简介：IsothermalcompressionofaTi-5.6Al-4.8Sn-2.0ZralloywasconductedonaThermecmaster-Zsimulatoratthedeformationtemperaturesrangingfrom960to1060°C,thestrainratesrangingfrom0.001to10.0s-1,andthemaximumheightreductionof70.0%.Inthetwo-phaseregionoftheTi-5.6Al-4.8Sn-2.0Zralloy,thevolumefractionofαphasedecreaseswithanincreaseindeformationtemperature,butthegrainsizehasaslightvariationwithdeformationtemperature.ThestrainrateaffectsbothmorphologiesandgrainsizeoftheαphaseintheisothermalcompressionoftheTi-5.6Al-4.8Sn-2.0Zralloy.Theoptimalheightreductionalsocontributestothesmallandwell-distributedαphaseintheisothermalcompressionofTi-5.6Al-4.8Sn-2.0Zralloy.

简介：Anewseriesofrareearthcompounds,Y2-xErxMo4O15(x=0.0-2.0),weresynthesizedandtheirstructuresweredeterminedbypowderX-raydiffraction(XRD).RietveldanalysisofXRDpatternsrevealsthatthecompoundsofthisseriescrystallizeinmonoclinicsystemwithspacegroupP21/c.Thelatticeparametersa,b,c,βandtheunitcellvolumeVde-creaselinearlywithincreasingErcontent.Thethermalexpansionpropertiesofthesecompoundswerestudiedunderhigh-temperatureXRD.PositivethermalexpansionsofcompoundsY2-xErxMo4O15arefoundtobeanisotropicalongthethreecrystallographicdirectionswhereaandcaxesexpandwhilebaxiscontractsinthewholetemperaturerange.Byanalysisofdata,theexpansionofweakbandMo2-O14withrisingtemperatureshouldberesponsibleforpositivethermalexpansion.