简介：Praseodymium(Pr)wasimpregnatedtoCeO2-ZrO2solidsolutionbyanimpregnationmethod.Theas-obtainedPrmodifiedCeO2-ZrO2wasimpregnatedwith1wt.%Pdtopreparethecatalysts.ThestructureandreducibilityofthefreshandhydrothermallyagedcatalystswerecharacterizedbyX-raydiffraction(XRD),Raman,X-rayphotoelectronspectroscopy(XPS),COchemisorptionandH2temperature-programmedreduction(H2-TPR).Theoxygenstoragecapacity(OSC)wasevaluatedwithCOservingasprobegas.EffectsofimpregnatedPronthestructureandoxygenstoragecapacityofcatalystswereinvestigated.TheresultsshowedthattheagedPr-impregnatedsampleshadmuchhigherOSCandbetterreducibilitythantheunmodifiedones.TheschemeofstructuralevolutionsofthecatalystswithandwithoutPrwasalsoestablished.PartialoftheimpregnatedPrdiffusedintothebulkofCeO2-ZrO2duringageing,whichinhibitedthesintering,andincreasedtheamountofoxygenvacanciesinCeO2-ZrO2support.Furthermore,thoseimpregnatedPrspecieswhichcoveredonthesurfaceofthesupportobstructedthestrongmetal-supportinteractionbetweenPdandCesoastoreducetheencapsulationofPdaswellasthebackspill-overoftheoxygenduringthecatalyticprocess.

简介：除铬、镍外，钼是不锈钢中最重要的合金元素。研究已证实，即使在海洋性大气中，仅靠铬，甚至铬量高达近24％也很难完全防止不锈钢的锈蚀，必须加入铝元素[12B]。但钼对不锈钢耐蚀性的有益作用的前提是钢中必须含有足够量的铬元素。

简介：受原燃料市场以及销售市场影响,鄂钢面临前所未有的压力,因此降低生铁成本成为高炉生产的主要任务。6号高炉通过采用降低矿石成本、降低高炉燃料比等措施,不断探寻低成本冶炼的方法。

简介：采用活性炭吸附法对株冶冶炼废水进行了COD去除研究，考察了pH值、反应时间、活性炭用量、反应温度对去除率的影响。结果表明：采用粉末活性炭为吸附剂，当pH值为8．5，搅拌时间为0．5h，活性炭用量为0．25g／L，温度为25℃时，COD去除率达到64．87％，出水COD约为20mg／L。

简介：氧化锌矿采用直接硫酸溶液浸出，通过控制适当的pH值、粒度、浸出温度、浸出时间、搅拌速度、液固比，一段浸出就得到理想的浸出效果，浸出液经净化除杂、碳酸钠沉淀、干燥、煅烧，得活性氧化锌产品。

简介：TwonovelwashcoatsCe0.8Zr0.15La0.05OδandCe0.8Zr0.2O2waspreparedbyanimpregnationmethod,whichactedasahostfortheactivePdcomponenttopreparePd/Ce0.8Zr0.15La0.05Oδ/substrateandPd/Ce0.8Zr0.2O2/substratemonolithiccatalystsfortoluenecombustion.ThewashcoatswascharacterizedbyX-raydiffraction(XRD),Ramanspectroscopy,Brunauner-Emmett-Teller(BET),andH2-temperature-programmedreduction(H2-TPR).Theresultindicatedthatboththewashcoatshadstrongvibration-shockresistanceaccordingtoultrasonictest.DopingLa3+intoCeO2-ZrO2solidsolutioncouldgeneratemoreoxygenvacancies,andcouldinhibitthesinterofCeO2-ZrO2solidsolutionwhencalcinedathightemperatures(800,900and1000°C).ThewashcoatCe0.8Zr0.15La0.05Oδhadmuchbetterredoxproperties.ThereductivetemperatureofCe4+speciesshiftedtolowtemperatureby60°Cwhenthewashcoatscalcinedathightemperatures(800,900and1000°C).ThePd/Ce0.8Zr0.15La0.05Oδ/substratemonolithiccatalystcalcinationat500°Chadthebestcatalyticactivityandthe95%tolueneconversionatatemperatureaslowas190°C.Whencalcinedatlowtemperature(500and700°C),thecatalyticactivityhaslittleimprovement,however,whencalcinedathightemperature,thecatalyticactivityofPd/Ce0.8Zr0.15La0.05Oδ/substratemonolithiccatalystshadsignificantimprovement.Ascatalystwashcoat,theCe0.8Zr0.15La0.05OδhadbetterthermalstabilitythanthewashcoatCe0.8Zr0.2O2,thedevelopedPd/Ce0.8Zr0.15La0.05Oδ/substratemonolithiccatalystinthisworkwaspromisingforeliminatingVolatileorganiccompounds.

简介：Usingmetallographicobservationandmechanicalmeasurement,themicrostructureandmechanicalpropertiesofGH4169Galloyhasbeeninvestigated.Theeffectofthephosphorus,borontraceelementsonmechanicalpropertiesoftheGH4169Galloyarecomparedandanalyzed.Theresultsshowedthatthehot-workabilityoftheGH4169Galloyisverygood.ThestressrupturespropertiesofGH4169Galloyisover3timesthanthetraditionalGH4169alloy.

