简介：SinglephaseofBa1-xMgAl10O17:xEu2+(0.02≤x≤0.14)phosphorswasfirstsuccessfullypreparedbyco-precipitationinaqueousmediumwitha'reversestrike'method,usingoxalicacidandammoniatogetherasprecipitants.Completelycrystallizedphosphorswereobtainedat1300℃,whichis300℃lowerthanthetemperatureofsolid-statereaction.TheirphotoluminescencewasinvestigatedunderUVandVUVregion,respectively.TheemissionspectraofBa1-xMgAl10O17:xEu2+samplesexcitedby254or147nmshowedacharacteristicwidebandwiththepeakcentredatabout450～454nm.Optimumemissionintensityreachedatx=0.1andthenconcentrationquenchingoccurred.Thesynthesizedphosphorshows10%higheremissionintensitythanthatpreparedbysolid-statereaction.

简介：~~

简介：~~

简介：试图为高温度的熔融的盐反应堆的安装和电极的建设开发材料，在750和950湩爠晥湩浥湥?瑳敲杮桴湥湩?猠汯摩猠汯瑵潩?瑳敲杮桴湥湩?眠牯?慨摲湥湩?愠摮瀠敲楣楰慴楴湯猠牴湥瑧敨楮杮的Ni-11Fe-10Cu的高温度的氧化行为上的艾尔和Y的效果

简介：日前，广西有色金属集团下属的广西冶金研究院开展的“贵州泥堡难处理金矿选冶工艺技术研究”取得突破，通过采用选择性多级浮选工艺及金矿的阶段式深度处理技术，使该金矿从原本不足10％的浸出率提高到92％以上，大大提高了该金矿的开采价值。

简介：

简介：主要介绍了首钢长钢公司轧钢厂四车间φ10mm螺纹钢二切分轧制工艺的生产实践情况.从成本、调整难度和工艺稳定性方面分析两种工艺方案的优劣,确定最佳工艺方案;通过试轧情况,分析存在问题,提出解决措施.

简介：《稀土信息》杂志是国家计委稀土办公室(原国务院稀土办)的机关刊物。是由国家计委稀土办公室主办、委托全国稀土信息网承办的我国稀土行业的权威性信息载体。是当前国内综合类稀土科技信息的唯一正式期刊(月刊)。它以促进我国稀土工业的发展,作好信息导向,繁荣稀土市场经济,为稀土行业服务为宗旨,以刊登党和国家发展稀土产业有

简介：InordertoimprovethehydrogenationanddehydrogenationperformancesoftheMg2Ni-typealloys,MgwaspartiallysubstitutedbyLainthealloy,andmeltspinningtechnologywasusedforthepreparationoftheMg20-xLaxNi10(x=0,2,4,6)hydrogenstoragealloys.ThestructuresofthealloyswerestudiedbyX-raydiffraction(XRD),scanningelectronmicroscopy(SEM)andhigh-resolutiontransmissionelectronmicroscopy(HRTEM).Itwasfoundthatnoamorphousphaseformedintheas-spunLa-freealloy,buttheas-spunalloyscontainingLaheldamajoramorphousphase.WhenLacontentx≤2,themajorphaseintheas-castalloyswasMg2Niphase,butwithfurtherincreaseofLacontent,themajorphaseoftheas-castalloyschangedintoLaNi5+LaMg3phase.Thermalstabilityoftheas-spunalloyswasstudiedbydifferentialscanningcalorimetry(DSC),showingthatspinningratewasanegligiblefactoronthecrystallizationtemperatureoftheamorphousphase.Thehydrogenabsorptionanddesorptionkineticsoftheas-castandas-spunalloysweremeasuredusinganautomaticallycontrolledSievertsapparatus,confirmingthatthehydrogenabsorptionanddesorptioncapacitiesandkineticsoftheas-castalloysclearlyincreasedwithrisingLacontent.ForLacontentx=2,theas-spunalloydisplayedoptimalhydrogendesorptionkineticsat200°C.

