简介:Thehotdeformationbehaviourof7075aluminiumalloyreinforcedwith10%ofSiCparticleswasstudiedbyemployingboth'processingmaps'andmicrostructuralobservations.Thecompositewascharacterizedbyemployingopticalmicroscopetoevaluatethemicrostructuraltransformationsandinstabilityphenomena.Thematerialinvestigatedwasdeformedbycompressioninthetemperatureandstrainraterangesof300-500℃and0.001-1.0s-1,respectively.Thedeformationefficiencywascalculatedbystrainratesensitivity(m)valuesobtainedbyhotcompressiontests.Thepowerdissipationefficiencyandinstabilityparameterswereevaluatedandprocessingmapswereconstructedforstrainof0.5.Theoptimumdomainsandinstabilityzonewereobtainedforthecomposites.Theoptimumprocessingconditionsareobtainedinthestrainraterangeof0.1-0.9s-1andtemperaturerangeof390-440℃withtheefficiencyof30%.
简介:ThehotdeformationbehaviorofextrudedAZ80magnesiumalloywasinvestigatedusingcompressiontestsinthetemperaturerangeof250-400℃andstrainraterangeof0.001-1.000s^-1.The3Dpowerdissipationmapwasdevelopedtoevaluatethehotdeformationmechanismsanddeterminetheoptimalprocessingparameters.Twodomainsofdynamicrecrystallizationwereidentifiedfromthe3Dpowerdissipationmap,
简介:利用AmoCAD2000绘图软件的强大功能,能快速进行压铸模具的设计。软件能根据持停形状迅速生成模具的三维实体圉,而三堆实体图又能自动生成三视图.大大简化了人工设计与绘图等工作.彻底改变了传统的模具设计方法,成为现代先进的模具设计技术
简介: