中国焊接资讯网参加了此次展会,并取得了良好的效果。

简介：近期,中华全国总工会、科学技术部、人力资源和社会保障部及工业和信息化部联合下发了《关于举办2015年中国技能大赛——第五届全国职工职业技能大赛的通知（总工发〔2015〕18号）》（以下简称《通知》）,决定共同举办2015年中国技能大赛——第五届全国职工职业技能大赛。