简介:TheAl2O3-SiCcompositepowderswerepreparedinargonatmosphereusingcoalgangueandcarbonaceousmaterials
简介:Simplethree-pointbendingtestatambienttemperaturecharacterizedthemechanicalbehaviorofburnedAl2O3-Crefractoriesbeforeandafterthermalshockinassociationwiththeprocessingparameters(graphitecontentandcokingtemperature,etc.).Theresultsshowedthatnon-linearplastic-elasticbehaviorunderloadlowerthancoldmodulusofrupture(CMOR)wasregisteredinallspecimensandreallinearelasticbehaviorcouldbeidentifiedafterthefirstload.Thetotaldeformationcouldbedividedintotwoparts,plasticandelasticareas.ThegraphitecontentandjointbondingsystemofcarbonandceramicphaseswereresponsibleformechanicalbehaviorofAl2O3-Crefractories.
简介:TheeffectoftheadmixturesofAlandSimetalsandB4CandMgAlONcompoundsontheoxidationofMgO/Si3N4compositerefractoryhasbeenstudied,whichisapromisingcarbonfreerefractoryforsteel-makingapplicatlon.Thefourkindsofadmixturescanbeusedasanti-oxidantsforSi3N4,butthemixtureofAlandSiachievedthebestresult.Themixturecannotonlyplaytheroleasantioxidant,butalsoassistthesinteringprocessandhelpformdensesinteringlayer,improvingthepropertyofthecomposite.
简介:UsingAl2O3-MgOcastableinlargeladlecanavoidcontainationofmoltensteelfromcarbon-containingrefractoriesandincreasladleservicliferemarkably,Theadditionofmagnesiaandfinepowder,theeffectofgrainsizeontheproper-tiesofthecastable,especiallylinearchangeandstructurespallinghavebeenstudied,Castablepro-duedforlargeladlewithsmallweareratehasgotgoodapplicatioresult.
简介:Cr2O3canbesinteredwellat1500℃incarbon-embeddedconditionorH2atmosphere.Butthehighchromebearingrefractoriescannotreachdensificationwhensinteredat1700℃for10hinweakreducingatmosphereformedbythecombustionoffuel,anditsapparentporosityisabout18%.Thehighchromebearingrefractoriesaremainlyusedincoalgasifiers.Thetemperatureinthefurnaceisabout1500℃andtheproductsareH2andCO,whicharejustthesinteringconditionsofthedensechromerefractorieswithapparentporositylessthan10%.Thehighchromebearingrefractoriesusedincoalgasifiersmaybesinteredagainandthenshrink,destroyingthegasifierlining.Thethermodynamiccalculationshowsthatitissafeaboutthehighchromebearingrefractoriesusedingasifiers.Itisalsoexplainedthatthehighchromebearingrefractoriescan’tbesintereddenselyinweakreducingatmosphereformedbythecombustionoffuel.Thenewsinteringtechnologiescanbeusedtoimprovethebulkdensityofthehighchromebearingrefractories.