简介:采用溶胶-凝胶(Sol-gel)法和旋涂法在单晶硅片表面制备了5%(摩尔分数)Er3+掺杂的Yb2Ti2O7薄膜.采用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对薄膜的相结构和表面及截面形貌进行了表征,通过荧光光谱仪检测了薄膜的上转换发光特性.结果表明:Ep+掺杂的Yb2Ti2O7薄膜为单一面心立方Yb2Ti2O7相结构,薄膜表面较光滑平整,颗粒尺寸约为80nm.976nm半导体激光器(LD)激发Er3+掺杂的Yb2Ti2O7薄膜获得了较强的绿色、红色和红外上转换发光,分别对应于Er3+的2H11/2/4S3/2→4I15/2、4F9/2→4I15/2和4S3/2→4I13/2跃迁.Er3+掺杂Yb2Ti2O7薄膜的绿色和红色上转换发光均为双光子吸收过程.Er3+掺杂Yb2Ti2O7薄膜和粉末的上转换发光光谱还出现了绿色和红色上转换发光强度的变化.
简介:Nd_2Zr_2O_7isbeingexploredasanalternatethermalbarriercoating(TBC)materialforoperatingabove1300°C,andgreatefforthasbeenmadetoenlargeitsthermalexpansioncoefficient(TEC)andimproveitstoughness.Inthisstudy,Sc_2O_3wasdopedtoNd_2Zr_2O_7.Thephasestructure,TECsandtoughnessof((Nd_(1-x)Scx))_2Zr_2_O7(x=0,0.025,0.05,0.075,0.1)compoundswereinvestigated.((Nd_(1-x)Scx))_2Zr_2_O7(x=0,0.025,0.05,0.075)exhibitedpyrochlorestructure,while((Nd_(0.9)Sc_(0.1)))_2Zr_2O_7consistedofpyrochloreandfluoritephases.WiththeincreaseoftheSc_2O_3content,theorderingdegreeofthepyrochloreinthecompoundsdecreased.In((Nd_(1-x)Scx))_2Zr_2O_7series,((Nd_(0.925)Sc_(0.075)))_2Zr_2O_7exhibitedthelargestTEC,whilethetoughnessofthecompoundsincreasedwithincreasingtheSc_2O_3content.Therelatedmechanismswerediscussedbasedonthecrystalstructureanalysis.ConsideringtheTECandtoughness,10mol%Sc_2O_3wassuggestedastheoptimaldopingcontentforNd_2Zr_2O_7ceramic.
简介:前言我国塑料加工技术经过20多年的高速发展,已渐趋成熟。塑料制品包装以其独有的特性,具有轻量化、环保和资源再利用等优点,正逐步代替其它的原材料而成为使用较广的包装材料。在塑料制品包装中,中空塑料制品包装占有较大的比例。随着工、农、商、贸、物流以及民生等对中空制品包装需求量的不断扩大和对质量要求越来越高,中空塑料制品包装成型设备的制造,中空吹塑技术也得到了快速提升和发展,从而又进一步促进了塑料中空制品包装质量和档次的提高。目前,我国中空吹塑制品包装品种日益增多,各种包装桶、饮料瓶、汽车内饰件、风管、包装箱、塑料托盘等塑料制品包装已进入各个行业,对中空吹塑成型机的技术和能力的适用要求也越来越高,为此,苏州同大机械有限公司在技术研发和制造等方面做出了不懈的努力,取得了很好的成效。
简介:武藏野涂料公司和从事产品研发的香川化学品公司首次成功开发了水性UV固化涂料,并将制订销售策略,预期使其成为该公司的拳头产品。这种新型涂料将降低以往UV固化涂料的环境负荷,可用于手机及其它移动设备塑料外壳的表面防护。该公司是在以往分子设计的基础上,通过在涂料的每一组份中引入水分散性官能团来实现水性UV固化的。该工艺理想地降低了涂料中对环境有危害的组份,如有机溶剂的含量。为了防护手机壳表面并改善其外观,通常要在其上涂覆厚度10~20μm的快速固化UV树脂薄膜。但目前市售产品含挥发性有机物,会危害环境。由于塑料的斥水性,在其上均匀涂覆水性涂料薄膜很困难。该公司通过优化乳液粒子大小、粒径分布及光聚合引发剂,控制成膜时的流动性解决了这一问题。