简介:本文重点介绍开发高导热高耐热CEM-3覆铜板的技术背景、技术路线和技术成果。
简介:Thecorrosionfatiguebehaviorofepoxy-coatedMg–3Al–1Znalloywasinvestigatedinairand3.5wt%NaClsolution.Epoxycoatingasanewmethodwasusedtoimprovethecorrosionfatiguepropertyofthematerial.Resultsshowthatthefatiguelimit(FL)ofthecoatedspecimensishigherthanthatoftheuncoatedspecimensin3.5wt%NaClsolutionbecauseofthestrengtheningandblockingfunctionsoftheepoxycoating.TheFLofthecoatedspecimensin3.5wt%NaClsolutionisashighasthatinair.Itimpliesthatthecoatedspecimensarenotassensitivetotheenvironmentasthemagnesiumalloy.Thelowtensilestrengthandtheshortelongationofthepureepoxycoatingleadtothatthefatiguecrackofthecoatedspecimenisalwaysinitiatedfromtheepoxy-coatingfilmPoresandpinholesacceleratethefatiguecrackinitiationprocess.PinholesarecausedbythecorrosionreactionsbetweentheepoxycoatingandtheNaClsolution.
简介:ThemicrostructuresandcrystallizationbehaviorofTi–47at%Ni–3at%Feshapememoryalloywireundertheconditionofseverecolddrawingatroomtemperatureanddifferentpost-deformationannealingprocesseswereintensivelyinvestigatedusingtransmissionelectronmicroscope(TEM)anddifferentialscanningcalorimetry(DSC).ItisindicatedthattheamorphousphaseisdominantintheTi50Ni47Fe3wireafterthecolddrawingof78%arealreduction.Thecriticaltemperatureforrecrystalizationisdeterminedatabout300°C.Theaveragegrainsizegrowsfrom7upto125nmwhenannealingtemperaturerisesfrom300to500°C.Post-deformationannealingprocessexertssignificantinfluenceonthecrystallizationtemperaturewhichclimbsupwiththeincreaseofannealingtemperature.