简介：ThestainlessFe-Mn-Sishapememoryalloy(SMA)coatingwaspreparedonthesurfaceofAISI304stainlesssteel.Theprincipalresidualstressmeasuredbythemechanicalhole-drillingmethodindicatesthattheFe-Mn-SiSMAcladdingspecimenpossessesalowerresidualstresscomparedwiththe304stainlesssteelcladdingspecimen.Themeanstressvaluesoftheformerandthelatteron10-mm-thicksubstrateare4.751MPaand7.399MPa,respectively.What’smore,theirdeformationvalueson2-mm-thicksubstrateareabout0°and15°,respectively.Meanwhile,thevariationtrendandthevalueoftheresidualstresssimulatedbytheANSYSfiniteelementsoftwareconsistwithexperimentalresults.TheX-raydiffraction(XRD)patternshowsε-martensiteexistsinFe-Mn-SiSMAcoating,whichverifiesthemechanismoflowresidualstress.That’stheγ→εmartensitephasetransformation,whichrelaxestheresidualstressofthespecimenandreducesitsdeformationinthelasercladdingprocessing.