简介：电炉炼钢厂应用"70tConsteel电炉+LF+CCM"三位一体短流程工艺,成功开发出电动玩具用硅钢片D2。此钢的试制成功,为电工硅钢在电炉上生产提供了实际经验,且进一步拓展了我厂电炉钢产品结构,为适应市场需要创造了有利条件。

简介：

简介：45D2再加热炉炉顶采用重叠法施工工艺，作为耐火陶瓷纤维炉顶（内衬）的施工方法。

简介：该文筒述了管线钢的市场状况，X60、X65、X70技术要求，生产难点、工艺流程，酒钢生产设备、前期开发情况，对洒钢开发管线钢X60、X65、X70板卷的可行性进行了分析。

简介：MeltspinningtechnologywasusedtopreparetheMg2Ni-type(Mg24Ni10Cu2)100–xNdx(x=0,5,10,15,20)alloysinordertoobtainananocrystallineandamorphousstructure.TheeffectsofNdcontentandspinningrateonthestructuresandelectrochemicalhydrogenstorageperformancesofthealloyswereinvestigated.ThestructurecharacterizationsofX-raydiffraction(XRD),transmissionelectronmicroscopy(TEM)andscanningelectronmicroscopy(SEM)linkedwithenergydispersivespectroscopy(EDS)revealedthattheas-spunNd-freealloydisplayedanentirenanocrystallinestructure,whereastheas-spunNd-addedalloysheldananocrystallineandamorphousstructureandthedegreeofamorphizationvisiblyincreasedwiththerisingofNdcontentandspinningrate,suggestingthattheadditionofNdfacilitatedtheglassformingoftheMg2Ni-typealloy.TheelectrochemicalmeasurementsindicatedthattheadditionofNdandmeltspinningimprovedtheelectrochemicalhydrogenstorageperformancesofthealloyssignificantly.Thedischargecapacitiesoftheas-castandspunalloysexhibitedmaximumvalueswhenNdcontentwasx=10,whichwere86.4,200.5,266.3,402.5and452.8mAh/gcorrespondingtothespinningrateof0(As-castwasdefinedasthespinningrateof0m/s),10,20,30and40m/s,respectively.Thecyclestability(S20,thecapacitymaintainrateat20thcycle)oftheas-castalloyalwaysrosewiththeincreasingofNdcontent,andthoseoftheas-spunalloysexhibitedthemaximumvaluesforNdcontentx=10,whichwere77.9%,83.4%89.2%and89.7%,correspondingtothespinningrateof10,20,30and40m/s,respectively.

简介：以钛粉,硅粉和石墨粉为原料,采用放电等离子烧结技术制备密度为4.14g/cm^3的Ti3SiC2和密度为4.03g/cm^3的0.8Ti3SiC2＋0.2SiC复合材料,并以此为基础制备Ti/Ti3SiC2/0.8Ti3SiC2＋0.2SiC层状材料。通过扫描电镜（SEM）和X射线衍射仪（XRD）分析材料的显微结构与相组成。结果表明：该层状材料的界面结合紧密,没有明显的孔洞、裂纹等缺陷,各层的相组成符合设计要求。经800℃热处理40h后Ti/Ti3SiC2界面处生成稳定的TiC层,在高温下该层状材料的界面基本稳定。

简介：Duetotheremarkablemagnetoresistance(MR)effectonperovskite-typemanganite,magnetoelectronicsandspintronicshavebecomeattractivesubjectsofexperimentalandtheoreticalinvestigationsfortheapplicationpurpose.(La0.9Nd0.1)2/3Ca1/3Mn1-xFexO3(x=0,x=0.05)werepreparedsuccessfullybysol-gelmethod.Thestructure,magneticproperties,andtransportpropertiesofthecompoundswereinvestigated.Themagnetoresistanceeffectdependsonthecompositionandthetemperature.XRDpatternsshowthatthecompoundisasinglephasepolycrystalwithpseudocubicstructure.Alargenegativeisotropicmagnetoresistanceeffectinthesampleswereobservedatlowtemperatureregion.ThemaximumMRofthesampleswas77%and97%,respectively.Itwasmostlikelyduetothescatteringorthetunnelingtransportofspin-polarizedcarriersinlatticeunderstrongmagneticfield.

