简介:AseriesofCd1-xZnxS/K2La2Ti3O10compositesweresynthesizedviaasimpleco-precipitationmethod.ThepreparedsampleswerecharacterizedbyX-raydiffraction(XRD),scanningelectronmicroscopy(SEM),X-rayenergydispersivespectroscopy(EDX),ultraviolet-visiblediffusereflection(UV-Vis),X-rayphotoelectronspectroscopy(XPS)andphotoluminescence(PL)measurements.ThecompositestructuresconsistedofCd1-xZnxSnanoparticlesevenlydistributedonthesurfaceofK2La2Ti3O10.TheabsorptionedgeofK2La2Ti3O10shiftedtothevisiblelightregionuponintroductionoftheCd1-xZnxSnanoparticles.Thephotocatalyticactivitiesofthecatalystswereevaluatedbyhydrogenproductionundervisiblelightirradiation.ThepreparedCd0.8Zn0.2S(30wt%)/K2La2Ti3O10exhibitedhigherphotocatalyticactivity,evolving6.92mmol/gH2undervisiblelightirradiationfor3h.ThepromotedphotocatalyticactivityofthecompositeswasattributedtothesynergisticeffectbetweenCd1-xZnxSandK2La2Ti3O10,whichresultedinenhancedseparationofphotogeneratedelectronsandholes.
简介:采用单辊法制备了宽20mm、厚25μm的Fe78Si9B13合金带材,用绕带机将其绕制成环型磁芯,然后将磁芯进行退火处理,结果表明,随着退火温度的升高,Fe78Si9B13非晶磁芯的初始磁导率m、饱磁感应强度Bs和矫顽力Hc呈先增大后减小的趋势,当退火温度达到450℃时,磁化曲线呈现出一定的线性关系,即恒导磁特性。将经4500(=/100min退火的Fe78Si9B13非晶磁芯用环氧树脂进行封装后,环氧封装后μi和Bs减小,而Hc和损耗Ps增大,磁化曲线和损耗曲线的形状与封装前相同。
简介:采用热注入法成功制备出三元AgInS2和四元Ag—Zn—In—S量子点,物性测试得到AgInS2量子点的发射峰为701nm,Ag—Zn—In—S量子点的发射峰593nm,即Ag-Zn-In—S量子点的发射峰相对于AgInS2量子点发生了蓝移,AgInS2和Ag—Zn—In—S量子点都表现出了较长的荧光寿命,分别为169ns和162ns,结合生物组织光学窗口范围限制,相对Ag—Z—In—S,AgInS2量子点更适用于生物标记。
简介:分析了制备和热处理过程中薄膜沉积方法和沉积条件、沉积速率、薄膜厚度、热处理方法和热处理条件等因素对β-FeSi2相的形成的影响,结果表明,影响β-FeSi2相形成的决定性因素是热处理的温度和时间,此外薄膜的沉积方法和薄膜厚度对β-FeSi2相也有重要的影响。
简介:SnO2nanotubearrayshavebeensynthesizedbymeansofasimpleandlow-costmethod.TheZnOnanorodarrayspreparedbyaqueouschemicalgrowthmethodwereusedastemplates.Byliquidphasedeposition,SnO2nanotubeswereobtainedwithproperdepositiontime.Scanningelectronmicroscopy,transmissionelectronmicroscopyandX-raydiffractionwereusedtocharacterizethemorphologiesandstructuresoftheproducts,andtheformationmechanismwasdiscussedaccordingtotheexperimentalresults.
简介:三不同Ti-Si氧化物structuares,硅石支持了titania,硅石涂的titania和亲密地混合的silica-titania,包含10%-40%SiO2,被nanocrystalline(nc)的微观结构参数的sol-gelprocess.The变化在二进制氧化物的三kirds成为TiO2锐钛矿包括在里面飞机间距d,电池常数(a0,C0),房间体积V,房间轴比c0/a0和水晶谷物缩放,被高决定传播电子显微镜学(HRTEM)和X光检查衍射(XRD)比较地调查。微观结构参数与增加SiO2内容显著地变化,这被发现,annealingtemperature.Different组织了Ti-Si二进制氧化物导致微观结构参数的不同变化趋势。二进制氧化物包含越多SiO2,ncTiO2锐钛矿的缺点越格子出现;Si阳离子的散开或移植能是在微观结构的变化的一个重要有影响的因素。在三种二进制氧化物的ncTiO2的谷物尺寸不仅取决于SiO2内容和退火的温度而且在ncTiO2-anatase.Both谷物尺寸和nc的阶段转变的格子microstrainand失真的度上,TiO2锐钛矿是有效地与增加SiO2内容禁止了。