简介:ThispaperintroducesabrazingprocessbetweenAl_2O_3ceramicandInvaralloy.Al_2O_3canbebrazedwithInvareffectively.TheinterfacialstructureofAl_2O_3/Invarjointcanbeexpressedas:Invar/Ag(s,s)+Cu(s,s)+Fe_2Ti(zoneⅠ)/Ag(s,s)+Cu(s,s)+Fe_2Ti+NiTi+Cu_3Ti(zoneⅡ)/Ag(s,s)+Cu(s,s)+Cu_2Ti+Al(s,s)+TiC+TiO(zoneⅢ)/Al_2O_3.Themaximumshearstrengthof139MPawasmeasuredforas-brazedAl_2O_3/Invarjointbrazedat850℃for25minor900℃for15min.
简介:AseriesofnovelAgCl/Ag2CO3heterostructuredphotocatalystswithdifferentAgClcontents(5wt%,10wt%,20wt%,and30wt%)werepreparedbyfacilecoprecipitationmethodatroomtemperature.TheresultingproductswerecharacterizedbypowderX-raydiffraction(XRD),scanningelectronmicroscopy(SEM),X-rayphotoelectronspectroscopy(XPS),andultraviolet–visiblediffusereflectancespectroscopy(UV–VisDRS),respectively.Thephotocatalyticactivityofthesampleswasevaluatedbyphotocatalyticdegradationofmethylorange(MO)underUVlightirradiation.WiththeoptimalAgClcontentof20wt%,theAgCl/Ag2CO3compositeexhibitsthegreatestenhancementinphotocatalyticdegradationefficiency.Itsfirst-orderreactionrateconstant(0.67h-1)is5.2timesfasterthanthatofAg2CO3(0.13h-1),and16.8timesfasterthanthatofAgCl(0.04h-1).TheformationofAgCl/Ag2CO3heterostructurecouldeffectivelysuppresstherecombinationofthephoto-generatedelectronandhole,resultinginanincreaseinphotocatalyticactivity.
简介:采用溶胶-凝胶法在纯钛基体上制备Zn掺杂纳米TiO2薄膜(Zn-TiO2),研究不同热处理温度下Zn掺杂对纳米TiO2薄膜的物理性能、光阴极保护效果和光电化学性能的影响。研究表明,与未掺杂TiO2薄膜相比,Zn的加入提高了Zn-TiO2薄膜的光电化学响应,在300°C热处理后的薄膜使金属基体的电极电位下降最大,降低了897mV。SEM-EDS分析表明,Zn在掺杂薄膜中的分布不均匀,XRD结果显示Zn掺杂的薄膜比未掺杂的薄膜晶粒更细小。红外光谱结果表明,TiO2晶粒表面有Zn—O键生成。紫外光谱表明,Zn掺杂使Zn-TiO2吸收带边红移,扩大了TiO2的光响应范围。根据Mott-Shottky曲线可知,Zn-TiO2薄膜比纯TiO2薄膜的平带电位更负,载流子量更大。这说明在平带电位、载流子量和空间电荷层宽度的协同作用下,300°C热处理后的Zn-TiO2薄膜表现了最佳的光电化学响应。
简介:氮(N)和磷(P)共同做锐钛矿TiO2nanosheets被与外国先锋做的高温度的P跟随的低温度的自我做的N-TiO2认识到。做过程的P能维持好TiO2nanosheets形态学与,这被发现暴露{001}方面。掺杂物的化学状态显示N和P原子在TiO2格子在O地点上代替O。与纯TiO2和做N的TiO2,N-P相比,共同做的TiO2nanosheets在可见轻政体展出更强壮的光吸收和染料分子的更高的降级率。提高的photocatalytic性质被归因于二个因素。一方面,N-P共同做能有效地从3.20~2.48减少TiO2的乐队差距?eV,在可见的光导致吸收的改进政体。在另一方面,存在暴露{001}TiO2nanosheets的方面能在反应导致photogenerated电子和洞的有效分离。