简介：

简介：在达到一定勘查程度的金矿区,有条件的合理利用部分D级储量作为矿山建设依据,可以减少投资风险,保障黄金生产稳步发展。

简介：以奥氏体再结晶型控制轧制和未再结晶型控制轧制相结合的轧制工艺生产的Q345D钢板,其组织均匀、晶粒细小、性能良好,特别是低温韧性较好,达到了控制轧制的目的。

简介：(Y,Gd)BxV1-xO4-x:Eu3+phosphorswerepreparedbysolidstatereaction.Theredemissioncolorpurityof(Y,Gd)BxV1-xO4-x:Eu3+phosphorismuchbetterthanthatoftherecentwidely-usedcommercialredemittingphosphor(Y,Gd)BO3:Eu3+anditsrelativeemissionintensityis84%ofthecommercialphosphor(Y,Gd)BO3:Eu3+.Itisexpectedthat(Y,Gd)BxV1-xO4:Eu3+phosphorwillbeapromisingcandidateforPDP(plasmadisplaypanels)application.

简介：用溶胶-凝胶法制备镍锌共掺杂Z型锶钴铁氧体Sr3（NiZn）xCo2（1-x）Fe24O41（x=0～0.5）粉末。用X射线衍射（XRD）和扫描电镜（SEM）表征该铁氧体粉末的晶体结构和表面形貌，并测试其室温磁滞回线和室温电阻率。用微波矢量网络分析仪测定该粉末在2～18GHz微波频率范围的复介电常数和复磁导率，根据测量数据计算电磁损耗角正切及微波反射率，分析该材料的微波吸收性能与电磁损耗机理。结果表明：Sr3（NiZn）xCo2（1-x）Fe24O41粉末呈六角片状形貌，晶体结构为Z型，具有良好的软磁特性；x=0.3时该材料的电阻率最低，微波吸收效果最好，在13.5GHz频率的吸收峰为25.1dB，10dB频带宽度为7.7GHz，兼具强的磁损耗和弱的介电损耗。

简介：Loadedonthecordierite,therareearthdopedcompositecatalystwaspreparedbysol-gelmethodcombinedwithdippingtechnique.TakingOrthodichlorobenzeneasmodel,thecatalystwasusedtoremovethedioxinsofthewastegas.Theresultsshowedthatat280℃andgasspacevelocitybeing8000h-1,theorthodichlorobenzenecouldberemovedeffectivilybythepreparedCeO2-TiO2-V2O5compositecatalystwhoseactivitywasremarkablyenhancedbythedopingofCe,whiletheindustrialside-streamtestofdioxinsfromrefuseincinerationsmokeindicatedthatthedecompositionratecouldreachabove93%underthesameconditions.

简介：CeO2andCuOx-CeO2supportedpotassiumcatalystsweresynthesizedbywetnessimpregnationmethod.ThecatalystswerecharacterizedbyBET,NO-TPO,NOx-TPDandsoot-TPOmeasurements.Bythedecorationofpotassiumandcopper,themaximumsootcombustiontemperatureoftheceria-basedcatalystdecreasedto338and379°CinthepresenceandabsenceofNOunderaloosecontactmode,re-spectively.ThepronouncedlyenhancedNOoxidationabilitybycopperintroductionandNOxstoragecapacitybypotassiummodif...

简介：BasedonAPISTD1104-2005andCSAZ662-2007,fieldgirthweldingtestsandgirthweldabilityevaluationswereexecutedforthreetypesofwallthicknessX70UOEpipeline,inwhichthemostpopularmainlinegirthweldingmethod,single-wireautomaticgasmetalarcwelding(GMAW),wasused.Theweldingprocedurespecificationwasoptimizedtoachieveagoodqualityandcold-crack-freegirthweldjointwithoutpreheatingorpost-weldheattreatment.Inaddition,porosities,inclusions,andincompletefusiondefectswereavoided.Thetensilestrength,bending,Vickershardness,CharpyV-notchimpacttoughness,andcracktipopeningdisplacementfracturetoughnessofthegirthweldjointwereevaluated,andthejointexhibitedgoodmechanicalperformance.Thus,thefieldgirthweldabilityofBaosteel’sX70UOEpipelineisexcellentforautomaticGMAW.