简介：SrB6O10:Tb黄磷被高温度的稳固的州的反应综合。合作掺杂物，Tb集中和照耀在SrB6O10的TL上开暴露的Ce或李的影响：Tb被调查。当合作掺杂物不能改进SrB6O10的敏感，结果显示出那Ce或李:Tb黄磷。TL反应取决于Tb集中，0.02是在从0.01～0.10的集中范围的最佳。用最佳Tb集中，我们计算了SrB6O10的运动参数:采用山峰形状方法的Tb，并且建议服从第二的黄磷订动力学。TL排放紧张线性地依赖于在50~的剂量范围以内的照耀剂量200Gy。典型Tb(3+)离子排放在TL排放光谱被观察。

简介：阐述了应用无功补偿装置消除谐波、提高功率因数改善6kV系统供电质量,杜绝了因电压瞬降而引发停机停产事故,减少了因停机停产带来的损失.

简介：结合工业污水处理设施的实际运行情况，研究了在活性污泥法处理工业污水过程中，水温对微生物的活性及其对污染物的降解效率的影响，并分析了产生影响的原因及应对措施。

简介：采用溶胶–凝胶法对盐酸预处理后的活性炭（activatedcarbon,AC）进行负载TiO2改性处理,利用扫描电镜（SEM）、能谱分析（EDS）、比表面积及孔径测试（BET）、热重分析（TG/DTG）、傅立叶红外光谱分析（FTIR）等对负载TiO2前后的活性炭结构与理化性能进行表征,并利用电化学工作站测试其电化学性能。结果表明,凝胶的最佳煅烧温度为450℃,制得的TiO2/AC复合体表面及孔道中有絮状或颗粒状的TiO2存在,Ti元素含量（质量分数）为24.91%,晶体类型为锐钛矿型;同时,TiO2/AC表面形成一些Ti—O键的含氧官能团。活性炭负载TiO2改性后,比表面积降低23.1%,比电容升高16.4%,电吸附性能提高,可作为电极材料用于去除废水中的无机盐离子。

简介：电炉厂采用100tUHP电炉短流程生产20G管坯钢。通过实施精料方针、规范脱氧工艺、优化吹氩处理工艺、选择最佳二冷区配水模型、采取钢水低过热度浇注、控制拉速、控制轧制温度等，产品能够满足市场需求。

简介：ＣｈａｒａｃｔｅｒｉｓｔｉｃｓａｎｄＣｏｎｔｒｏｌｉｎｇｏｆＬａＢ６ＺｒＢ２ＥｕｔｅｃｔｉｃＭｉｃｒｏｓｔｒｕｃｔｕｒｅＣｈｅｎＣｈａｎｇｍｉｎｇ（陈昌明），ＺｈｏｕＷａｎｃｈｅｎｇ（周万城），ＺｈａｎｇＬｉｔｏｎｇ（张立同）（ＮａｔｉｏｎａｌＫｅ...

简介：~~

简介：以8种不同孔结构的活性炭为实验对象,利用低温N2（77K）吸附法测定活性炭的比表面积和孔径分布,并将其涂布到铝箔集流体上组装成双电层超级电容器。以1mol/L四氟硼酸四乙基铵的乙腈溶液（Et4NBF4/AN）为电解液,利用循环伏安和恒流充放电技术研究活性炭的比表面积、中孔和微孔分布以及孔容等对双电层电容器倍率衰减性能的影响。结果表明：活性炭的比表面积、孔径和孔容的适量增大均能提高活性炭的比容量;中孔的适量增加不仅可以减小超级电容器的电阻,还可以提高活性炭的大电流充放电性能,降低大电流充放电时的电容衰减。当电流密度从0.15A/g增大到9.6A/g时：中孔活性炭的比电容衰减率平均为14.13%,而微孔活性炭的平均衰减率为20.58%;中孔表面积对比电容的贡献由10.10μF/cm2下降至9.95μF/cm2,而微孔表面积的贡献则由5.68μF/cm2下降至4.21μF/cm2。

简介：针对电厂除灰渣系统渣浆泵流量过大,水耗、电耗过高的状况,对渣浆泵叶轮进行了切割改造,从而取得了显著的节电、节水效果.

简介：马钢球团厂现有4台网盘造球机，经过5年多的生产实践，虽然取得了一定的成绩，但与国内先进球团厂相比仍有很大的差距。对整个球团工艺而言，造球工序对降低膨润土的消耗、提高球团矿的品位，尤其对提高球团矿的粒度合格率起着决定性的作用。同时，优质的生球是改善竖炉操作参数的基础。

简介：

简介：截至2018年,汽运分公司在用6m^3铲运机76台。多年来6m^3铲运机前驱动桥的损坏、维修量一直居高不下,不但加大了修理工的维修工作量,还导致备件费用高,成本压力增大。因此,对6m^3铲运机前驱动桥的损坏进行原因分析,找出症结所在,制定应对措施,就显得尤为重要。

简介：