简介：Themicrostructuresofas-castandas-solutionMg–12Gd–2Er–1Zn–0.6Zralloyswereinvestigatedbyopticalmicroscopy（OM）,scanningelectronmicroscopy（SEM）,transmissionelectronmicroscopy（TEM）,highresolutiontransmissionelectronmicroscopy（HRTEM）X-raydiffraction（XRD）andselected-areaelectrondiffraction（SAED）inthepresentinvestigation.TheresultsshowthattheprimaryeutecticphaseMg5（Gd,Er,Zn）andsomeflocculentfeaturesarefoundintheas-castalloy;theSAEDpatternindicatesthattheseflocculentfeaturesarethedenseareasofstackingfaults.The14H-LPSOstructureprecipitatesinthetemperaturerangeof673–793K,andthevolumefractionof14H-LPSOstructureincreaseswiththeextensionofheatingtime;however,thereisnoprecipitationof14H-LPSOstructurewhenthetemperaturereachesupto803K.Inaddition,theMg5（Gd,Er,Zn）phasedissolvesgraduallyalongwiththeprecipitationof14H-LPSOstructure.

简介：在H2SO4-Fe2（SO4）3体系中研究载金黄铁矿的浸出动力学,探讨反应温度、Fe3＋浓度、硫酸浓度、搅拌速度等对黄铁矿浸出的影响规律。结果表明：在H2SO4-Fe2（SO4）3体系中,在30~75°C下黄铁矿浸出过程主要受化学反应控制Fe3＋浓度与黄铁矿的浸出呈正相关,通过Arrhenius经验公式求得浸出表观活化能为51.39kJ/mol。EDS与XPS分析结果表明：黄铁矿氧化过程中硫的氧化经一系列中间形态,最终被氧化成硫酸根,并伴有部分元素硫生成,符合硫代硫酸根氧化路径机理。

简介：提出一种从黑泥中回收利用钛的新工艺,该工艺包括NaOH水热转化、水洗和H2SO4浸出制备TiO2。在优化的反应条件下,即NaOH溶液浓度为50%（质量分数）、NaOH/黑泥质量比为4：1、反应温度为240°C、反应时间为1h和氧气分压为0.25MPa,钛转化率可达97.2%,主要含钛产物是Na2TiO3。非目标产物Na2TiSiO5在水洗中保持稳定,在水热反应中提高NaOH浓度可以抑制Na2TiSiO5的生成。水热产物经过水洗后,97.6%的Na^＋可以回收。含有NaOH的溶液经过浓缩之后可以回用。在较低温度下,水洗物料中96.7%的钛能被较低浓度的硫酸浸出得到钛液。利用所得钛液进一步制备合格TiO2产品。

简介：采用计时电位、SEM、XRD、EIS和Tafel等方法对比研究Pb-Ag-Nd合金在160g/LH2SO4溶液中的脉冲电流极化和恒电流极化过程中的氧化膜和析氧行为。研究结果表明：脉冲电流极化的Pb-Ag-Nd合金表面的氧化膜孔洞更少,膜层更致密。这是由于在脉冲电流极化过程中的低电流阶段析氧反应更缓和,有利于多孔氧化膜的修复,因此低电流阶段可作为氧化膜的＂修复期＂。Pb-Ag-Nd阳极在脉冲电流极化过程中表现出更低的阳极电位,这与脉冲电流极化过程中阳极更小的传荷阻抗和高过电位区间更小的Tafel斜率相对应。更低的阳�

简介：采用动电位和电化学阻抗谱技术研究了纯Ti（2级）和Ti-Pd合金（7级）的耐腐蚀性能。实验温度为36.6℃,实验溶液包括模拟的健康人体条件的pH7.4的PBS溶液和添加了H2O2（0.015mol/L）的pH5.2的炎症状态的PBS溶液。Ti-Pd合金（7级Ti）,在含H2O2的PBS溶液中,其耐腐蚀性能比纯Ti的好（较低的腐蚀电流密度）,表明其是一种很好的骨科植入材料。