简介:研究了Sb^3+-OH^--Cl^-体系中配位溶解-沉淀平衡的理论模拟和实验验证,包括SbOCl、Sb4O5Cl2和Sb2O3的水解沉淀过程。对不同配体浓度、不同pH值条件下的锑离子平衡浓度进行理论计算及实验验证,同时分别从溶解平衡和物质转变吉布斯自由能的角度对沉淀产物进行理论分析,并开展验证实验。结果表明,实际锑离子平衡浓度大于理论计算的浓度,其中理论计算的锑离子最小平衡浓度在pH值4.6时为10^-10.92mol/L,而实验验证结果表明在pH值5.1时最小平衡浓度为10^-3.8mol/L。在一定pH值条件下可以得到不同沉淀产物,无论是在理论计算或是验证实验中均不存在SbOCl,验证实验中得到了产物Sb8O11Cl2-H2O。
简介:Theobjectiveofthisstudyistoinvestigatetheinfluenceofaddingtinyamountofmixedrareearth(La,Ce)andSrtoAl-20Cu-5Si-2Nifillermetal,byanalyzingthemicrostructure,wettabilityandmechanicalpropertiesofbrazedjoints.Theresultsshowthawiththeadditionofmixedrareearth(La,Ce)intoAl-20Cu-5Si-2Nialloy,theα-AlsolidsolutionaswellasCuAl_2(Ni)intermetalliccompoundphasesignificantlyreduced,whilemoreAl-SieutecticphaseandAl-Si-Cuternaryeutecticphasewereproduced.Andasmixedrareearth(La,Ce)addedin,thewettabilityofAl-20Cu-5Si-2Nifillermetaldecreased,whiletheshearstrengthofthebrazedjointsincreased.TheadditionofMinorSrmodificatedAl-20Cu-5Si-2Nifillermetal,furtherreducedtheCuAl_2(Ni)intermetalliccompoundphase,whichwaspartiallyreplacedAl-Si-Cuternaryeutecticphase.Asaresult,thetensilestrengthaswellasthewettabilityofthefillermetalwasimproved.
简介:Thispaperintroducedthebasictheoryandalgorithmofthesurrogatedatamethod,whichproposedarigorouswaytodetecttherandomandseeminglystochasticcharacteristicsinasystem.TheGaussiandataandtheRosslerdatawereusedtoshowtheavailabilityandeffectivityofthismethod.Accordingtotheanalysisbythismethodbasedontheshort-circuitingcurrentsignalsundertheconditionsofthesamevoltageanddifferentwirefeedspeeds,itisdemonstratedthattheelectricalsignalstimeseriesexhibitapparentlyrandomnesswhentheweldingparametersdonotmatch.However,theelectricalsignalstimeseriesaredeterministicwhenamatchisfound.Thestabilityofshort-circuitingtransferprocesscouldbejudgedexactlybythemethodofsurrogatedata.
简介:疲劳和磨损是影响枪炮身管寿命的两个重要因素。本研究简述了枪炮身管抗疲劳和磨损技术研究进展,并对身管烧蚀磨损寿命和疲劳寿命评估现状进行评述,指出以药室增长量或膛线起始部位,径向磨损量预测身管剩余寿命科学依据不足,且未考虑疲劳和磨损的耦合作用促使裂纹萌生和扩展速率加速的现象。鉴于传统的寿命预测技术不能准确预测身管失效时间,身管健康监测已成为确保枪炮安全服役的重要手段。任一发弹射击时身管外表面产生的应变包含了弹、炮、药三者的综合信息,文中提出以应变增量为身管损伤状态特征值,基于实测身管外壁面应变和局部应变法,建立身管健康状态、外壁面应变和寿命(射弹数)三者之间的内在联系,对枪炮设计、试验、使用和维护具有重要的理论意义和应用价值。