简介：采用玻璃化试剂，于铂黄坩埚中，在高温下熔融金川高锍，冷却成形，实现了金川高锍中镍、钴、铜、铁的Ｘ－荧光测定。

简介：Inthiswork,boththethermalexpansionandelectricalconductivityofnanocrystallineLa2Mo2O9werestudied.ThenanocrystallinepowderofLa2Mo2O9wasobtainedbysol-gelmethod,andwiththehelpofSHP(superhighpressure)upto4.5×104atmat700℃forashorttime,andthenanocrystallinepowderwasdensifiedwithoutobviousparticlesizegrowth.TheelectricalconductivityofnanocrystallineLa2Mo2O9wasoneorderofmagnitudelowerthanthatofthemicrocrystallinesampleatthesametemperature.Owingtothephasetransition,themicrocrystallineLa2Mo2O9hasanabruptincreaseofthermalexpansionwithapeakvalueof48×10-6K-1at556℃.Forthenanocrystallinematerial,thepeakvalueincreasesto112×10-6K-1at520℃.Ontheotherhand,above600℃thesignificantgrowthofparticlesizeofthenanocrystallineLa2Mo2O9wasobserved,accompanyingbyatremendousincreaseofthermalexpansionwithapeakvalueofthirdhigherthanthatofLa2Mo2O9.

简介：Basedonthethermodynamicallyself-consistentanalysisandoptimizationofthreesub-binarysystemsoftheternarysystemPrCl3-CaCl2-MgCl2,thethermodynamicsofthisternarysystemhasbeenstudied.UsingHillertmodelandtakingMgCl2asanasymmetriccomponent,thePrCl3-CaCl2-MgCl2phasediagramhasbeencalculated.Theagreementbetweencalculatedandmeasuredcompositionsandtemperaturesatdeflectingpointsonliquidusisgood.Thesystemisasimpleeutecticonewithaeutecticpointat26.0mol%PrCl3,41.5mol%CaCl2,32.5mol%MgCl2;560℃（calculated）and26.0mol%PrCl3,39.4mol%CaCl2,34.6mol%MgCl2;546℃（measured）,respectively.

简介：TheZrO2-Al2O3ceramiccompositeswerepreparedbyappropriatetechniqueswithcommercialZrO2andAl2O3powdersasrawmaterialsandY2O3asstabilizer.TheresultsindicatethatwiththeintroductionofAl2O3intotheZrO2matrixwherethequantityofadditiveY2O3is3.5%(molefraction),thegrowthofZrO2grainsisefficientlyinhibited,whichhelpstheZrO2grainsexistinametastabletetragonalmanner;thushigherstrengthandtoughnessareacquired.Whenthecontentofaluminais20%(massfraction),thebendingstrengthandfracturetoughnessofthecompositesare676.7MPaand10MPa·m1/2respectively,themechanicalbehaviorsareclosetothosepreparedwithZrO2andAl2O3powderssynthesizedthroughwetchemicalapproach.Themechanicalbehaviorsofthecompositesarewellimprovedowingtothedispersiontougheningofaluminagrainsandphasetransformationtougheningofzirconiagrains.

简介：Differentrareearth(RE)ionsdopantswereaddedintotheSrAl2SiO7:Eu2+phosphorsinordertoenhancethephosphorescenceproperties,andtheeffectoftheREionsincludingYb3+,Ce3+,Nd3+,Dy3+andTm3+,wascomparativelyinvestigated.ItwasfoundthatNd3+additionimprovedthephosphorescencepropertiesobviouslyamongallthestudiedREions.Therefore,Sr1.96–xAl2SiO7:xEu2+,yNd3+phosphorswerestudiedindetail,andtheoptimumEu2+andNd3+concentrationsweredeterminedwiththeafterglowtimeofabout20min.Thephasestructures,photoluminescence(PL)properties,long-lastingphosphorescence(LLP)properties,afterglowdecaycurvesandthermo-luminescence(TL)fortheselectedphosphorsduringthecorrespondingstudywereinvestigated.AllthephosphorsexhibitedgreenPLemissionandLLPemission.ThereweretwoTLbandslocatedatabout325and380Kforthestudiedsamples,andtherelationshipbetweenREadditionandphosphorescencepropertieswasdiscussed.