简介：TheNd60Fe20Al8Co10B2alloywaspreparedbysuctioncastingofthemoltenalloyintoacoppermoldunderargonatmosphere.Themicro-structuralandmagneticpropertychangesintheNd60Fe20Al8Co10B2alloyduringcrystallizationwereinvestigatedbyX-raydiffraction(XRD),differentialscanningcalorimetry(DSC),scanningelectronmicroscope(SEM)andthevibratingsamplemagnetometer(VSM).TheprecipitationandNd-richandFe-richphaseshavenosignificanteffectontheintrinsiccoercitityforNd60Fe20Al8Co10B2alloyannealedbelow723K.However,thegrowthofFe-richphasedecreasesthesaturatemagnetizationandremanenceofthealloy.Thehardmagneticbehaviorisdisappearedwhenthealloyisfullycrystallized.

简介：8月29日，包头国家稀土高新区对外发布消息称，稀土高新区根据包头市建设稀土新材料基地的战略目标，拟用5～10年的时间，将包头建成全国最重要的稀土新材料基地。

简介：(Cu60Zr30Ti10)98Y2bulkmetallicglass(Φ4mm×70mm)wasobtainedsuccessfullybycoppermouldcoolingandspraying-casting,andsomesampleswereisothermallyannealedattemperaturesof473and623K,whichwaslowerthantheglasstransitiontemperature(Tg)for1h.Microstructureandpropertiesofas-castandannealedsampleswerestudied.Crystallizationphases(Cu10Zr7andCuZr)wereobservedinannealedsamples,andthespeciesandfractionofthesephasesincreasedwithincreasingannealingtemperature.Mic...

简介：MeltspinningtechnologywasusedtopreparetheMg2Ni-type(Mg24Ni10Cu2)100–xNdx(x=0,5,10,15,20)alloysinordertoobtainananocrystallineandamorphousstructure.TheeffectsofNdcontentandspinningrateonthestructuresandelectrochemicalhydrogenstorageperformancesofthealloyswereinvestigated.ThestructurecharacterizationsofX-raydiffraction(XRD),transmissionelectronmicroscopy(TEM)andscanningelectronmicroscopy(SEM)linkedwithenergydispersivespectroscopy(EDS)revealedthattheas-spunNd-freealloydisplayedanentirenanocrystallinestructure,whereastheas-spunNd-addedalloysheldananocrystallineandamorphousstructureandthedegreeofamorphizationvisiblyincreasedwiththerisingofNdcontentandspinningrate,suggestingthattheadditionofNdfacilitatedtheglassformingoftheMg2Ni-typealloy.TheelectrochemicalmeasurementsindicatedthattheadditionofNdandmeltspinningimprovedtheelectrochemicalhydrogenstorageperformancesofthealloyssignificantly.Thedischargecapacitiesoftheas-castandspunalloysexhibitedmaximumvalueswhenNdcontentwasx=10,whichwere86.4,200.5,266.3,402.5and452.8mAh/gcorrespondingtothespinningrateof0(As-castwasdefinedasthespinningrateof0m/s),10,20,30and40m/s,respectively.Thecyclestability(S20,thecapacitymaintainrateat20thcycle)oftheas-castalloyalwaysrosewiththeincreasingofNdcontent,andthoseoftheas-spunalloysexhibitedthemaximumvaluesforNdcontentx=10,whichwere77.9%,83.4%89.2%and89.7%,correspondingtothespinningrateof10,20,30and40m/s,respectively.

简介：Ca-dopedBaMgAl10O17:Eu2+,Mn2+(BAM)bluephosphorsweresynthesizedbyfluxassistedsolid-statereactionmethodusingCaF2andBaF2asco-flux.GooddispersityandparticlesizehomogenizationofhexagonalpurephaseBAMwereobtainedbysinteringat1400℃.TheeffectsoftheCa2+ionscontentonthestructure,morphologyandphotoluminescencepropertiesofthephosphorswerestudied.TheresultsindicatedthattheincorporationofCacoulddecreasethelatticeconstant,improvethehomogeneityanddispersityandenhancethephotoluminescence(PL)intensityofthephosphoreffectively.TheoptimumBa0.86Ca0.04Mg0.97Al10O17:0.1Eu2+,0.03Mn2+PLintensitywasenhancedforabout30%andrelativebrightnesswasimprovedabout4%.Furthermore,thesynthesizedBAMandcommercialBAMphosphorswereannealedfor30minat600oCinair.TheCa-dopedphosphorshadstrongeremissionintensity,higherbrightnessandbetterchromaticitystabilitythanthatofthecommercialphosphor.TheseresultsindicatedthatCa-dopedbluephosphorshadgoodpotentialapplicationsinthecommercialtricolorfluorescentlampsaswellasinotherdisplayandlamps.